Method for preparing light-absorbing polymeric compositions

ABSTRACT

The present invention recites a method comprising reacting in a solvent in the presence of a base  
     a) at least one diacidic monomer comprising about 1 to 100 mole % of at least one light-absorbing monomer having a light absorption maximum between about 300 nm and about 1200 nm and 99-0 mole % of a non-light absorbing monomer which does not absorb significant light at wavelengths above 300 nm or has a light absorption maximum below 300 nm, with  
     b) an organic compound of Formula II  
     X—B—X 1    
     wherein B is a divalent organic radical to form a light absorbing composition comprising a mixture of a polymer having the formula  
                 
 
     and a cyclic compound having the general formula  
                 
 
     wherein B is as defined above; n is at least 2, m is 1, 2, 3 or 4 and A comprises the residue of a diacidic monomer comprising about 1 to 100 mole % of at least one light-absorbing monomer having a light absorption maximum between about 300 nm and about 1000 nm and wherein the remaining portion of A comprises the residue of a non-light absorbing monomer which does not absorb significant light at wavelengths above 300 nm or has a light absorption maximum below 300 nm.

RELATED APPLICATION

[0001] This application is a continuation-in-part of our application Ser. No. 08/976,206 filed Nov. 21, 1997, which is based upon and claims the priority of provisional application 60/031,478 filed Nov. 27, 1996.

BACKGROUND OF THE INVENTION

[0002] This invention relates to an improved method for preparing light-absorbing polymeric compositions, which are useful as powders or pellets for incorporation into a variety of thermoplastic resins such as cellulose esters, polyesters, polyolefins, polycarbonates, polyamides, etc. by conventional melt or solution blending techniques. The colored thermoplastic resins thus produced have good clarity, good color development, excellent fastness to light and are useful for a variety of end uses where nonhazardous, nonmigrating, or nonextractable colorants are needed.

[0003] It is well-known that thermoplastic polymers may be colored by adding pigments or solvent dyes (e.g., see Thomas G. Weber, Editor, Coloring of Plastics, John Wiley & Sons, New York, 1979). The use of pigments, however, is accompanied by undesirable properties such as opacity, dullness of color, low tintorial strength, etc. Also, difficulties in uniformly blending the insoluble pigments with the thermoplastic resin are often encountered. Also useful for coloring thermoplastic polymers are the solvent dyes (K. Venkataraman, Editor, The Chemistry of Synthetic Dyes, Vol. 8, Academic Press, New York, 1978, pp. 81-131), which provide compositions having improved clarity, brightness in hue and high tinctorial strength, but which may lead to dye migration, extraction, etc. from the colored thermoplastic polymer. These problems are of particular concern when solvent dyes are used to color flexible polymers such as polyvinyl chloride, polyethylene and polypropylene which have low glass transition temperatures.

[0004] Plastics, paints, printing inks, rubber, cosmetics, and similar materials are typically colored by organic pigments when superior brilliance and tinctorial strength are important. Toxicity considerations have presented chronic problems relative to the use of organic pigments since some have been shown to be potential carcinogens and to cause contact dermatitis.

[0005] Plastics are also colored by using color concentrates consisting of physical admixtures of polymers and colorants (usually solvent dyes). However, the use of such physical admixtures to color polymeric materials such as polyester, e.g., poly(ethylene terephthalate) and blends thereof, present a number of problems, including:

[0006] Colorant migration during drying of the colored polyester pellets.

[0007] Colorant migration during extrusion and colorant accumulation on dies which can cause shutdowns for clean-up. Such colorant migration and accumulation result in time consuming and difficult clean-up, particularly when a polymer of another color is subsequently processed on the same equipment.

[0008] Colorants may not mix well, for example, when using two or more color cencentrates to obtain a particular shade.

[0009] Colorants may diffuse or exude during storage and use of the colored polymeric material.

[0010] The colored polymeric compositions which are prepared by the process of this invention eliminate or minimize the aforementioned problems associated with the use of conventional dyes and pigments.

PRIOR ART

[0011] To attempt to overcome some of the problems mentioned above, particularly as relates to coloring polyesters, colored polyester compositions have been prepared by copolymerizing relatively low amounts of monomeric colorants during the polymer preparation (U.S. Pat. Nos. 5,194,571; 5,106,942; 5,102,980; 5,032,670; 4,892,922; 4,740,581; 4,403,092; 4,359,570; 4,267,306 and W092/07913). However, the preparation of these colored polymers require dyes having outstanding thermal stability since the colorants are exposed to very high temperatures for prolonged periods of time necessary for polyester formation, thus severely circumscribing the selection of efficacious colorants. For example, only the nonazo type colorants have been shown to have the adequate thermal stability for copolymerization into polyesters, since azo type compounds do not have the resquite thermal stability for copolymerization.

[0012] Furthermore, it is known to prepare polymeric dyes by reacting dyes containing reactive hydroxy and amino groups with organic di-acid chlorides in solvents (U.S. Pat. Nos. 2,994,693; 3,403,200; 4,619,990; 4,778,742; 5,401,612). Although this method of polymer preparation allows the use of a wide range of chromophoric classes, including azo compounds, as colorant monomers, the polymerization reaction in each case involves the use of very reactive organic di-acid chlorides which are toxic and involve difficult to handle inorganic halogen compounds in their preparation and have accompanying problems of hydrolysis in the presence of water which causes serious handling and storage problems. The hydrolysis product (HCl) is particularly corrosive and makes storage of these compounds difficult. Furthermore, since the di-acid chlorides will react with water, the monomeric dyes must be specially dried to avoid side reactions in the polymer preparation.

[0013] In a similar attempt to prepare polymeric dyes using relatively low temperatures, polyurethanes have been prepared by reacting dyes bearing two hydroxyalkyl group with aliphatic and aromatic isocyanates (U.S. Pat. No. 5,194,463). However, the organic isocyanates themselves are extremely toxic and present difficult handling problems. They also are reactive with water and thus the reaction requires specially dried monomeric dyes. Also, the colored polyurethanes as a class do not have excellent thermal stability.

[0014] It is further known to prepare colored condensation polymers by reacting a polymerizable lactone or a hydroxyalkanoic acid with a dye containing reactive hydroxy group (U.S. Pat. No. 4,933,426). The procedure again requires relatively high reaction temperatures and prolonged times and use a large excess of the lactone reactant. The method is further hindered by the fact that some lactones are suspected carcinogens.

[0015] Light-absorbing polymeric compositions have also been produced by free radical polymerization of vinyl functionalized light-absorbing monomers (U.S. Pat. Nos. 5,310,837; 5,334,710; 5,359,008; 5,434,231 and 5,461,131).

[0016] Finally, it is known that one may color plastics, in particular polyolefins, with low melting, cross-linked colored polyester compositions containing residues of terephthalic acid, isophthalic acid, or both, a low-molecular weight trimethylol alkane, i.e., 1,1,1-trimethylol propane and a copolymerizable colorant, said colorant being present at a level of 0.1-25% by weight (U.S. Pat. No. 4,116,923). Difficulties are encountered, however, in preparing these highly cross-linked colored polymers as extreme care with regard to the temperature, amount of vacuum, the level of colorant present, and the reaction time, is necessary in order to attempt to reproduce the same quality of cross-linked colored polyester composition. Further, these colored polyester compositions are brittle or low melting and may cause deterioration in physical properties of themoplastic polymers when added in quantities sufficient to produce a high level of coloration.

PRACTICE OF THE INVENTION

[0017] This invention relates to a method for preparing a light absorbing linear polymeric having Formula I

[0018] wherein A comprises the residue of a diacidic monomer comprising about 1 to 100 mole % of at least one light-absorbing monomer having a light absorption maximum between about 300 nm and about 1200 nm and wherein the remaining portion of A comprises the residue of a non-light absorbing monomer which does not absorb significantly at wavelengths above 300 nm or has a light absorption maximum below 300 nm and wherein B is a divalent organic radical selected from C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃—C₈-cycloalkylene-C₁—C₄ alkylene, C₁—C₄ alkylene-arylene- C₁—C₄ alkylene, C₂—C₄ alkylene-O- C₂—C₄ alkylene, and C₂— C₄-alkylene-L-arylene-C₂—C₄ alkylene and C₂—C₄ alkylene-(L- C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; wherein n is at least 2.

[0019] The process comprises reacting said diacidic monomer with an organic compound of Formula II

X—B—X₁   II

[0020] wherein B is as defined above and X and X₁ reactive groups and are independently selected from bromine, iodine and R—SO₂O; wherein R is selected from C₁—C₆ alkyl; C₁—C₆ alkyl substituted with chlorine, fluorine, C₁—C₆ alkoxy, aryl, aryloxy, arylthio or C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl or aryl, with said reaction being carried out in a solvent in the presence of a base; wherein the useful diacid light-absorbing monomers have Formula III

H—Y—H   III

[0021] wherein H represents an acidic hydrogen atom; Y is a divalent light-absorbing moiety selected from a variety of chromophoric classes including azo, disazo, bis-azo, methine, arylidene, polymethine, azo-methine, azamethine, anthraquinone, anthrapyridone (3H-dibenz[f,ij]isoquinoline- 2,7-dione, nitroarylamines anthrapyridine (7H-dibenz[f,ij]isoquinoline-7-one, phthaloylphenothiazine (14H-naphth[2,3-a] phenothiazine-8,13-dione, benzanthrone(7H (de) anthracene-7-one), anthrapyrimidine(7H-benzo[e] perimidine-7-one), anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, fluorindine (5,12-dihydroquinoxaline[2,3-b]phenazine, quinophthalone, phthalocyanine, metal phthalocyanine, naphthalocyanine, metal naphthalocyanine, nickel dithiolenes, squarylium compounds, croconium compounds, coumarin (2H-1-benzopyran-2-one), coumarin imine (2H-1-benzopyran-2-imine), perinone, benzodifuran, phthaloylacridone, phthaloylphenoxazine (14H-naphtho[2,3-a]phenoxazine-8,13-done, phthaloylacridone (13H-naphtho[2,3-c]acridine-5,8,14-trione), anthraquinonethioxanthane (8H-naphtho[2,3-c]thioxanthene-5,8,13-trione, anthrapyridazone, pyrrolo[3,4-c]pyrrole, indigo, thioindigo, quinoline, xanthene, acridine, azine, cyanine, oxazine, 1,4 and 1,5-naphthoquinones, 2,5-diarylaminoterephthalic acids and esters, pyromellitic acid dimide, naphthalene-1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylenetetracarboxylic acid diimide, 3-aryl- 2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline, arylisoindoline, hydroxybenzophenone, benoztriazole, naphthotriazole, diminoisoindoline, naphthopyran (3H-naphtho[2,1-6]pyran-3-one and 3-imine, phthalimides, 2-arylbenzazoles, carbostyryls, 1,2-diarylethenes, 2,5-diarylthiophenes, 2,5-diaryl-1,3,4-oxadiazoles, triazines, 2,5-diarylfurans, 2,5-diaryl-1,3,4-thiadiazoles, thiophenes, 1,3-diphenyl-2-pyrazolines, 2-arylbenzofurans, 2,6-diphenylbenzofurans, quinolines, quinoxalines, 3,4-diarylfuanones, distyrylarenes, benzanthrones, polyarenes and naphthalimides; wherein the hydrogen atoms of Formula III are independently bonded to an oxygen, sulfur, or nitrogen atom which is a part of the light absorbing moiety Y; wherein the useful non light-absorbing monomers have Formula IV,

H—Y₁—H   IV

[0022] wherein H represents an acidic hydrogen atom; Y₁ is a divalent moiety, selected from—O₂C—R₁—CO₂— and—O—R₂—O— and—O₂C—R₃—O—, wherein R₁ is selected from C₂—C₁₂ alkylene, 1-4-cyclohexylene, arylene, arylene-O- arylene, arylene-SO₂-arylene, arylene-S-arylene, and C₁—C₄ alkylene-O- C₁—C₄ alkylene; wherein R₂ is selected from arylene, arylene-O-arylene, arylene-S-arylene, arylene-SO₂-arylene, phenylene-phenylene, and phenylene-C(R₄)₂-phenylene; wherein R₄ is selected from hydrogen and C₁—C₄ alkyl; wherein R₃ is selected from arylene.

[0023] In diacid light absorbing monomers having Formula III, the hydrogen atoms are preferably attached to an oxygen, a sulfur or a nitrogen atom which in combination provides two acidic functional group which can produce the corresponding anions under basic conditions by removal of the protons. The acidic functional groups usually have an acid dissociation constant of about 10^(−1.5) to about 10⁻¹² (pK_(a) of from about 1.5 to about 12). In the case of nitrogen, both protons may be attached to a single nitrogen which is attached to a sulfonyl moiety thus providing two acidic hydrogens on a single functional group.

[0024] Typical, acidic groups which provide one acidic hydrogen include—CO₂H, —SH, —OH attached to an aromatic ring, —CONHCO—, —SO₂—NH—CO—, —SO₂—NH—SO₂—, 1(H)-1,2,4-triazol-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from C₁—C₆ alkyl; C₁—C₆ alkyl substituted with at least one group selected from C₁—C₆ alkoxy, aryl, aryloxy, arylthio or C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl; aryl.

[0025] An example of an acidic functional group providing two acidic hydrogen attached to nitrogen is the sulfamoyl group (—SO₂NH₂).

[0026] The preferred method for producing light absorbing polymeric compositions utilizes the monomers of Formula III, wherein the protons are a part of the—CO₂H, OH attached to aromatic ring, —CO—NH—CO— or 1(H)-1,2,4-triazol-3-yl functional groups. The carboxy groups are normally attached to an aromatic ring carbon or aliphatic carbon which is a part of Y. The hydroxy groups are normally attached to an unsubstituted or substituted phenyl or naphthyl radical which is a part of Y. The —CO—NHCO— groups are usually attached to an aromatic ring to provide an imide such as phthalimide or naphthalimide which are a part of Y. The 1(H)-1,2,4-triazol-3-yl group has the following Formula V, wherein R₅′ is

[0027] selected from hydrogen, C₁—C₆ alkyl or aryl. It should be observed that the triazole may exist in isomeric form as follows:

[0028] The 1(H)-1,2,4-triazol-3-yl group is preferably attached to a sulfur atom which is attached to the remainder of Y.

[0029] The method of the invention in the broadest sense involves the preparation of light absorbing polymeric compositions by reacting a diacidic monomer comprising at least 1 mole % of at least one diacidic light absorbing monomer represented by H-A-H with an organic compound containing two reactive groups represented by X—B—X₁, where B, X and X₁ are as defined above. Thus, the method may be summarized as:

[0030] The diacidic monomer H-A-H must be acidic enough to form two nucleophiles in the presence of base under convenient reaction conditions for the most advantageous process. This usually requires that diacidic monomers have pK_(a) values of about 12 or below.

[0031] The dinucleophilic monomer, formed by the removal of the two hydrogen atoms by the base, attacks the electrophilic compound II, thus displacing anions X⁻ and X₁ ⁻with head-to-tail combination with covalent bonding to produce a linear polymer A—B_(n), wherein n represents the number of repeating units. The number of repeating units must be at least 2, but usually ranges between about 2 and about 25, with the preferred number being between about 3 and about 15.

[0032] The composition produced by the method of the invention comprises, as stated above, a polymer having the general formula A-B_(n). The composition also comprises one or more cyclic compounds having the general formula

[0033] wherein m may be 1, 2, 3, or 4, e.g., the cyclic compounds having the general structures:

[0034] The number and concentrations of the cyclic compounds is dependent upon a variety of factors such as the structure of diacid H-A-H, the structure of the organic compound X—B—X₁, and the conditionss used to facilitate the reaction to produce the composition. The cyclic compounds may constitute up to about 35 weight percent, typically about 0.5 up to 30 weight percent, of the total weight of the composition produced by the method of the invention.

[0035] Suitable bases include alkali metal carbonates; alkali metal bicarbonates; tertiary amines such as triethylamine, tri-n-butylamine, N-methylpiperidine, N,N′-dimethylpiperazine, N-methylmorpholine, N,N,N′,N′-tetramethylenediamine, etc.; aromatic nitrogen bases such as pyridines, picolines, quinolines, isoquinolines, N-alkylpyrroles, N-alkylimidazoles, etc.; bicyclic nitrogen containing bases having non-hindered electron pairs, such as 1,8-diazabicyclo[4,3,0]undec-7-ene (DBU), 1,5-diazabicylco[4,3,0]non-5-ene (DBN) and 1,4-diazadicyclo[2,2,2]octane (DABCO®).

[0036] Typical solvents useful in the polymerization reaction include aprotic polar solvents such as N,N-dimethylacetamide, N,N-dimethylformamide, N-methyl-2-pyrrolidone, N-methyl-N-phenyl formamide, dimethyl sulfoxide, aliphatic nitrites, sulfolane, hexamethyl phosphoramide, etc. and mixtures thereof. Water, alcohols, ketones pyridine and ether-alcohols, such as the Cellosolves, also are sometimes useful. One requirement is that the solvent not form a stronger nucleophile in the presence of the base than that obtained from the diacidic monomer H-A-H.

[0037] The new improved process of the invention allows the preparation of near ultraviolet (UV-A, UV-B and UV-C), visible and near infrared light absorbing linear polymeric compositions at relatively low temperatures, usually at from about 75° C. to about 125° C., without prolonged heating times. Furthermore, the method is adaptable to batch-process production which is advantageous for expensive products such as colorants, near infrared absorbers and near ultraviolet absorbers. The method is adaptable to a wide range of chromophoric classes since the polymer preparative reaction is carried out at relatively low temperature, which for example, allows colored polymeric compositions to be readily prepared from the very important azo class of colorants.

[0038] The preferred reactants of Formula II

X—B—X₁

[0039] are the disulfonate compounds where X and X₁ are both a sulfonate ester of the formula-OSO₂R, wherein R is selected from C₁—C₄ alkyl, phenyl or p-methylphenyl and wherein B is selected from C₂—C₆ alkylene, —CH₂-1,4-cyclohexylene-CH₂—, 2,2,4,4-tetramethyl-1,3-cyclobutylene, 1,4-cyclohexylene, —CH₂CH₂(OCH₂CH₂)₂₋₃ and —CH₂CH₂O—1,4-phenylene-O—CH₂CH₂—. Particularly, preferred reactants of Formula II are those where B is selected from—CH₂CH₂—, —CH₂CH(CH₃)CH₂—, —CH₂C(CH₃)₂CH₂—, —(CH₂)₄—, —(CH₂)₆—, —CH₂CH₂(OCH₂CH₂)₁₋₄ and—CH₂-1,4-cyclohexylene-CH₂—.

[0040] Typical reactants of Formula II are as follows:

[0041] The invention also relates to a light absorbing linear polymeric composition having Formula Ia:

[0042] wherein A₁ comprises the residue of at least one diacidic monomer having a light absorption maximum between about 300 nm and about 1200 nm, preferably between about 325 nm and 1100 nm and most preferably between about 350 nm and 1000 nm and wherein B is defined above and which has been prepared by reacting a diacid light-absorbing monomer of Formula III (H—Y—H) as defined above with an organic compound having Formula II (X—B—X₁) as defined above, with the polymer producing reaction having been carried out in a solvent in the presence of base. The above-described light absorbing composition of formula Ia also contains or comprises one or more cyclic compounds having the formula

[0043] wherein A₁ and B are defined above and m may be 1, 2, 3, or 4. As stated hereinabove, the number and concentrations of the cyclic compounds is dependent upon a variety of factors such as the structure of diacid H-A-H, the structure of the organic compound X—B—X₁, and the conditions used to facilitate the reaction to produce the composition. The cyclic compounds of formula I-B may constitute up to about 35 weight percent, typically about 1 up 30 weight percent, of the total weight of the above-described light absorbing composition.

[0044] The invention also relates to a light absorbing linear polymeric composition having Formula Ib

[0045] wherein A₂ comprises the residue of at least one diacidic monomer, having a light absorption maximum between about 300 nm and about 1200 nm, preferably between about 325 nm and 1100 nm and most preferably between about 350 nm and 1000 nm and which comprises at least about 50% by weight of the total of the composition of Formula Ib and wherein the remainder of A₂ comprises the residue of at least one non-light absorbing monomer of Formula IV above, and wherein said polymeric composition has been prepared by reacting diacidic monomers of Formula III and Formula IV with an organic compound having Formula II above, with the polymer producing reaction having been carried out in a solvent in the presence of base. The light absorbing composition of formula Ib also contains or comprises one or more cyclic compounds having the formula

[0046] wherein A₂ and B are defined above and m may be 1, 2, 3, or 4. Again, the number and concentrations of the cyclic compounds is dependent upon a variety of factors such as the structure of diacid H-A-H, the structure of the organic compound X—B—X₁, and the conditions used to facilitate the reaction to produce the composition. The cyclic compounds of formula I-B may constitute up to about 35 weight percent, typically about 1 up 30 weight percent, of the total weight of the above-described light absorbing composition.

[0047] The polymer compositions of Formula I, Ia, and Ib and the cyclic compositions of formulas I-A, I-B and I-C are referred to as “polydyes” herein when they absorb visible light thus rendering them strongly colored.

[0048] The invention further relates to a thermoplastic polymeric composition which comprises a thermoplastic polymer blended with at least one light absorbing linear polymeric composition of Formula I, Ia or Ib above which, as noted above, contain or comprise one or more cyclic compounds having the general formula I-A. The thermoplastic polymeric composition is usually selected from polyesters, polyolefins, polyamides, polyimides, polyvinyl chloride, polyurethanes, polycarbonates, cellulose esters, polyacrylates, polyvinylesters, polyester-amides, polystyrene, polyacrylonitrile-butadiene- styrene and polystyrene-acrylonitrile. The preferred thermoplastic polymeric composition comprises the light-absorbing polymeric compositions of Formula Ia.

[0049] The invention also relates to some of the diacidic light absorbing monomers used to prepare the light absorbing polymeric composition of Formula I, Ia, or Ib.

[0050] Preferred azo compounds useful in the practice of the invention correspond to Formula VI

R₆—N═N—Z   VI

[0051] wherein R₆ is the residue of an aromatic or heteroaromatic amine which has been dizaotized and coupled with a coupling component H—Z and is preferably derived from the aromatic and heteroaromatic amine classes of aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino-2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz- 2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino- 1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide with said aromatic and heteroaromatic ring systems being unsubstituted or substituted with one or more groups selected from C₁—C₁₀ alkyl, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl, carboxy, halogen, C₁—C₆ alkoxycarbonyl, formyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, dicyanovinyl, C₃—C₈-cycloalkanoyl, thiocyano, trifluroacetyl, cyano, carbamoyl, —CONH C₁—C₆ alkyl, CONHaryl, CON(C₁—C₆ alkyl)₂, sulfamoyl, SO₂NH C₁—C₆ alkyl, SO₂N(C₁—C₆ alkyl)₂, SO₂NHaryl, SO₂NH C₃—C₈ cycloalkyl, CONH C₃—C₈ cycloalkyl, aryl, aroyl, —NHSO₂ C₁—C₆ alkyl, —N(C₁—C₆ alkyl)SO₂ C₁—C₆ alkyl, —NHSO₂ aryl, NHCO C₁—C₆ alkyl, NHCO C₃—C₈ cycloalkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHCONH C₁—C₆ alkyl, NHCONHaryl, N(C₁—C₆ alkyl)aryl, arylazo, heteroaryl, aryloxy, arylthio, C₃—C₈ cycloalkoxy, heteroarylazo, heteroarylthio, arylsulfonyl, tricyanovinyl, aryloxysulfonyl, C₁—C₆ alkylsulfonyl, trifluoromethyl, fluorosulfonyl, trifluoromethylsulfonyl, thiocyano, hydroxy, nitro or CH═D, wherein D is the residue of an active methylene compound as defined below.

[0052] Z is the residue of an electron rich coupling component selected from the classes of anilines, 1-aminonaphthalenes, 1,2-dihydroquinolines, 1,2,3,4-teterahydroquinolines, benzmorpholines (3,4-dihydro-2H-1,4-benzoxazine), pyrazolones, pyrazoles, 3-cyano-6-hydroxy-2-pyridones, 2,3-dihydroindoles, indoles, 4-hydroxycoumarins, 4-hydroxy-2-quinolones, imidazo[2,1-b]thiazoles, julolidines (2,3,6,7-tetrahydro-1H, 5H-benzo[ij]quinolizines), 1-oxajulolidines, 1,2,5,6-tetrahydro-4H-pyrrolo[3,2,1-ij]quinolines, 2,6-diamino-3 cyanopyridines, 2-aminothiazoles, 2-aminothiophenes, 5,5-dimethyl-1,3-cyclohexanedione (dimedone), phenols, naphthols, 2,4-pentanediones or acetoacetarylides; with the proviso that the compounds of Formula VI contain two acidic functional groups containing one acidic hydrogen each or contain one sulfamoyl group (—SO₂NH₂) which contains two acidic hydrogens.

[0053] Preferred disazo compounds correspond to Formula VII

R₆—N═N—R₇N═N—Z   VII

[0054] wherein R₆ and Z are as defined above and R₇ is a divalent aromatic or heteroaromatic radical selected from the classes 1,4-phenylene, naphthalene-1,4-diyl, thiazol-2,5-diyl and thiophene-2,5-diyl:

[0055] wherein R₈ is selected from hydrogen or 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, cyano, halogen, —NHCO C₁—C₆ alkyl, —NHCO₂ C₁—C₆ alkyl, —NHCO aryl, —NHCONH aryl or NHCONH C₁—C₆ alkyl; R₉ is selected from hydrogen, C₁—C₆ alkyl, halogen, aryl, heteroaryl; R₁₀ is selected from hydrogen, C₁—C₆ alkoxycarbonyl, cyano, carbamoyl, aryl, arylsulfonyl,aroyl, —CONH C₁—C₆ alkyl, or C₁—C₆ alkylsulfonyl; with the provision that two acidic functional groups containing one acidic hydrogen each or one functional group containing two acidic hydrogens are present on compounds of Formula VII.

[0056] The preferred methine, arylidene, polymethine, azamethine, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline and aryl isoindoline compounds correspond to Formula VIII, VIIIa, VIIIb, IX, X, XI and XII, respectively:

[0057] wherein R₁₁ is the residue of an aniline, 1-naphthylamine, 1,2-dihydroquinoline, 1,2,3,4-tetrahydroquinoline, 1,3,3-trimethyl-2-methyleneindole, 1,3-dihydro-2-methylene-1,1,3-trimethyl-2H-benz[e]indole, imidazo [2,1-b] thiazole, benzomorpholine (3,4-dihydro-2H-1,4, benzoxazine), indole, 2,3-dihydroindole, 2-aminothiazole, julolidine (2,3,6,7-tetrahydro-1H, 5H- benz [ij] quinolizine, 1-oxajulolidine, 4H-pyrrolo [3,2,1-ij]-quinoline, phenol, naphthol, thiophenol, pyrrole, pyrazole, furan, thiophene, carbazole, phenothiazine or phenoxazine compound; R₁₂ is selected from hydrogen, C₁—C₁₀ alkyl, C₃—C₈ alkenyl, C₃— C₈-alkynyl, C₃—C₈ cycloalkyl, aryl, CH₂CH₂O₁₋₃ R₁₃ and C₁—C₄ alkylene- C₃—C₈ cycloalkylene, wherein the C₁—C₆ alkyl groups may be substituted by at least one group selected from carboxy, C₁—C₆ carbalkoxy, C₁—C₆ alkanoyloxy, cyano, hydroxy, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl or aryl; R₁₃ is selected from hydrogen, C₁—C₆ alkoxy or C₁—C₆ alkanoyloxy; wherein D is the residue of an active methylene compound selected from malononitrile, -cyanoacetic acid esters, malonic acid esters, -cyanacetic acid amides, —C₁—C₆ alkylsulfonylacetonitriles, -arylsulfonylacetonitriles, —C₁—C₆ alkanoylacetonitriles, -aroylacetonitriles, -heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis (dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups containing one acidic hydrogen each, or a functional group containing two acidic hydrogens are present in compounds of Formula VIII, VIIIa, VIIIb, IX, X, XI, and XII.

[0058] Preferred azo-methine compounds corresond to Formula XIII

D═HC—R₇—N═N—Z   XIII

[0059] wherein D, R₇ and Z are as defined previously. The bis-azo compound corresponds to Formula VIIa

R₆—N═N—Y₁N═N—R₆   VIIa

[0060] wherein R₆ is as defined above and Y₁ is the residue of a bis coupling component selected from the classes of anilines, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro-2H-1, 4-benzoxazines), 3-cyano-6-hydroxy-2-pyridones, 2,6-diaminopyridines, 2,3-dihydroindoles, naphthylamines, 2-aminothiazoles, or a combination of these; with the provision the compounds of Formula VIIa contain two acidic functional groups containing one acidic hydrogen each or contain one sulfamoyl group (—SO₂NH₂) which contains two acidic hydrogens.

[0061] Several diacid monomers which are described in U.S. Pat. Nos. 4,804,719 and 3,689,501 are useful in the practice of the invention, including various anthraquinones, anthrapyridones, anthraisothiazoles, anthrapyrimidines, anthrapyrimidones, phthaloylacridones, etc.

[0062] Some of the preferred anthraquinone, anthrapyridone and anthrapyrimidine compounds correspond to the light absorbing compounds of Formulae XIV- XIXf

[0063] wherein R₁₄ is selected from the group consisting of hydrogen, 1-4 groups selected from amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, halogen, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, NHCO C₁—C₆ alkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl, C₁—C₆ alkoxycarbonyl, aryloxy, arylthio, heteroarylthio, cyano, nitro, trifluoromethyl, thiocyano, SO₂C₁—C₆ alkyl, SO₂ aryl, —SO₂NH C₁—C₆ alkyl, —SO₂N(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON(C₁—C₆ alkyl)₂, CON(C₁—C₆ alkyl) aryl, C₁—C₆ alkyl, furfurylamino, tetrahydrofurfurylamino, 4-(hydroxymethyl) cyclohexanemethylamino,

[0064] or hydroxy; Q and Q′ are independently selected from—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; R₁₅ is selected from hydrogen, cyano, C₁—C₆ alkylamino, C₁—C₆ alkoxy, halogen, arylthio, aryl, heteroaryl, heteroarylthio, C₁—C₆ alkoxycarbonyl, aroyl or arylsulfonyl; R₁₆ is selected from hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; R₁₆ is selected from the group consisting of hydrogen, one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; wherein each C₁—C₆ alkyl group and C₁—C₆ alkyl group which is a portion of another group may contain at least one substituent selected from hydroxy, cyano, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkoxy, C₁—C₆ alkylcyclohexyl, hydroxmethyl cyclohexyl, aryl and heteroaryl; with the provision that two acidic groups containing one acidic proton each or one acidic group containing two acidic hydrogens be present in the compounds of Formula XIV-XIXf.

[0065] Typical coupler residues which are represented by Z above in Formulae VI, VII, XIII for the classes of azo, disazo and azo-methine compounds, respectively include:

[0066] wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O— C₂—C₆ alkylene-OH, O—C₂—C₆ alkylene-C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene-C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄, NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

[0067] wherein R⁵′, R₁₆′ and Q are as defined above; R₁₈ and R₁₉ are independently selected from hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

[0068] wherein Q₂ is selected from a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.

[0069] Typical electron, rich aromatic residues which are represented by R₁₁ in Formulae VIII- XII include:

[0070] wherein R₂₆ is selected from the group consisting of hydrogen, a group selected from C₁—C₆ alkoxycarbonyl, CO₂H, C₁—C₆ alkyl or C₁—C₆ alkoxy; wherein R₁₇-R₂₃ are as defined previously.

[0071] Preferred coumarin compounds useful in the practice of the invention correspond to the following formulae:

[0072] wherein Z₃ is selected from cyano, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkylsulfonyl, arylsulfonyl, aryl, heteroaryl, formyl, aroyl, C₁—C₆ alkanoyl or-CH═D, wherein D, R₁₇, R₁₈ and R₁₉ are as defined previously with the provision that the coumarin compounds contain two acidic functional groups containing one acidic hydrogen each or contain one sulfamoyl (—SO₂NH₂) group which contains two acidic hydrogens.

[0073] Typical coupler residues which are represented by Y₁ in Formula VIIa above include those of the formula (Z₁-L₁-Z₂) wherein Z₁ and Z₂ are independently selected from

[0074] wherein L₁ is bonded to the nitrogen atom of Z₁ and Z₂; wherein L₁ is selected from C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, arylene, C₁—C₄ alkylene-C₃—C₈ cycloalkylene-C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, C₂—C₄ alkylene-O-arylene-O—C₂—C₄ alkylene, —C₂—C₄ alkylene O₁₋₃— C₂—C₄ alkylene, C₂—C₄ alkylene-S—C₂—C₄ alkylene, C₂—C₄ alkylene-SO₂—C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ C₁—C₆ alkyl)—C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ aryl)-C₂—C₄ alkylene, C₂—C₄ alkylene-OCO₂—C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C-arylene-CO₂—C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C—C₁—C₁₂ alkylene-CO₂—C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C—C₃—C₈ cycloalkylene-CO₂—C₂—C₄ alkylene, C₂—C₄ alkylene-NHCO—C₂—C₄ alkylene and C₂—C₄ alkylene-NHSO₂—C₂—C₄ alkylene; wherein R₁₇, R₁₈, R₂₀, R₂₁, R₂₂, and R₂₃ are as defined previously.

[0075] In the above definitions it is intended that in the terms C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkylthio, C₁—C₆ alkylsulfonyl, C₁—C₆ alkanoyl, —CONH C₁—C₆ alkyl, —SO₂NH C₁—C₆ alkyl, —CON(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl)₂, —NHSO₂ C₁—C₆ alkyl, —N(C₁—C₆ alkyl) SO₂ C₁—C₆ alkyl, etc. unless otherwise stated that the C₁—C₆ alkyl portion of the group refers to a straight or branched chain alkyl group containing one to six carbon atoms and these substituted with one or more groups selected from carboxy, cyano, —SO₂NH₂, SO₂NH C₁—C₆ alkyl, cyano, fluorine, chlorine, C₁—C₆ alkoxy, aryloxy, aryl, heteroaryl, arylthio, heteroarylthio, C₃— C₈-cycloalkyl, -O₂C C₁—C₆ alkyl or—CO₂ C₁—C₆ alkyl.

[0076] The terms C₁—C₄ alkylene, C₂—C₄ alkylene, C₁—C₆ alkylene, C₂—C₆ alkylene, and C₂—C₁₂ alkylene are used to refer to divalent aliphatic hydrocarbon radicals containing one to four carbon atoms, two to four carbon atoms one to six carbon atoms, two to six carbon atoms, or two to twelve carbon atoms, respectively, and these optionally substituted with one or more groups selected from C₁—C₆ alkoxy, hydroxy, —O₂C C₁—C₆ alkyl, carboxy, CO₂ C₁—C₆ alkyl, chlorine, fluorine, aryl or aryloxy.

[0077] The terms C₃—C₈ cycloalkyl and C₃—C₈ cycloalkylene are used to refer to fully saturated monovalent and divalent cycloaliphatic radicals, respectively, and these substituted by one or more C₁—C₆ alkyl groups.

[0078] The terms C₃—C₈ alkenyl and C₃—C₈ alkynyl are used to refer to straight or branced hydrocarbon radicals containing at least one double bond or at least one triple bond, respectively.

[0079] In the terms aryl, NH aryl, aryloxy, aroyl, arylthio, arylsulfonyl, aryloxysulfonyl, —N(SO₂ aryl)—, —N(CO aryl)—, NHCO aryl, —NH CONH aryl, NHSO₂, aryl, etc., the aryl portion of the group represents phenyl and naphthyl and these substituted with one or more groups selected from—CO₂H, C₁—C₆ alkyl, CO₂ C₁—C₆ alkyl, SO₂NH₂, SO₂NH C₁—C₆ alkyl, hydroxy, O C₁—C₆ alkyl, S C₁—C₆ alkyl, phenyl, O-arylene-CO₂H, —S-arylene-CO₂H, SO₂ arylene-CO₂H, halogen, NHSO₂ C₁—C₆ alkyl, trifluoromethyl, NH CO C₁—C₆ alkyl, cyano, or 1(H)-1,2,4-triazol-3-ylthio.

[0080] The term arylene is used to represent 1,2-, 1,3-, and 1,4- phenylene and these optionally substituted with one or more groups mentioned above as possible substituents on the aryl radical.

[0081] The term “heteroaryl” is used to describe a 5 or 6 membered heterocyclic aromatic ring containing one oxygen atom, and/or one sulfur atom, and/or up to three nitrogen atoms, said heterocyclic aryl ring optionally fused to one or two phenyl rings or another 5 or 6-membered heteroaryl ring. Examples of such ring systems include thienyl, furyl, pyrrolyl, imidazolyl, pyrazolyl, thiazolyl, isothiazolyl, oxazolyl, isoxazolyl, triazolyl, thiadiazolyl, oxadiazolyl, tetrazolyl, thiatriazolyl, oxatriazolyl, pyridyl, pyrimidyl, pyrazinyl, pyridazinyl, thiazinyl, oxazinyl, triazinyl, thiadiazinyl, oxadiazinyl, dithiazinyl, dioxazinyl, oxathiazinyl, tetrazynyl, thiatriazinyl, oxatriazinyl, dithiadiazinyl, imidazolinyl, dihydropyrimidyl, tetrahydropyrimidyl, tetrazolo [1,5-b]-pyridazinyl and purinyl, benzoxazolyl, benzothiazolyl, benzimidazolyl, indolyl, and the like and those rings substituted with one or more substituents listed above in the definition of the term “aryl”.

[0082] The term halogen is used to refer to fluorine, chlorine, bromine and iodine.

[0083] In the above definitions the unsubstituted and substituted C₁—C₁₀ alkyl groups or portion of groups mentioned refer to fully saturated hydrocarbon radicals containing one to ten carbon atoms, either straight or branched chain, and such alkyl radicals substituted with one or more of the following: C₃—C₈ cycloalkyl, aryl, hydroxy, cyano, —O—C₂—C₄ alkylene OH, —O—C₂—C₄ alkylene O₂ C—C₁—C₆ alkyl, —S—C₂—C₄ alkylene-OH, chlorine, fluorine, —O—C₁—C₆ alkyl, —O-aryl, —SO₂ aryl, —SO₂—C₁—C₆ alkyl, 2-pyrrolidino, phthalimidino, phthalimido, succinimido, glutarimido, o-benzoic sulfimide, vinyl sulfonyl, —NHCO C₁—C₆ alkyl, NHCOH, —NHSO₂—C₁—C₆ alkyl, NHSO₂ aryl, —NHCO aryl, —NH—CO₂—C₁—C₆ alkyl, —SO₂NH₂, —SO₂—NH—C₁—C₆ alkyl, —SO₂N— (C₁—C₆ alkyl)₂, —CO₂—C₁—C₆ alkyl, CONH₂, —CONH—C₁—C₆ alkyl, —CO₂-aryl, —CON(C₁—C₆ alkyl)₂, —CONH aryl, —CONH(C₁—C₆ alkyl) aryl, —SO₂N(C₁—C₆ alkyl) aryl, —SO₂—NH—C₃—C₈ cycloalkyl, —CONH—C₃—C₈ cycloalkyl, —OCO₂—C₁—C₆ alkyl, —O C₂—C₄ alkylene CN; groups of the formulae:

[0084] wherein Y₂ is selected from 1,2-phenylene; 1,2 pheylene substituted with C₁—C₆ alkyl, C₁—C₆ alkoxy, halogen, —CO₂H, —CO₂ C₁—C₅ alkyl or nitro; C₂—C₄ alkylene, vinylene, —O CH₂—, —SCH₂—, —CH₂OCH₂—, —OCH₂CH₂—, —CH₂SCH₂—, —NHCH₂—, —NHCH₂CH₂, —N(C₁—C₆ alkyl)CH₂—, NHC(C₁—C₆ alkyl)₂, —N(C₁—C₆ alkyl) CH₂CH₂ or—NHC (aryl)₂—; groups of the formulae:

[0085] —SR₂₅, —SO₂CH₂CH₂SR₂₅, —OCH₂CH₂SR₂₅,

[0086] wherein R₂₆ is selected from hydrogen, C₁—C₁₀ alkyl, C₂—C₄ alkylene-OH, C₂—C₄ alkylene-CO₂H, C₂—C₄ alkylene- CO₂ C₁—C₆ alkyl, chloro, C₁—C₆ alkoxy, C₁—C₄ alkylene-arylene-CO₂H, C₂—C₄ alkylene-O-arylene-CO₂H or C₂—C₄ alkylene-S-arylene-CO₂H and R₅′ R₁₇, R₂₅ and Q are as defined previously:

[0087] The term “light absorbing” is used to indicate the property of absorbing near ultra violet, visible or near infrared light, more particularly absorbing light between the wavelengths of 300-1200 nm, preferably between about 325 nm and 1100 nm, and most preferably between about 325 nm and 1000 nm.

[0088] Typical aromatic amines which are useful as the coupling components to prepare compounds of Formulae VI, VII and VIII and as intermediates for preparing the compounds of Formula VIII, VIIIa, IX, X, XI and XII are as follows:

[0089] wherein Q, R₅′, R₁₇, R₁₈, R₁₉, R₂₀, R₂₁, R₂₂ and R₂₃ are as defined previously.

[0090] Typical diazotizable amines (R₆ NH₂) useful in the preparation of azo, disazo and bis-azo compounds of Formulae VI, VII, and VIIa, respectively, are adequately disclosed in the literature, e.g.:

[0091] M. Weaver and L. Shuttleworth, Dyes and Pigments, 3 (1982) 81-121;

[0092] L. Shuttleworth and M. Weaver, Chem. Appl. Dyes, 1990, 107-63, edited by D. Waring and G. Hallas, Plenum, New York, N.Y.;

[0093] U.S. Pat. Nos. 3,438,961; 3,573,273; 3,639,384; 3,707,532; 3,790,557; 3,816,388; 3,816,392; 3,878,189; 3,980,634; 4,012,372; 4,039,522; 4,049,643; 4,083,684; 4,083,844; 4,097,475; 4,105,655; 4,119,621; 4,140,683; 4,180,503; 4,189,428; 4,207,233; 4,211,696; 4,264,495; 4,283,332; 4,400,318; 4,431,585; 4,456,551; 4,487,719; 4,542,207; 4,564,673; 4,619,991; 4,621,136; 4,650,861; 4,668,775; 4,734,490; 4,751,288; 4,760,133; 4,764,600; 4,837,269; 4,841,036; 4,843,153; 4,888,432; 4,960,874; 5,037,966; 5,132,411; 5,144,015; 5,283,326; 5,296,325; 5,352,774.

[0094] Typical coupling components H—Z useful in preparing azo compounds, disazo and azo-methine compounds of Formula VI, VII and XIII, respectively, are disclosed in the literature, e.g: H. R. Schwander, Dyes and Pigments, 3(1982) 133-160; L. Shuttleworth and M. Weaver, Chem. Appl. Dyes, 1990, 107-63, edited by D. Waring and G. Hallas, Plenum, New York, N.Y.; U.S. Pat. Nos. 3,639,384; 3,639,385; 3,657,215; 3,673,169; 3,816,388; 3,829,410; 3,919,188; 3,950,130; 3,980,634; 4,041,025; 4,097,475; 4,119,621; 4,179,435; 4,234,482; 4,283,332; 4,341,700; 4,400,318; 4,431,585; 4,396,547; 4,619,992; 4,642,339; 4,650,861; 4,668,775; 4,764,600; 4,837,269; 4,843,153; 5,235,047; 5,283,326; 5,352,774.

[0095] Typical active methylene compounds useful in the preparation of methine, arylidene, polymethine, azamethine and azo-methine compounds corresponding to Formulae VIII, VIIIa, VIIIb, IX and XIII, respectively, are disclosed in the literature, e.g. U.S. Pat. Nos. 4,338,247; 4,617,373; 4,617,374; 4,707,537; 4,749,774; 4,826,903; 4,845,187; 4,950,732; 4,981,516 and 5,283,326.

[0096] According to the present invention the light-absorbing polymeric and cyclic compositions are incorporated into a wide variety of thermoplastic polymers using conventional techniques, e.g. solution or melt blending, such as those employed to incorporate other additives in such polymers (see R. Gachter and H. Mueller, Editors: Plastics Additives Handbook, Hansu Publishers, New York, 1985, pp. 507-533; 729-741). For example, the light absorbing polymeric and cyclic compositions may be dry blended in the form of pellets or powders with or without adhesion promoters or dispersing agents. This premix can be subsequently processed on extruders or injection molding machines. Other conventional additives such as plasticizers, nucleating agents, flame retardants, lubricants, etc. may also be present in the final thermoplastic composition.

[0097] A wide range of thermoplastic polymers useful for blending with the light absorbing polymeric and cyclic compositions are known in the art and includes the homopolymers, copolymers and blends of polyesters, e.g., poly(ethylene terephthalate); polyolefins, e.g., polypropylene, polyethylene, linear low density polyethylene, polybutylene, and copolymers made from ethylene, propylene and/or butylene; copolymers from acrylonitrile, butadiene, and styrene; copolymers from styrene and acrylonitrile; polyamides, e.g., Nylon 6 and Nylon 66; polyvinyl chloride; polyurethanes; polyvinylidene chloride; polycarbonates; cellulose esters, e.g., cellulose acetate, propionate, butyrate, or mixed esters; polyacrylates, e.g., poly(methyl methacrylate); polyimides; polyester-amides; polystyrene; and mixtures or blends thereof etc.

[0098] It should also be appreciated that a multiplicity of colors may be obtained by combining individual colors, e.g., subtractive colors such as yellow, magenta and cyan according to known color technology (see N. Ohta, Photographic Science and Engineering. Volume 15, No. 5, September-October 1971, pp. 395-415).

[0099] The particular chromophore groups present will, of course, determine the color (hue+value+chroma) of the colored polymer composition and finally the color (hue+value+chroma) of the thermoplastic polymer blends of the present invention. A large gamut of colors may be obtained, as noted above.

[0100] The actual amount of the light absorbing polymers used in combination with thermoplastic polymer will depend upon the inherent tinctorial strength of the chromophore used to prepare the light absorbing polymer, the mole % of the light absorbing monomer used to prepare the light absorbing polymer and the required level of light absorption necessary to achieve a certain property. Typically, the amount of light-absorbing polymer added to the thermoplastic polymer is such that the total amount of light-absorbing polymer in the final thermoplastic blend is from about 0.001% by weight to about 20% by weight, preferably from about 0.01% by weight to about 10% by weight. The final thermoplastic polymer blends thus provided are useful as a variety of molded and extruded articles, including thick and thin plastic films, plastic sheeting, molded plastic articles, containers and fibers, and the like.

[0101] When the light-absorbing polymeric compositions absorb visible light they may be used to impart light or heavy shades of a variety of colors to thermoplastics. Certain compounds which possess unique visible light-absorbing properties are useful also as toners in imparting a desirable neutral to slightly blue hue to polyesters having a yellow appearance as described in U.S. Pat. No. 5,384,377, which discloses the copolymerization of certain thermally stable colorants for this purpose during polyester manufacture. Some of the infra-red absorbing polymeric and cyclic compositions are useful in imparting invisible markings to thermoplastics as described in U.S. Pat. No. 5,461,136, wherein the infrared absorbing compounds are fluorescent in the near infrared and are copolymerized into the thermoplastic condensation polymer during manufacture. The ultra violet absorbing polymeric and cyclic compositions may be used to impart ultra violet (UV) light screening properties to the thermoplastics; to serve as optical brighteners for the thermoplastics or to serve as UV stabilizers for the polymers themselves or for other light absorbers such as colorants.

[0102] The weight average molecular weights (Mw) and the number average molecular weights (Mn) of the polymeric compositions were determined using gel permeation chromatography (GPC) analysis.

[0103] The following examples illustrate further the practice of the invention.

EXAMPLE 1

[0104] A mixture of 1,5-bis(2-carboxyphenylthio) anthraquinone (25.60 g, 0.05 mole), 1,2-ethanediol, dimethanesulfonate (10.90 g, 0.05 mole), potassium carbonate (13.82 g, 0.10 mole) and N-methyl-2-pyrrolidinone (NMP) (400 mL) was heated with stirring at 125° C. for 1.0 hr. The reaction mixture was poured into methanol (600 mL) with stirring. The yellow polymeric product was collected by filtration and washed with methanol until filtrate was essentially clear. The methanol- wet filter cake was slurried in 1.0 L of water, absorbing properties are useful also as toners in imparting a desirable neutral to slightly blue hue to polyesters having a yellow appearance as described in U.S. Pat. No. 5,384,377, which discloses the copolymerization of certain thermally stable colorants for this purpose during polyester manufacture. Some of the infra-red absorbing polymeric and cyclic compositions are useful in imparting invisible markings to thermoplastics as described in U.S. Pat. No. 5,461,136, wherein the infrared absorbing compounds are fluorescent in the near infrared and are copolymerized into the thermoplastic condensation polymer during manufacture. The ultra violet absorbing polymeric and cyclic compositions may be used to impart ultra violet (UV) light screening properties to the thermoplastics; to serve as optical brighteners for the thermoplastics or to serve as UV stabilizers for the polymers themselves or for other light absorbers such as colorants.

[0105] The weight average molecular weights (Mw) and the number average molecular weights (Mn) of the polymeric compositions were determined using gel permeation chromatography (GPC) analysis.

[0106] The following examples illustrate further the practice of the invention.

EXAMPLE 1

[0107] A mixture of 1,5-bis(2-carboxyphenylthio) anthraquinone (25.60 g, 0.05 mole), 1,2-ethanediol, dimethanesulfonate (10.90 g, 0.05 mole), potassium carbonate (13.82 g, 0.10 mole) and N-methyl-2-pyrrolidinone (NMP) (400 mL) was heated with stirring at 125° C. for 1.0 hr. The reaction mixture was poured into methanol (600 mL) with stirring. The yellow polymeric product was collected by filtration and washed with methanol until filtrate was essentially clear. The methanol- wet filter cake was slurried in 1.0 L of water, the mixture acidified by the addition of acetic acid and the yellow product was collected by filtration, washed with hot water and dried in air (yield- 21.16 g). By gel permeation chromatography (GPC) the polymeric product has a weight average molecular weight of 6,083, and number average molecular weight of 3,000 and a polydispersity value of 2.03.

EXAMPLE 2

[0108] A mixture of a blue anthraquinone compound (19.65 g 0.03 mole) containing two carboxy groups and having the following structure:

[0109] 1,2-ethanediol, dimethanesulfonate (6.54 g, 0.03 m),potassium carbonate (8.28 g, 0.06 mole) and N,N-dimethylformamide (DMF) (100 mL) was heated with stirring at about 95° C. for 1.5 hr. The reaction mixture became too thick to stir effectively and additional DMF (50 mL) was added to facilitate stirring. Stirred about 15 min. longer at about 95° C., and then added methanol (100 mL) with good stirring to the slightly cooled reaction mixture. The blue polymeric product was collected by filtration and washed with methanol. The methanol-wet filter cake was added to water (600 mL) and the mixture was acidified with acetic acid, and then the polymeric product was collected by filtration, washed with water and dried in air (yield 18.18 g). By GP analysis the blue polymer had a molecular weight average of 3,038, a number average molecular weight of 1,814 and a polydispersity of 1.67.

EXAMPLE 2a

[0110] A mixture of 1,5-bis (isobutylamino)-4,8-dibromoanthraquinone (25.3 g, 0.05 mole), thiosalicylic acid (23.1 g, 0.15 mole), anhydrous K₂CO₃ (20.7 g, 0.15 mole), cupric chloride dihydrate (1.2 g) and DMF (250 mL) was heated at 90-95° C. with stirring for 2.0 hours. Thin layer chromatography (TLC) using 1:1 tetrahydrofuran (THF):cyclohexane showed complete conversion of the red starting material to the desired blue polar product. The reaction mixture was allowed to cool and then was drowned into water (800 mL). The blue solid was precipitated by acidification with acetic acid with stirring. The mixture was heated to about 60° C. with occasional stirring and the solid was collected by filtration, washed with hot water and dried in air. Further purification was accomplished by reslurrying the product in hot methanol (300 mL), allowing to cool to room temperature, collecting by filtration, washing with methanol and air drying to yield the starting material (31.5 g) for Example 2.

EXAMPLE 2b

[0111] 1,5-Bis(isobutylamino)anthraguinone (28.0 g, 0.08 mole) was added to DMF (300 mL) and the mixture stirred at room temperature. A solution of 1,3-dibromo-5,5-dimethylhydantoin (23.0 g, 0.08 m) dissolved in DMF (75.0 mL) was added dropwise to the reaction mixture while warming to about 50° C. After complete addition of the brominating agent, the reaction mixture was heated at 50-60° C. for 1.5 hours, allowed to cool and then drowned by gradual addition to water (500 mL) with stirring. The red product was collected by filtration, washed with water and dried in air. The yield of product was 39.6 g and field desorption mass spectrum analysis (FDMS) showed the product to be 1,5-bis(isobutylamino)-4,8-dibromoanthraquinone used as the intermediate in Example 2a.

EXAMPLE 2c

[0112] A mixture of 1,5-dichloroanthraquinone (69.5 g, 0.25 mole), isobutylamine (100 g, 1.4 mole) and 2-ethoxyethanol (400 mL) was heated at reflux for 36.0 hours and allowed to cool. Methanol (400 mL) was added to make the mixture containing the crystallized product more stirrable. The dark red product was collected by filtration, washed with methanol, reslurried in hot methanol and allowed to cool, collected by filtration, washed with methanol and dried in air (yield—67.7 g). FDMS showed the product to be the 1,5-bis(isobutylamino)anthraquinone in high purity which was used as the starting material for Example 2b.

EXAMPLE 3

[0113] A mixture of an azo compound (2.93 g, 0.005 m) containing two 1(H)-1,2,4-triazol-3-thio groups and having the following structure:

[0114] 1,2-ethanediol, dimethanesulfonate (1.08 g, 0.005 mole), potassium carbonate (1.50 g) and DMF (25.0 mL) was heated at about 95° C. with stirring for 2.5 hrs. The reaction mixture was drowned into methanol (150 mL) and the red polymeric product was collected by filtration, washed with water containing a little acetic acid and then washed with hot water and dried in air (yield- 2.35 g). The polymer by GPC analysis had a weight average molecular weight of 5,396, a number average molecular weight of 3,044 and a polydispersity value of 1.77.

EXAMPLE 4

[0115] Eastar® PETG copolyester 6763, a poly(ethylene-1,4-cyclohexanedimethylene) terephthalate, (Eastman Chemical Co.) (400 g. of previously dried pellets) was dry blended with the yellow anthraquinone polymeric composition (0.12 g) of Example 1. The blend was extruded with a C. W. Brabender ¾ in. extruder, equipped with a mixing screw, at 250° C. into a water bath and the extrudate pelletized.

[0116] The pellets were redried at 70° C. for about 17 hrs. at a pressure of about 1-5 torr. A portion of the dried pellets (1.40 g) was pressed into a 18-20 mil film at 250° C. using a 2-inch diameter circular mold in a Pasadena Hydraulic, Inc. press using 12,000 pounds ram force (4 inch ram). A transparent yellow film was produced with excellent color development, which contained about 300 ppm by weight of the yellow polymeric composition.

EXAMPLE 5

[0117] Example 4 was repeated using 0.12 g of the blue anthraquinone polymeric composition of Example 2 to give a bright blue transparent copolyester film with good color development.

EXAMPLE 6

[0118] Example 4 was repeated using 0.12 g of the red azo polymeric composition of Example 3 to produce a bright red transparent film having good color development.

EXAMPLE 7

[0119] A mixture of a blue anthraquinone compound (3.46 g, 0.005 mole) containing two acidic 1(H)-1,2,4-triazol-3-ylthio groups and having the following structure

[0120] 1,2-ethanediol, dimethanesulfonate (1.09 g, 0.005 mole) DMF (30 mL) and potassium carbonate (1.5 g) was heated with stirring at about 95° C. for 2.0 hours and then drowned into methanol (100 mL). The blue polydye was collected by filtration and washed with methanol. The methanol-wet cake was reslurried in water (400 mL) and the stirred mixture was acidified by addition of acetic acid and heated to about 60° C. The final polymeric product was collected by filtration, washed with water and dried in air (yield—1.5 g). Absorption maxima were observed at 594,636 nm in a solution of DMF in the visible light absorption spectrum. By GPC, the polydye has a weight average molecular weight (Mw) of 3,769, a number average molecular weight (Mn) of 2,119 and a polydispersity of 1.78.

EXAMPLE 7a

[0121] A mixture of 1,5-bis[(3-acetoxy-2,2-dimethylpropyl)amino-4,8-dibromoanthraquinone (6.50 g, 0.01 mole) (product of Example 2—Invention Report Docket No. 70524), 3-mercapto-1(H)-1,2,4-triazole (3.03 g, 0.03 mole), potassium carbonate (4.15 g, 0.03 mole), cupric chloride dihydrate (0.65 g) and DMF (100 mL) was heated 14 hours at about 100-105° C. The reaction mixture was drowned into a mixture of water (400 mL) and 10% aqueous solution of hydrochloric acid (200 mL). The blue product was collected by filtration, washed with hot water and dried in air (yield—6.58 g). FDMS supported the desired structure of the starting anthraquinone compound for Example 7.

EXAMPLE 8

[0122] A mixture of blue anthraquinone compound (2.48 g, 0.0033 mole) having the following structure

[0123] 1,2-ethanediol, dimethanesulfonate (0.73 g, 0.0033 mole), potassium carbonate (0.5 g) and DMF (30.0 mL) was heated at about 95° C. for 3.0 hours. The reaction mixture was drowned into methanol (150 mL) with stirring and the blue polydye product was collected by filtration and washed with methanol. The methanol-wet cake was reslurried in water (200 mL) and the mixture acidified with acetic acid. Collecting the blue solid by filtration, washing with hot water and air drying gave 1.21 g of polydye product, which has absorption maxima at 606,652 nm in DMF in the visible absorption spectrum, a weight average molecular weight of 4,453, a number average molecular weight of 2,721 and a polydispersity of 1.6.

EXAMPLE 8a

[0124] A mixture of 1,5-bis [(3-acetoxy-2,2-dimethylpropyl)amino]-4,8-dibromoanthraquinone (19.56 g, 0.03 mole), p-hydroxybenzenethiol (17.64 g, 0.14 mole), potassium carbonate (19.32 g, 0.14 mole), cupric chloride dihydrate (1.0 g) and DMF (150 mL) was heated and stirred at 90-95° C. for 7.0 hours and then at 120° C. for about 2.0 additional hours. TLC (50:50 THF: cyclohexane) showed mostly the desired blue product, but still a small amount of violet half-reacted product was present. The reaction mixture was drowned into methanol (500 mL) and the mixture allowed to cool. After crystallization, the blue solid was collected by filtration, washed with methanol, washed with hot water and then dried in air (yield—17.6 g). FDMS supported the desired structure of the starting anthraquinone compound for Example 8. In the visible light absorption spectrum in DMF, a maximum absorbance (λmax) was observed at 652 nm (extinction coefficient ε of 24,638).

EXAMPLE 9

[0125] A mixture of 1,4-bis-(2,6-dimethyl-4-hydroxyanilino)anthraquinone (4.78 g, 0.01 mole) (Synthesis Example 1 of U.S. Pat. No. 3,918,976), 1,2-ethanediol, dimethanesulfonate (2.18 g, 0.01 mole), potassium carbonate (3.0 g) and DMF (60 mL) was heated at 90-95° C. with stirring for 4.0 hours. After drowning the reaction mixture into methanol (300 mL), the product was collected by filtration and washed with methanol until filtrate was essentially colorless. The methanol-wet cake was reslurried in 100 mL water and acidified by adding acetic acid with stirring. After heating to about 50° C., the product was collected by filtration, washed with hot water and dried in air (yield—1.2 g). By GPC, the blue polydye had a weight average molecular weight (Mw) of 2,764, a number average molecular weight (Mn) of 1,607 and a polydispersity of 1.72. In DMF, the visible light absorption maxima were at 586,630 nm.

EXAMPLE 10

[0126] A mixture of an anthraquinone diacidic compound (1.52 g, 0.002 mole) having the following structure

[0127] 1,2-ethanediol, dimethanesulfonate (0.44 g, 0.002 mole), potassium carbonate (0.5 g) and DMF (8.0 mL) was heated at about 95° C. with occasional stirring for 20 hours. The reaction mixture was downed into methanol (50 mL) and the product was collected by filtration, washed with methanol, water plus acetic acid, hot water and then dried in air (yield—1.05 g). The blue polydye had a weight average molecular weight (Mw) of 3,586, a number average molecular weight (Mn) of 1,867 and a polydispersity value of 1.92. In the visible light absorption spectrum, maxima of absorbance occurred at wavelengths of 605 and 647 nm in DMF.

EXAMPLE 10a

[0128] A mixture of 1,5-bis-(4-methylcyclohexanemethylamino)-4,8-dibromoanthraquinone (20.0 g, 0.0324 mole), thiosalicyclic acid (11.55 g, 0.075 mole), potassium carbonate (10.35 g, 0.075 m), cupric chloride dihydrate (1.0 g) and DMF (175 mL) was heated at about 95° C. for 4.0 hours and then drowned into acetone (400 mL). The solid which crystallized was collected by filtration, washed with acetone until the filtrate was no longer red. The dipotassium salt of the diacidic anthraquinone compound was dissolved by adding to water (500 mL) and stirring. The blue product which was precipitated by acidification with acetic acid was collected by filtration, washed with hot water and then dried in air (yield—21.5 g). FDMS indicated the structure to be consistent with that given above in Example 10 for the starting diacidic anthraquinone compound.

EXAMPLE 10b

[0129] A solution of 1,5-bis-(4-methylcyclohexanemethylamino)anthraquinone (65.0 g, 0.142 mole) dissolved in DMF (1.0 L) by stirring at about 55° C. was treated with a solution of N-bromosuccinimide (50.5 g, 0.284 mole) in DMF (200 mL). After addition was completed, the bromination reaction was completed by heating at 55-60° C. for 2.0 hours. Water (1.0 L) was added to precipitate the red product which was collected by filtration, washed with water and dried in air. After being reslurried in hot methanol and cooling, the product was collected by filtration, washed with a little methanol and air dried (yield—84.0 g). FDMS indicated the structure to be that of the starting, dibrominated anthraquinone compound of Example 10a.

EXAMPLE 10c

[0130] A mixture of 1,5-dichloroanthraquinone (48.0 g, 0.17 mole), 4-methyl-1-aminomethylcyclohexane (88.9 g, 0.70 mole), 2-ethoxyethanol (400 mL) was stirred and heated at reflux for 35.0 hours and the reaction mixture allowed to cool. The red product was precipitated by the addition of methanol and was the collected by filtration, washed with methanol and dried in air (yield—66.0 g). FDMS indicated the product to be the starting anthraquinone compound for Example 10b.

EXAMPLE 11

[0131] A mixture of diacidic anthraquinone compound (0.69 g, 0.001 m) having the following structure

[0132] 1,6-hexanediol, dimethanesulfonate (0.27 g, 0.001 mole), potassium carbonate (0.3 g) and DMF (5.0 mL) was heated with occasional stirring for 2.5 hours at about 95° C. The reaction mixture was drowned into methanol (100 mL) and the product collected by filtration, washed with methanol, water containing a little acetic acid and then finally with hot water and air dried (yield—0.45 g). The blue polydye had an absorption maximum at 610 nm in DMF, a weight average molecular weight of 3,311 a number average molecular weight of 1,272 and a polydispersity value of 2.63.

EXAMPLE 11a

[0133] A mixture of 1,8-di-(2-carboxyphenylthio)-4,5-dinitroanthraquinone (4.00 g, 0.0066 mole), aniline (2.5 g) and nitrobenzene (30.0 mL) was heated at reflux with stirring for 5.0 hours. The reaction mixture was drowned into hexane and the hexane decanted. The product was washed again by adding hexane, stirring and decanting. The crude product was slurried in acetone and heated to reflux and the blue product collected by filtration, washed with water and air dried (yield—0.75 g). FDMS indicated the product to be mostly 1,8-dianilino-4,5-di-(2-carboxyphenylthio)anthraquinone, the starting diacidic, anthraquinone compound for Example 11.

EXAMPLE 11b

[0134] The potassium salt of thiosalicyclic acid (4.75 g, 0.03 mole) was made by addition to DMF (75 mL) and heating in the presence of potassium carbonate (8.70 g, 0.06 mole) for 2.0 hours at about 95° C. The cooled mixture was added to a solution of 1,8-dichloro-4,5-dinitroanthraquinone (5.51 g, 0.015 mole) dissolved in DMF (150 mL) at about 0-5° C. with stirring. The reaction mixture was allowed to warm to about 25° C. with stirring continued for 2.0 hours and then poured into water. The product was obtained in essentially quantitatively yield by slowly acidifying with 10% hydrochloric acid and was then collected by filtration, washed with water and dried in air. FDMS indicated the product to be mostly the starting anthraquinone compound used in Example 11a.

EXAMPLE 12

[0135] A mixture of the diacidic anthraquinone compound (0.85 g. 0.0015 m) having the following structure

[0136] 1,6-hexanediol, dimethanesulfonate (0.41 g, 0.0015 m), potassium carbonate (0.5 g) and DMF (5.0 mL) was heated at about 95° C. for 2.0 hours with occasional stirring. The reaction mixture was drowned into methanol (100 mL) and the blue polydye was collected by filtration, washed with methanol, water containing a little acetic acid and finally hot water and then dried in air (yield—0.62 g). GPC analysis indicated a weight average molecular weight of 20,020, a number average molecular weight of 2,313 and a polydispersity of 8.66. An absorption maximum was observed at 591 nm in the visible light absorption spectrum in DMF.

EXAMPLE 12a

[0137] The anthraquinone diester compound (4.00 g) having the following structure

[0138] 50% aqueous sodium hydroxide (2.40 g) and 2-ethoxyethanol (60 mL) were combined and heated with stirring at about 95° C. for 0.5 hour. Hydrolysis of ester groups appeared to be complete by TLC (50:50 THF:cyclohexane). The reaction mixture was drowned into water (600 mL) and the blue solution acidified using acetic acid. The blue solid was collected by filtration washed with water and dried in air (yield—3.80 g). FDMS indicated the structure to be mostly that of the starting diacidic anthraquinone compound in Example 12 plus a small amount of a violet compound probably produced by displacement of the bromine atom with the 2-(ethoxy)ethoxy group.

EXAMPLE 12b

[0139] A mixture of 1-amino-2,4-dibromoanthrquinone (7.62 g, 0.02 mole), dimethyl 5(4-aminophenoxy)isophthalate (9.03 g, 0.03 mole), 1-pentanol (100 mL), potassium acetate 4.0 g), and cupric acetate (0.2 g) was heated at reflux for 4.0 hours and until all of the starting material had been used up as indicated by TLC analysis (20:80 THF:cyclohexane). Several blue components presumed to be a mixture of ester products produced by transesterification were observed. The reaction mixture was drowned into methanol (100 mL) and the product was collected by filtration, washed thoroughly with methanol to remove a red by-product and then washed with water and dried in air (yield—7.81 g). FDMS indicated ions corresponding to the dimethylester, monopentyl ester and dipentylester of the product—the structure of the starting material for Example 12a.

EXAMPLE 12c

[0140] A mixture of dimethyl 5-(4-nitrophenoxy)isophthalate (30.0 g, 0.09 mole), isopropanol alcohol (350 mL) and ethanol wet Raney nickel catalyst (5.0 g) was hydrogenated at 90° C. for 4.0 hours at 1500 psi hydrogen pressure in an autoclave. Isopropanol (100 mL) was added to the reaction mixture from the autoclave and the solid product dissolved by heating. The Raney nickel was removed by hot filtration and the filtrate allowed to cool. The off-white solid was collected by filtration and dried in air (yield—17.8 g). FDMS indicated the product to be dimethyl 5-(4-aminophenoxy)isophthalate used in Example 12b.

EXAMPLE 12d

[0141] A mixture of 1-chloro-4-nitrobenzene (47.1 g, 0.30 mole), dimethyl 5-hydroxyisophthalate (63.0 g, 0.30 mole), anhydrous potassium carbonate (41.4 g), potassium iodide (0.2 g) and DMF (200 mL) was heated at 120-125° C. for 1.5 hours, under a slow nitrogen sweep allowing some distillate to be removed (about 75 mL) via a Dean-Stark trap. Additional DMF (50 mL) was added back to the reaction mixture and heating continued for an additional 1.5 hours while an additional amount of distillate (25 mL) was allowed to collect in the Dean-Stark trap. The reaction mixture was allowed to cool to about 45° C. A heavy slurry of pale yellow product resulted which was diluted further by the addition of an ice-water mixture (350 g) with good stirring. Filtration followed by washing with water and drying in air gave the pale yellow dimethyl 5-(4-nitrophenoxy)isophthalate (90.7 g) (structure supported by FDMS) which was used in Example 12c.

EXAMPLE 13

[0142] A mixture of the diacidic anthraquinone compound (1.26 g, 0.002 mole) having the following structure

[0143] 1,6-hexandiol, dimethanesulfonate (0.58 g, 0.002 mole), potassium carbonate (0.5 g) and DMF (6.0 mL) was heated at 90-95° C. for 2.0 hours with occasional stirring. The reaction mixture was drowned into methanol (100 mL) and the dark blue-green polydye was collected by filtration, washed with methanol, water containing a little acetic acid and finally with water and then dried in air (yield 1.13 g). GPC analysis indicated a weight average molecular weight of 14,776, a number average molecular weight of 2,514 and a polydispersity of 5.88. An absorption maximum was observed at 620 nm in the visible light absorption spectrum in DMF.

EXAMPLE 13a

[0144] A portion (1.72 g, 0.003 mole) of the bromoanthraquinone product of Example 12a, benzenesulfinic acid, Na salt (0.98 g, 0.006 mole), potassium carbonate (1.38 g) and DMF (25 mL) were mixed and the reaction mixture heated with stirring at 90-95° C. for 1.0 hour. A bathochromic shift in color was observed as the 2-bromo substituent was replaced by the 2-phenylsulfonyl group on the anthraquinone nucleus. The greenish-blue solution was drowned into acetone (100 mL) and the solid material was collected by filtration and washed with acetone until the filtrate was pale blue. The acetone-wet solid was added with stirring to water (200 mL) and the mixture acidified with acetic acid. After being heated to about 75° C., the reaction mixture was filtered and the dark blue solid was washed with hot water and dried in air (yield—1.50 g). FDMS indicated the structure to be that of the starting diacidic anthraquinone compound used in Example 13.

EXAMPLE 14

[0145] A mixture of the diacidic anthraquinone compound (1.45 g, 0.003 mole) having the structure

[0146] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.5 g) and DMF (8.0 mL) was heated at about 95° C. for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the blue polydye was collected by filtration and washed with methanol, water containing a little acetic acid and finally hot water and dried in air (yield—1.10 g). GPC analysis indicated a weight average molecular weight of 3,727, a number average weight of 1,031 and a polydispersity of 3.61. Absorption maxima were observed at 623 nm and 585 nm in the visible light absorption spectrum in DMF.

EXAMPLE 15

[0147] A mixture of the diacidic anthraquinone compound (1.50 g, 0.003 mole) having the following structure

[0148] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.5 g) and DMF (8.0 mL) was heated with occasional stirring at about 95° C. for 2.0 hours. The reaction mixture was then drowned into methanol (100 mL) and the blue polydye was collected by filtration, washed with methanol, water containing a little acetic acid, and hot water and then dried in air (yield- 0.90 g). An absorption maximum at 591 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 15a

[0149] To DMF (40 mL) was added 1-amino-2-Br-4-(5-chlorosulfonyl-2-methoxyanilino) anthraquinone (4.0 g) with stirring. When solution appeared to be complete, conc. ammonium hydroxide (4.0 g) was added and stirring was continued at ambient temperature for 30 minutes. TLC using 50:50 THF:cyclohexane indicated complete reaction of the sulfonyl chloride compound to produce the desired sulfonamide. The reaction mixture was drowned into water and the blue product was collected by filtration, washed with water and air dried (yield- 3.8 g). FDMS indicated the structure to be that of the starting compound for Example 15.

EXAMPLE 15b

[0150] To chlorosulfonic acid (100 mL) was added 1-amino-4-o-anisidino-2-bromoanthraquinone (10.0 g, 0.0236 mole) portionwise with good stirring at 25-30° C. After addition was completed, the reaction mixture was stirred at room temperature for 1.0 hour. The reaction mixture was added in a fine stream to cold isopropanol (800 mL) with stirring. The blue product was collected by vacuum filtration on a sintered glass funnel, washed with isopropanol and dried in air (yield- 10.3 g) and used without further purification in Example 15a.

EXAMPLE 16

[0151] A mixture of the diacidic anthraquinone compound (0.58 g, 0.001 m) having the following structure

[0152] 1,2-ethanediol, dimethanesulfonate (0.22 g, 0.001 m), potassium carbonate (0.3 g) and DMF (5.0 mL) was heated at 95° C. for 2.5 hours. The reaction mixture was drowned into methanol (100 mL) and the greenish-blue polydye was collected by filtration, washed with methanol, water containing a little acetic acid and water and then air dried (yield—0.33 g). GPC analysis indicated a weight average molecular weight of 4,144 a number average molecular weight of 1,643 and a polydispersity of 2.52. An absorption maximum at 629 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 16a

[0153] A mixture of 1,8-diamino-2,7-dibromo-4,5-dihydroxyanthraquinone (2.19 g, 0.005 mole), thiosalicyclic acid (1.60 g, 0.104 mole), potassium carbonate (1.5 g) and DMF (25.0 mL) was heated at 95-100° C. for 6.0 hours. A bathochromic shift in color occurred as the two bromine atoms were replaced by the 2-carboxyphenylthio groups. The reaction mixture was drowned into methanol and the solid product was collected by filtration and washed with methanol. The product was dissolved in water (100 mL) and the diacidic anthraquinone which precipitated by addition of acetic acid was collected by filtration, washed with water and dried in air (yield—0.86 g). FDMS indicated the product to be that used as starting material for Example 16.

EXAMPLE 17

[0154] The anthraquinone disulfonyl chloride compound (3.50 g, 0.005 mole) having the following structure

[0155] (prepared according to the procedure of U.S. Pat. No. 5,453,482, Example 2), m-aminobenzoic acid (1.37 g, 0.10 mole), potassium carbonate (2.80 g) and DMF (30 mL) were mixed and the reaction mixture heated at 90-95° C. for 30 minutes. TLC (50:50 THF:cyclohexane) indicated complete reaction of the disulfonyl chloride to produce the disulfonamide derivative. To the reaction mixture were added 1,6-hexanediol, dimethanesulfonate (1.38 g, 0.005 m), potassium carbonate (1.38 g) and heating and stirring were continued for 2.0 hours at 90-95° C. The reaction mixture was drowned into water and acidified with acetic acid. The bright blue polydye was collected by filtration, washed with water and then air dried (yield—2.07 g) and is believed to have the following repeat unit:

[0156] GPC analysis indicated a weight average molecular weight of 5,252, a number average molecular weight of 2,179 and a polydispersity of 2.41. Absorption maxima at 583 nm and 628 nm were observed in the visible light absorption spectrum in DMF.

EXAMPLE 18

[0157] A mixture of the diacidic anthraquinone compound (4.21 g, 0.01 mole) having the following structure

[0158] 1,2-ethanediol, dimethanesulfonate (2.18 g, 0.01 mole), potassium carbonate (2.68 g, 0.02 mole) and DMF (50 mL) was heated and stirred at 90-95° C. for 1.5 hours. The reaction mixture was drowned into water (400 mL) and acidified with stirring and by adding acetic acid. After being heated to about 50° C., the mixture was filtered and the red polydye washed well with water and dried in air (yield—4.47 g). GPC analysis showed the polydye to have a weight average molecular weight of 1,603, a number average molecular weight of 922 and a polydispersity of 1.74. An absorption maximum at 524 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 18a

[0159] A mixture of 1-amino-2,4-dibromoanthraquinone (11.43 g, 0.03 mole), 3-mercapto-1(H)-1,2,4-triazole (9.09 g, 0.09 mole), potassium carbonate (11.52 g, 0.09 mole) and DMF (150 mL) was heated at about 95° C. with stirring for 1.0 hour. The reaction mixture was drowned into water (500 mL) with stirring and acidified with acetic acid and the red product collected by filtration, washed with water and dried in air (yield—12.64 g). FDMS indicated the product to be the diacidic anthraquinone compound used in Example 18.

EXAMPLE 19

[0160] A mixture of 1,5-bis-(4-hydroxyphenylthio)anthraquinone (4.56 g, 0.01 mole), 1,2-ethanediol, dimethanesulfonate (2.18 g, 0.01 mole), potassium carbonate (3.0 g) and DMF (50 mL) was heated and stirred at about 95° C. for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the yellow polydye was collected by filtration and washed with methanol. The methanol-wet cake was reslurried in water (500 mL) and acidified and the polydye then collected by filtration, washed with water and dried in air (yield—4.25 g). GPC analysis indicated the polydye to have a weight average molecular weight of 1,901, a number average molecular weight of 1,588 and a polydispersity of 1.20. An absorption maximum at 461 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 19a

[0161] A mixture of 1,5-dichloroanthraquinone (5.54 g, 0.02 mole), 4-hydroxybenzenethiol (6.30 g, 0.05 mole), potassium carbonate (6.90 g, 0.05 mole) and DMF (100 mL) was heated at about 95° C. for 5.0 hours. The reaction mixture was drowned into water (400 mL) and the yellow product was collected by filtration, washed with water and dried in air (yield—9.0 g). The solid was added to acetic acid (150 mL) and the mixture heated to boiling. After being allowed to cool, the yellow solid was collected by filtration, washed with acetic acid and dried in air (yield—6.75 g). FDMS confirmed that the product was the 1,5-bis(4-hydroxyphenylthio)anthraquinone used in Example 19.

EXAMPLE 20

[0162] A mixture of 1,4-bis-(2-carboxyphenylthio)anthraquinone (1.53 g, 0.003 m), 1,2-ethanediol, dimethanesulfonate (0.66 g, 0.003 mole), potassium carbonate (0.75 g) and DMF (8.0 mL) was heated at about 95° C. with occasional stirring for 2.0 hours. The reaction mixture was then drowned into methanol (100 mL) and the dark orange polydye was collected by filtration, washed with water containing some acetic acid then with hot water and dried in air (yield—0.50 g). GPC analysis indicated a weight average molecular weight of 8,686, a number average molecular weight of 1,356 and a polydispersity of 6.41.

EXAMPLE 20a

[0163] A mixture of 1,4-dichloroanthraquinone (2.77 g, 0.01 mole), thiosalicylic acid (3.85 g, 0.025 m), potassium carbonate (3.45 g, 0.025 m), cupric chloride dihydrate (0.1 g) and DMF (50 mL) was heated at 95-100° C. with stirring for 4.0 hours. The reaction mixture was drowned into acetone and the solid was collected by filtration and washed with acetone. The resulting potassium salt of the product was dissolved by stirring in water (200 mL). The red solution was neutralized to give the orange product which was collect by filtration, washed with water and dried in air (yield—4.58 g). FDMS indicated the structure to be that of the starting material for Example 20. An absorption maximum at 501 nm was observed in the visible light absorption spectrum.

EXAMPLE 21

[0164] A mixture of 1,8-bis-(2-carboxyphenylthio)-4,5-bis-(p-tolylthio)anthraquinone (1.51 g, 0.002 mole), 1,4-butanediol, dimethanesulfonate (0.49 g, 0.002 mole), potassium carbonate (0.60 g and DMF (8.0 mL) was heated at 90-95° C. with occasional stirring for 2.5 hours. The reaction mixture was drowned into methanol (100 mL) and the red polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—1.1 g). GPC analysis indicated a weight average molecular weight of 2,157, a number average molecular weight of 1,111 and a polydispersity of 1.94. An absorption maximum was observed at 529 nm in the visible light absorption spectrum in DMF.

EXAMPLE 21a

[0165] A mixture of thiosalicyclic acid (4.75 g, 0.03 mole), potassium carbonate (8.70 g, 0.06 mole) and DMF (75 mL) was heated at about 100° C. for 1.0 hour and the reaction mixture, which was allowed to cool, was added at 0-5° C. to a solution of 1,8-dichloro-4,5-dinitroanthraquinone (5.51 g. 0.015 mole) dissolved in DMF (150 mL) with good stirring. Cooling was removed and the temperature of the reaction mixture allowed to come to ambient temperature and the mixture was stirred for about 3.0 hours. A solution of p-thiocresol (3.73 g, 0.03 mole) dissolved in DMF (80 mL) was added to the reaction mixture with stirring and the temperature raised to about 100° C. and held for 2.0 hours. After allowing to cool, the reacting mixture was drowned into water (300 mL) and the mixture gradually acidified by the addition of 10% aqueous hydrochloric acid. The red solid product was collected by filtration, washed with water and dried in air (yield—11.28 g). FDMS analysis indicated that the product consisted mostly of the starting material for Example 21.

EXAMPLE 22

[0166] A mixture of 1,5-bis(2-carboxyphenylthio)anthraquinone (1.54 g, 0.003 mole), 1,5-bis(2-carboxyhenylthio)-4,8-bis(isobutylamino)anthraquinone (1.31 g, 0.002 mole) (product of Example 2a), 1,2-ethandiol, dimethanesulfonate (1.09 g, 0.005 mole), potassium carbonate (1.0 g) and DMF (10 mL) was heated at 90-95° C. with occasional stirring for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the green polydye was washed with methanol, water containing acetic acid, hot water and then dried in air (yield—1.30 g). GPC analysis indicated a weight average molecular weight of 1,839, a number average molecular weight of 1,040 and a polydispersity of 1.77. Absorption maxima were observed in the visible light absorption spectrum in DMF at 448, 603, and 645 nm.

EXAMPLE 23

[0167] A mixture of 1,5-bis(2-carboxyphenylthio)anthraquinone (1.28 g, 0.0025 mole), 1,4- cyclohexanedimethanol, dimethanesulfonate (1.75 g, 0.0025 mole), potassium carbonate (0.82 g) and DMF (7.5 mL) was heated at about 95° C. with occasional stirring for 3.0 hours. The reaction mixture was drowned into methanol (100 mL) and the yellow polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—0.31 g). GPC analysis indicated a weight average molecular weight of 1,158, a number average molecular weight of 1,008 and a polydispersity of 1.15.

EXAMPLE 24

[0168] Example 23 was repeated except that the disulfonate used was 1,3-propanediol, 2,2-dimethyl, dimethanesulfonate (0.65 g, 0.0025 mole) to give the yellow polydye (yield—0.76 g) which had a weight average molecular weight of 1,056, a number average molecular weight of 979 and a polydispersity of 1.08 by GPC analysis.

EXAMPLE 25

[0169] Example 23 was repeated except that 1,6-hexanediol, dimethanesulfonate (0.68 g, 0.0025 mole) was used as the disulfonate to give the yellow polydye (yield—1.16 g) which had a weight average molecular weight of 1,827, a number average molecular weight of 961 and a polydispersity of 1.90 by GPC analysis.

EXAMPLE 26

[0170] Example 23 was repeated except that 1,2-ethanediol, bis(4-methylbenzenesulfonate (0.82 g, 0.0025 mole) was used as the disulfonate to yield the yellow polydye (yield—0.41 g) which had a weight average molecular weight of 2,442, a number average molecular weight of 1,885 and a polydispersity of 1.29 by GPC analysis.

EXAMPLE 27

[0171] A mixture of the acidic anthraquinone compound (2.02 g, 0.0027 mole) having the structure

[0172] the acidic UV light absorbing compound (0.29 g, 9×10⁻⁴ mole) having the structure

[0173] 1,2-ethanediol, dimethanesulfonate (0.78 g, 0.0036 mole), potassium carbonate (1.0 g) and DMF (25 mL) was heated and stirred at 90-95° C. for 2.0 hours. The cooled reaction mixture was drowned into water (200 mL) and made slightly acidic by the addition of acetic acid with stirring. The polymeric product was collected by filtration, washed well with water and dried in air (yield—2.00 g). GPC analysis indicated a weight average molecular average of 5,642, a number average molecular weight of 1,720 and a polydispersity of 3.28.

EXAMPLE 28

[0174] A mixture of the diacidic anthraquinone compound (1.27 g, 0.002 mole) having the structure

[0175] 1,2-ethanediol, dimethanesulfonate (0.44 g, 0.002 mole), potassium carbonate (0.75 g) and DMF (8.0 mL) was heated at 90-95° C. with occasional stirring for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the dark red polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—1.23 g). GPC analysis indicated a weight average molecular weight of 1,545, a number average molecular weight of 1,213 and a polydispersity of 1.27.

EXAMPLE 28a

[0176] To a mixture of 1,5-bis(2-carboxyanilino)anthraquinone (9.57 g, 0.02 mole) in DMF (250 mL) was added portionwise N-bromosuccinimide (7.12 g, 0.04 mole) with stirring at room temperature. The reaction mixture was then heated at about 60° C. for 1.5 hours and allowed to cool. Water was added dropwise to precipitate the product, which was collected by filtration, washed with water and dried in air (yield—11.17 g). FDMS indicated the structure of the product to be that of the starting anthraquinone compound in Example 28.

EXAMPLE 29

[0177] A mixture of the diacidic anthraquinone compound (4.06 g, 0.01 mole) having the structure

[0178] 1,2-ethanediol, dimethanesulfonate (2.18 g, 0.01 mole), potassium carbonate (2.76 g) and DMF (150 mL) was heated at about 100° C. for 3.0 hours. The reaction mixture was drowned into water, acidified with acetic acid and the yellow polydye was collected by filtration, washed with water and dried in air. GPC analysis indicated a weight average molecular weight of 5,333, a number average molecular weight of 2,441, and a polydispersity of 2.18.

EXAMPLE 29a

[0179] A mixture of 1,5-dichloroanthraquinone (6.93 g, 0.025 mole), 3-mercapto-1(H)-1,2,4-triazole (5.56 g, 0.055 mole), potassium carbonate (6.91 g, 0.05 mole) and DMF (100 mL) was heated and stirred at about 95° C. for 5.0 hours. The mixture was drowned into water and the yellow product was collected by filtration, washed with water and air dried. The cake was reslurried in hot isopropanol and the product collected by filtration, washed with isopropanol and dried in air (yield 8.62 g). FDMS indicated the product to be 1,5-bis[1(H)-1,2,4-triazol-3-ylthio]anthraquinone used as the diacidic anthraquinone starting material in Example 29.

EXAMPLE 30

[0180] A mixture of diacidic anthraquinone compound (1.01 g, 0.0025 mole) having the structure

[0181] 1,2-ethanediol, dimethanesulfonate (0.55 g, 0.0025 mole), potassium carbonate (0.75 g) and DMF (10 mL) was heated at about 95° C. for 3.0 hours. The reaction mixture was then drowned into methanol (100 mL) and the yellow polydye was collected by filtration, water containing acetic acid, hot water and then air dried (yield—0.35 g). GPC analysis indicated a weight average molecular weight of 2,478, a number average molecular weight of 742 and a polydispersity of 3.34. An absorption maximum was observed in the visible light absorption spectrum at 425 nm in DMF.

EXAMPLE 30a

[0182] A mixture of 1,8-dichloroanthraquinone (6.93 g, 0.025 mole), 2-mercaptoimidazole (5.01 g, 0.05 mole), potassium carbonate (6.91 g) and DMF (60 mL) was heated and stirred at about 95° C. for 8.0 hours. The reaction mixture was drowned into water and acidified using acetic acid. The yellow product was collected by filtration, washed with water and dried in air. FDMS indicated the product to be the 1,8-bis(imidazol-2ylthio) anthraquinone diacidic compound used as the starting material in Example 30.

EXAMPLE 31

[0183] A mixture of 1,5-bis[1(H)-1,2,4-triazol-3ylthio] anthraquinone (1.80 g, 0.00443 mole) (product of Example 29a), 1,4-dibromobutane (0.96 g, 0.00444 mole), tributylamine (1.64 g, 0.00885 mole), and N-methyl-2-pyrrolidinone (30 mL) was heated at 8.0 hours at about 130° C. with stirring. The reaction mixture was drowned into acetone (150 mL) and the yellow polydye was collected by filtration, washed with acetone until filtrate was essentially clear and dried in air. GPC analysis indicated a weight average molecular weight of 5,022, a number average molecular weight of 3,220 and a polydispersity of 1.56.

EXAMPLE 32

[0184] A mixture of the diacidic anthraquinone compound (1.63 g, 0.003 mole) having the structure

[0185] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.5 g) and DMP (8.0 mL) was heated at about 95° C. with occasional stirring for 2.0 hours. The mixture was drowned into methanol (100 mL) and the dark blue polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.92 g). Absorption maxima at 602 and 644 nm were observed in the visible light absorption spectrum in DMF. GPC analysis indicated a number average molecular weight of 1,860.

Example 32a

[0186] A mixture of 1,4-diamino-2,3-dichloroanthraquinone (12.24 g, 0.04 mole), thiosalicylic acid (15.4 g, 0.10 mole), potassium carbonate (13.8 g, 0.10 mole) and DMF (150 mL) was heated at about 95° C. with stirring for 2.0 hours. A bathochromic shift in color from violet to blue was observed as the reaction progressed. The reaction mixture was drowned into acetone (500 mL) and the solid product was collected by filtration and washed well with acetone. The acetone-wet cake was added to water (600 mL) and the mixture acidified with acetic acid to precipitate the free acid compound, which was collected by filtration, washed with water and dried in air (yield—21.4 g). FDMS indicated the product to be the 1,4-diamino-2,3-bis(2-carboxyphenylthio) anthraquinone used in Example 32.

EXAMPLE 33

[0187] A mixture of 1,5-bis(2-carboxyphenylthio) anthraquinone (1.02 g, 0.002 mole), terephthalic acid (1.00 g, 0.006 mole), potassium carbonate (1.38 g) 1,2-ethanediol, dimethanesulfonate (1.74 g, 0.008 mole) and DMF (10 mL) was heated at about 95° C. with occasional stirring for 2.0 hours. The mixture was then drowned into methanol (100 mL) and the yellow polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.88 g). GPC analysis indicated a weight average molecular weight of 794, a number average molecular weight of 713 and a polydispersity of 1.11.

EXAMPLE 34

[0188] Example 33 was repeated using 1,5-bis(2-carboxyphenylthio) anthraquinone (1.02 g, 0.002 mole) and terephthalic acid (0.33 g, 0.002 mole), 1,2-ethanediol, dimethanesulfonate (0.87 g, 0.004 mole) and potassium carbonate (0.87 g) to yield the yellow polydye (0.90 g). GPC analysis indicated a weight average molecular weight of 875, a number average molecular weight of 811, and a polydispersity of 1.08.

EXAMPLE 35

[0189] A mixture of the diacidic anthraquinone compound (2.00 g, 0.00285 mole) having the following structure (Preparation 5 of IR Docket 70351):

[0190] 1,2-ethanediol, dimethanesulfonate (0.63 g, 0.00289 mole), potassium carbonate (0.80 g) and DMF (25 mL) was heated at 95° C. for 4.0 hours with stirring. The reaction mixture was drowned into methanol (100 mL) and the greenish-blue polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.01 g). GPC indicated a weight average molecular weight of 6,720, a number average molecular weight of 2,211 and a polydispersity of 3.04. Absorption maxima were observed at 599 and 647 nm in the visible absorption spectrum in DMF.

EXAMPLE 36

[0191] A mixture of the diacidic anthraquinone compound (0.41 g, 0.508 mmole) having the following structure (Preparation 4 in IR Docket 70351):

[0192] 1,2-ethanediol, dimethanesulfonate (0.11 g, 0.504 mmole), potassium carbonate (0.14 g) and DMF (5.0 mL) was heated with occasional stirring or about 95° C. for 3.0 hours. The reaction mixture was drowned into methanol (50 mL) and the greenish-blue polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield 0.15 g). Absorption maxima were observed at 599 and 645 nm in the visible light absorption spectrum in DMF.

EXAMPLE37-66

[0193] Colored EASTAR® copolyester 6763 film was produced by melt blending the polydyes of Examples 7-36 and extruding according to the following procedure to produce Examples 37-66 (Table 1).

[0194] EASTAR® PETG polyester 6763, a poly(ethylene-1,4-cyclohexanedimethylene) terephthalate (Eastman Chemical Company) (300 g of previously dried pellets) was dry blended with the anthraquinone polydye composition (0.12 g). The blend was extruded with a C. W. Brabender ¾ in. extruder, equipped with a mixing screw, at 250° C. into a water bath and the extrudate pelletized.

[0195] The pellets were redried at 70° C. for 17 hrs. at a pressure of about 1-5 torr. A portion (1.40 g) of the dried pellets was pressed into a 18-20 mil film at 250° C. using a 2-inch diameter circular mold in a Pasadena Hydraulic, Inc. press using 12,000 pounds ram force (4 inch ram). The transparent films contained about 300 ppm of the polydyes and each showed excellent color development to produce the colors indicated in Table 1.

EXAMPLE 67

[0196] A mixture of 1,4-bis(2-carboxyphenythio)anthraquinone (15.4 g, 0.03 mole) (prepared as in Example 20a), 1,5-bis(2-carboxyphenylthio)-4,8-bis(isobutylamino)anthraquinone (6.55 g, 0.01 mole) (Example 2a), 1,2-ethanediol, dimethanesulfonate (8.72 g, 0.04 mole), potassium carbonate (8.0 g) and DMF (100 mL) was stirred and heated at about 95° C. for 2.0 hours with occasional stirring. The reaction mixture was drowned into methanol (500 mL) and the black polydye was collected by filtration, washed with water containing acetic acid, hot water and dried in air (yield—9.5 g). GPC analysis indicated a weight average molecular weight of 7,512, a number average molecular weight of 1,700 and a polydispersity of 4.42.

EXAMPLE 68

[0197] EASTAR® PETG copolyester 6763 (291 g of previously dried pellets) was dry blended with the black polydye of Example 67 (9.0 g) and the blend extruded and a portion of the resulting pellets was pressed into a black film containing approximately 3.0% by weight of polydye by using the procedure described in Example 4.

EXAMPLE 69

[0198] A mixture of the diacidic azo compound (3.20 g, 0.005 mole) having the structure

[0199] 1,2-ethanediol, dimethanesulfonate (1.09 g, 0.005 mole), potassium carbonate (1.5 g) and DMF (25 mL) was heated and stirred at about 95° C. for 3.0 hours. The reaction mixture was drowned into methanol and the violet polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.60 g). GPC analysis indicated a weight average molecular weight (Mw) of 6,403, a number average molecular weight (Mn) of 3,700 and a polydispersity (Mw/Mn) of 1.73. In the visible light absorption spectrum in DMF an absorption maximum was observed at 556 nm.

EXAMPLE 69a

[0200] A mixture of the dibromoazobenzene dye (6.01 g, 0.010 mole) having the structure

[0201] 3-mercapto-1(H)1,2,4-triazole (2.2 g, 0.022 mole), potassium carbonate (3.45 g, 0.025 mole) and DMF (100 mL) was stirred and heated at about 95° C. for 2.0 hours. TLC (75 parts THF: 25 parts cyclohexane) showed incomplete reaction. An additional quantity (1.01 g, 0.01 m) 3-mercapto-1(H)-1,2,4-triazole was added and heating and stirring were continued for 2.0 additional hours. TLC indicated essentially complete reaction to produce the violet product. The reaction mixture was drowned into water (400 mL) and the mixture was acidified by addition of acetic acid, heated to about 40° C. and filtered. The product was washed with warm water and dried in air (yield—5.60 g). FDMS indicated the product to have the structure of the diacidic azobenzene compound used in Example 69.

EXAMPLE 70

[0202] A mixture of the diacidic azo compound (1.59 g, 0.0025 mole) having the structure

[0203] 1,2-ethanediol, dimethanesulfonate (0.55 g, 0.0025 mole), potassium carbonate (0.5 g) and DMF (8.0 mL) was heated at 95° C. with occasional stirring for 3.0 hours. The reaction mixture was drowned into methanol (100 mL) and the blue polydye product was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.06 g). GPC analysis indicated a Mw of 5,497, a Mn of 2,648 and a Mw/Mn of 2.08. An absorption maximum was observed at 605 nm in DMF in the visible light absorption spectrum.

EXAMPLE 70a

[0204] A mixture of the dibromo azobenzene dye (2.38 g, 0.004 mole) having the structure

[0205] 3-mercapto-1(H)-1,2,4-triazole (1.21 g, 0.012 mole), potassium carbonate (1.65 g, 0.012 mole) and DMF (25 mL) was heated and stirred for 1.0 hour. TLC (50 parts THF:50 parts cyclohexane) showed complete reaction to produce the product. The reaction mixture was drowned into water (100 mL) and the mixture acidified with acetic acid. The dark blue product was collected by filtration, washed with water and dried in air (yield—2.55g). FDMS indicated the product to have the structure of the diacidic azobenzene compound used in Example 70.

EXAMPLE 71

[0206] A mixture of the diacidic disazo compound (1.59 g, 0.005 mole) having the structure

[0207] 1,2-ethanediol, dimethanesulfonate (1.09 9. 0.005 mole), potassium carbonate (1.5 g), DMF (10 mL) was heated and stirred at about 95° C. for 3.0 hours. The reaction mixture was drowned into methanol (100 mL) and the dark brown polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—0.66 g). GPC analysis indicated a Mw of 4,926, a Mw of 1,574 and a Mw/Mn of 3.13.

EXAMPLE 72

[0208] A mixture of the diacidic azo compound (1.88 g, 0.005 mole) having the structure

[0209] 1,2-ethanediol, dimethanesulfonate (1.09 g, 0.005 mole), potassium carbonate (1.5 g) and DMF (20 mL) was heated at about 95° C. with stirring for 3.0 hours. The reaction mixture was drowned in methanol (100 mL) and the red polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.35 g). GPC analysis indicated a Mw of 6,888, a Mn of 2,127 and a Mw/Mn of 3.24. An absorption maximum was observed at 527 nm in the visible light absorption spectrum in DMF.

EXAMPLE 72a

[0210] To a stirred mixture of the azo compound (4.05 g, 0.01 mole) [4-(3′,5′-dicarbomethoxy-4′-methylthiophene-2-ylazo)-N-ethyl—N(2-hydroxyethyl)aniline] and 2-ethoxyethanol (50 mL) at room temperature was added aqueous 50% NaOH solution(3.75 g). After being heated at about 95° C. for 1.0 hour, the reaction product was drowned into acetone (300 mL). The disodium salt of the diacidic azo dye was collected by filtration washed with acetone and then quickly dissolved in water (200 mL). Acidification with acetic acid precipitated the free diacid dye, which was collected by filtration, washed with water and dried in air (yield—2.35 g). FDMS indicated the product to have the structure of the diacidic azo compound used in Example 72.

EXAMPLE 73

[0211] A mixture of the diacidic azobenzene compound (1.19 g, 0.003 mole) having the structure

[0212] 1,2-ethanediol, dimethanesulfonate (0.66 g, 0.003 mole) potassium carbonate (0.75 g), and DMF (8.0 mL) was stirred occasionally and heated at about 95° C. for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the orange polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.65 g). GPC analysis showed a Mw of 3,015, a Mn of 2,128 and a Mw/Mn of 1.42. An absorption maximum was observed in the visible light absorption at 479 nm in DMF.

EXAMPLE 73a

[0213] To a mixture of 3-acetamido-4-(3′,5′-dicarbomethoxyphenylazo)-N,N-diethylaniline (1.7 g, 0.004 mole) in 2-ethoxyethanol (20 mL) was added aqueous 50% NaOH (1.6 g). The reaction mixture was heated with stirring of 95° C. for 10 minutes and then drowned into water (100 mL). The solution was acidified with acetic acid to precipitate the diacid dye which was collected by filtration, washed with water and dried in air (yield—1.6 g). FDMS indicated the structure to be that of the starting diacid azobenzene compound in Example 73.

EXAMPLE 74

[0214] A mixture of the diacidic azobenzene compound (1.10 g, 0.003 mole) having the structure

[0215] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.45 g) and DMF (8.0 mL) was heated at 95° C. with occasional stirring for 2.0 hours. The reaction mixture was drowned into methanol (100 mL). A slightly sticky yellow product resulted. The methanol was removed by decantation and the product dissolved in DMF (10 mL) by heating and stirring. Water (100 mL) was added and the mixture acidified by addition of acetic acid. The solid yellow polydye was collected by filtration, washed with water and dried in air (yield—0.47 g). GPC analysis indicated a Mw of 9,314, a Mn of 3,208 and a Mw/Mn of 2.90. An absorption maximum at 428 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 74a

[0216] To a mixture of 4-(2′,5′-dicarbomethoxyphenylazo)-N-(2-cyanoethyl)-N-ethylaniline (1.97 g, 0.005 mole) in 2-ethoxyethanol (20 mL) was added aqueous 50% NaOH (1.90 g). The reaction solution was heated at 95° C. for 15 minutes and then drowned into water (200 mL). The solution was acidified and the yellow dye which precipitated was collected by filtration, washed with water and dried in air (yield—1.75 g). FDMS indicated the structure to be that of the starting diacid azobenzene dye of Example 74.

EXAMPLE 75

[0217] A mixture of diacidic azo compound (38.6 g, 0.10 mole) having the structure

[0218] 1,6-hexanediol, dimethanesulfonate (27.4 g, 0.10 mole), potassium carbonate (27.6 g, 0.20 mole), and DMF (350 mL) was heated at 95-100° C. for 2.0 hours. The reaction mixture was drowned into a solution of acetic acid (70.0 mL) in water (1700 mL) with good stirring. After stirring for about 15 minutes, the yellow polydye was collected by filtration, washed with hot water and dried in air (yield—42.6 g). An absorption maximum at 422 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 75a

[0219] To a mixture of the diester dye (41.4 g, 0.10 mole) [3-cyano-5-(3′,5′-dicarbomethoxyphenylazo)-6-hydroxy-N-(2-hydroxyethyl)-4-methyl-2-pyridone] in 2-ethoxyethanol (400 mL) was added aqueous 50% NaOH (40.0 g) and the reaction mixture was heated at 75-80° C. for about 30 minutes. Acetone (200 mL) was added to the slightly cooled reaction mixture. The yellow solid was collected by filtration, washed with acetone and then reslurried in warm water (750 mL). After acidification using conc. HCl (20 mL), the yellow diacid dye was collected by filtration, washed with hot water and dried in air (yield- 36.0 g). FDMS indicated the structure to be that of the starting diacid azo compound of Example 75.

EXAMPLE 76

[0220] A mixture of the diacidic azo compound (2.03 g, 0.005 mole) having the structure

[0221] 1,2-ethanediol, dimethanesulfonate (1.09 g, 0.005 mole), potassium carbonate (1.5 g) and DMF (20 mL) was heated at about 95° C. with occasional stirring for 5.0 hours. The reaction mixture was drowned into methanol. Acetic acid (1.0 mL) was added and the polydye was collected by filtration and washed with water and dried in air. GPC analysis indicated a Mw of 9,876, a Mn of 3,917 and a polydispersity of 2.52. An absorption maximum at 506 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 77

[0222] A mixture of the diacidic azo compound (0.60 g, 0.00155 mole) having the structure

[0223] 1,2-ethanediol, dimethanesulfonate (0.34 g, 0.00155 mole), potassium carbonate (0.3 g) and DMF (4.0 mL) was heated at about 95° C. for 4.0 hours. The reaction mixture was drowned into methanol (20 mL) and the yellow polydye was collected by filtration, washed with methanol, water containing acetic acid, water and then air dried (yield—0.5 g). GPC analysis showed a Mw of 4,566, a Mn of 2,474 and a Mw/Mn of 1.84. In the visible light absorption spectrum in DMF an absorption maximum was observed at 420 nm.

EXAMPLE 77a

[0224] To a mixture of 3-(3′,5′-dicarboxymethoxyphenylazo)-2-phenylindole (1.0 g, 0.00242 mole) in 2-ethoxyethanol (10 mL) was added aqueous 50% NaOH (0.75 g) and the hydrolysis reaction carried out by heating at about 95° C. for 30 minutes. The reaction mixture was drowned into water (100 mL) and the solution treated with acetic acid to precipitate the product which was collected by filtration, washed with water and dried in air (yield—0.85 g). FDMS indicated the structure to be that of the starting diacidic azo compound in Example 77.

EXAMPLE 78

[0225] A mixture of the diacidic azo compound (0.99 g, 0.002 mole) having the structure

[0226] 1,2-ethanediol, dimethanesulfonate (0.42 g, 0.002 mole), potassium carbonate (0.5 g) and DMF (7.0 mL) was heated at about 95° C. for 3.0 hours. The reaction mixture was drowned into methanol (50 mL) and the scarlet polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—0.18 g). GPC analysis indicated a Mw of 8,246, a Mn of 2,619 and a polydispersity of 3.15.

EXAMPLE 79

[0227] A mixture of the diacidic azo dye (2.50 g, 0.00733 mole) having the following structure

[0228] 1,2-ethanediol, dimethanesulfonate (1.60 g, 0.00733 mole), potassium carbonate (2.07 g) and DMF (25 mL) was heated at 95° C. for 3.0 hours. The reaction mixture was drowned into methanol and a small amount of acetic acid added. The yellow polydye was collected by filtration, washed with a little methanol, water containing acetic acid, hot water and dried in air. GPC analysis indicated a Mw of 1,949, a Mn of 1,569 and a Mw/Mn of 1.24. An absorption maximum was observed at 411 nm the visible light absorption spectrum.

EXAMPLE 80

[0229] A mixture of the diacidic azo compound (1.22 g, 0.0025 mole) having the structure

[0230] 1,2-ethanediol, dimethanesulfonate (0.55 g, 0.0025 mole), potassium carbonate (0.75 g) and DMF (8.0 mL) was heated and stirred at about 95° C. for 3 hours with occasional stirring. The reaction mixture was drowned into methanol (50 mL) and the polydye was collected by filtration washed with methanol, water containing acetic acid, hot water and then dried in air (yield—0.68 g). GPC analysis indicated a Mw of 2,259, a Mn of 1,571 and a Mw/Mn of 1.44. An absorption maximum was observed at 503 nm in DMF in the visible light absorption spectrum.

EXAMPLE 81

[0231] A mixture of the diacidic azo compound (1.25 g, 0.003 mole) having the structure

[0232] 1,2-ethanediol, dimethanesulfonate (0.65 g, 0.003 mole), potassium carbonate (1.0 g) and DMF (10 mL) was heated at about 95° C. for 3.0 hours with occasional stirring. The reaction mixture was drowned into methanol (25 mL) and the orange polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.75 g). GPC analysis indicated a Mw of 2,014, a Mn of 1,520 and a Mw/Mn of 1.32. An absorption maximum was observed at 493 nm in the visible light absorption spectrum in DMF.

EXAMPLE 82

[0233] A mixture of the diacidic azo compound (1.11 g, 0.0025 mole) having the structure

[0234] 1,2-ethanediol, dimethanesulfonate (0.55 g, 0.0025 mole), potassium carbonate (0.80 g and DMF (8.0 mL) was heated at about 95° C. for 2.5 hours. The reaction mixture was drowned into methanol (100 mL) and the brown polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.30 g). GPC analysis indicated a Mw of 2,301, a Mn of 1,345 a Mw/Mn of 1.71. In the visible light absorption spectrum in DMF a maximum absorption was observed at 434 nm.

EXAMPLE 83

[0235] A mixture of the diacidic azo compound (2.40 g, 0.005 mole) having the structure

[0236] 1,2-ethanediol, dimethanesulfonate (1.09 g, 0.005 mole), potassium carbonate (1.5 g) and DMF (25 mL) was heated at about 95° C. for 3.0 hours with occasional stirring. The reaction mixture was drowned into methanol (200 mL) and the dark red polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—1.80 g). GPC analysis indicated Mw of 2,914, a Mn of 809 and a Mw/Mn of 3.60. An absorption maximum at 528 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 84

[0237] A mixture of the diacidic azo compound (1.07 g, 0.002 mole) having the structure

[0238] 1,2-ethanediol, dimethanesulfonate (0.44 g, 0.002 mole), potassium carbonate (0.5 g) and DMF (10 mL) was heated at 95° C. with occasional stirring for 5 hours. The reaction mixture was drowned into methanol (50 mL) and the reddish-blue polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.83 g). GPC analysis indicated a Mw of 7,038, a Mn of 832 and a Mw/Mn at 8.44. An absorption maximum was observed at 574 nm in the visible light absorption spectrum in DMF.

EXAMPLE 85 Displacement of Bromine in Polydye of Example 84 with Cyano Group

[0239] A mixture of a portion (0.5 g) of the polydye of Example 84, sodium dicyanocuprate (0.2 g) and DMF (8.0 mL) was heated at about 95° C. with occasional stirring for 3.0 hours. The reaction mixture, the color of which changed from reddish-blue to neutral-blue as the displacement reaction occurred, was then drowned into methanol and the polydye was collected by filtration, washed with methanol and dried in air. GPC analysis indicated a Mw of 9,427, a Mw of 1,117 and a Mw/Mn of 8.44. An absorption maximum at 590 nm was observed in DMF in the visible light absorption spectrum.

EXAMPLE 86

[0240] A mixture of diacidic azo compound (1.53 g, 0.0025 mole) having the structure

[0241] 1,6-hexanediol, dimethanesulfonate (0.69 g, 0.0025 mole), K₂CO₃ (0.8 g) and DMF (8.0 mL) was heated at about 95° C. with occasional stirring for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the brown polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and then dried in air (yield—0.62 g). GPC analysis indicated a Mw of 4,795, a Mn of 2,051 and a Mw/Mn of 2.33. An absorption maximum at 434 nm in DMF was observed in the visible light absorption spectrum.

EXAMPLE 86a

[0242] To conc. H₂SO₄ (33.0 mL) was added 2,6-dichloro-4-nitroaniline (6.21 g, 0.03 mole) with stirring. The solution was cooled to 0-5° C. and stirred while a nitrosyl sulfuric acid mixture, prepared by adding sodium nitrite (2.19 g) to conc. H₂SO₄ (15 mL) portionwise with stirring and allowing the temperature to rise, was added below 5° C. with stirring. The diazotization reaction mixture was stirred at 0-5° C. for 2.0 hours. An aliquot of the diazonium salt solution (0.01 mole) was added to a chilled solution of the diacid coupler (3.95 g, 0.01 mole) (N,N-bis(4-carboxyphenylmethyl)-3-chloroaniline) dissolved in 1:5 (1 part propionic acid:5 parts acetic acid) (120 mL) containing some conc. HCl (5.0 mL) with stirring at 0-5° C. The coupling reaction mixture was neutralized by the addition of ammonium acetate with stirring and allowed to stand with occasional stirring at below 5° C. for about 1.0 hour. Water was added to precipitate the solid dye, which was collected by filtration, washed with water and dried in air (yield—4.0 g). The crude dye was reslurried in hot methanol and the mixture allowed to cool. The final dye was collected by filtration, washed with methanol and dried in air. An absorption maximum was observed at 431 nm in DMF. The diacid dye was used as the starting material in Example 86.

EXAMPLE 86b

[0243] A mixture of m-chloroaniline (2.56 g, 0.02 mole), methyl 4-(bromomethyl)benzoate (10.08 g, 0.044 mole), sodium carbonate (4.66 g) and sodium iodide (0.2 g) and 2-ethoxyethanol (50 mL) was heated under nitrogen at about 90° C. for 3.0 hours with stirring The reaction mixture was drowned into water and the product was extracted into methylene chloride. Methylene chloride was removed to leave an oily product (11.0 g), which was added to 2-ethoxyethanol (100 mL). To the solution was added aqueous 50% NaOH solution (7.50 g) and the reaction mixture was warmed. At about 30° C., white solids began to precipitate and at about 50° C. the reaction mixture become very thick. When the temperature had reached 70° C., water (20 mL) was added to dissolve the salts of the diacidic product. After stirring at 70° C. for 1.5 hours the reaction mixture was clarified by filtering through Celite filter aid and the filtrate acidified by the addition of 10% aqueous HCl to pH of about 4.0. The white solid was collected by filtration, washed with water and dried in air (yield—7.20 g). FDMS indicated the product to have the structure of the coupler used in Example 86a.

EXAMPLE 87

[0244] A mixture of the diacidic azo compound (1.64 g, 0.003 mole) having the structure

[0245] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.5 g) and DMF (8.0 mL) was heated at about 95° C. for 25 hours with occasional stirring. The reaction mixture was drowned into methanol (150 mL) and the polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.5 g). GPC analysis indicated a Mw of 2,741, a Mn of 1,367 and a Mw/Mn of 2.00. An absorption maximum at 441 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 87a

[0246] An aliquot (0.01 mole) of the diazonium salt from 2,6-dichloro-4-nitroaniline prepared in Example 86a was added to a chilled solution of the coupler (3.29 g, 0.01 mole) having the formula

[0247] dissolved in 1:5 acid (100 mL) with stirring at 0-5° C. Ammonium acetate was added with stirring until the coupling mixture was neutral to Congo Red Test paper. After allowing to stand for 1.0 hour, water was added to the coupling mixture to precipitate the dye, which was collected by filtration, washed with water and dried in air (yield—4.27 g). An absorption maximum was observed at 460 nm in the visible light absorption spectrum in DMF.

EXAMPLE 87b

[0248] A mixture of N-(2-chloroethyl)—N-ethylaniline (46.0 g, 0.25 mole), dimethyl 5-hydroxyisophthalate (52.5 g, 0.25 mole), potassium carbonate (69.08), a trace of pulverized potassium iodide and DMF (350 mL) was heated at 125-30° C. for 3.5 hours with stirring. The reaction mixture was allowed to cool and drowned in water/ice mixture (1.0 L). The product separated as a brown oil and the aqueous layer was removed by decantation. To the oily product was added 2-ethoxyethanol (175 mL) and aqueous 50% NaOH (50.0 g) and the hydrolysis reaction mixture was heated at 60-65° C. for about 20 minutes. Acetone was added to the reaction mixture and the white solid was collected by filtration, washed with acetone and dried in air (yield—99.0 g). The disodium salt was dissolved in water (250 mL) by stirring. Acidification with conc. HCl to a pH of about 3.0 gave a slightly sticky product which solidified in a few minutes. The pale yellow granular solid was collected by filtration, washed with water and dried in air (yield—58.0 g). FDMS indicated the structure to be that of the coupler used in Example 87a.

EXAMPLE 88

[0249] A mixture of the diacid azo compound (0.70 g, 0.0013 mole) having the structure

[0250] 1,6-hexanediol, dimethanesulfonate (0.36 g, 0.0013 mole), potassium carbonate (0.35 g) and DMF (5.0 mL) was heated at about 95° C. with occasional stirring for 2.0 hours. The reaction mixture was drowned into methanol (50 mL) and the polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.55 g). GPC indicated a Mw of 7,353, a Mn of 2,431 and a Mw/Mn of 3.02. An absorption maximum at 537 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 88a

[0251] To a mixture of the diester dye (1.75 g, 0.0013 mole) having the structure

[0252] and 2-ethoxyethanol (20 mL) was added aqueous 50% NaOH solution (1.2 g) and the hydrolysis mixture was heated at about 10 minutes at about 95° C. The reaction mixture was drowned into acetone and the solid material collected by filtration. The acetone-wet material was dissolved by stirring in water (200 mL) and the diacid dye precipitated by adding acetic acid. The product was collected by filtration washed with water and dried in air (yield—1.35 g). FDMS showed the product to be mostly

[0253] indicating hydrolysis of the acetamido group in addition to the ester group. All of the product was added to acetic acid (8.0 mL) and acetic anhydride (1.0 mL). The reaction mixture was heated at 95° C. for 30 minutes with occasional stirring. A bathochromic shift in color from red to magenta was observed as the amine group was acetylated. The reaction mixture was allowed to cool, whereupon a solid dark red product crystallized, and then was drowned into methanol (40 mL). The product was collected by filtration, washed with water and dried in air (yield—0.90 g). FDMS indicated the structure to be that of the diacidic azo dye in Example 88.

EXAMPLE 88b

[0254] A mixture of the dibromo azo dye (3.00 g, 0.0044 mole) having the structure

[0255] sodium dicyanocuprate (0.69 g, 0.005 mole) and DMF (30 mL) was heated at 95° C. for 1.0 hour. The reaction mixture was drowned into methanol (150 mL) and the dye was collected by filtration, washed with methanol and dried in air (yield—1.91 g). FDMS indicated the structure to be that of the dicyano dye used in Example 88a.

EXAMPLE 88c

[0256] To conc. H₂SO₄ (7.5 mL) was added dry NaNO₂ (1.08 g) portionwise with stirring and the temperature allowed to rise. The nitrosyl sulfuric acid mixture was cooled and 1:5 acid (15 mL) was added at less than 10° C. with stirring. To this mixture was added at 0-5° C. with stirring dimethyl 5-(4′-amino, 2′,6′-dibromophenoxy)isophthalate (6.86 g, 0.015 mole), followed by an additional 15 mL of 1:5 acid. The diazotization reaction mixture was stirred at 0-5° C. for 2.0 hours and then an aliquot (0.0075 mole) was added to a solution of 3-acetamido-N,N-diethylaniline (1.54 g, 0.0075 mole) dissolved in 1:5 acid (75 mL) at 0-5° C. Ammonium acetate was added with stirring to the coupling mixture until neutral to Congo Red test paper. Coupling was allowed to continue at 0-5° C. for 1.0 hour and the dye then precipitated by addition of water, collected by filtration, washed with water and dried in air. FDMS indicated the structure to be that of the starting dibromo azo dye in Example 88b. An absorption maximum at 546 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 88d

[0257] A mixture of the dimethyl 5-(4′-aminophenoxy)isophthalate (15.0 g, 0.05 mole) (Example 12c), anhydrous sodium acetate (9.6 g) and acetic acid (85 mL) was treated with stirring with bromine (17.4 g, 0.11 mole) allowing the temperature to rise. The reaction mixture was heated at 70-80° C. for 1.5 hours, allowed to cool, and then drowned into ice water (350 mL). The product was collected by filtration, washed with water and dried in air (yield—21.9 g). FDMS indicated the structure to be that of the amine compound diazotized in Example 88c.

EXAMPLE 89

[0258] A mixture of the diacidic azo compound (1.39 g, 0.0025 mole) having the structure

[0259] 1,6-hexanediol, dimethanesulfonate (0.68 g, 0.0025 mole), potassium carbonate (1.0 g) and DMF (8.0 mL) was heated at 95° C. for 2.5 hrs with occasional stirring. The reaction mixture was drowned into methanol (100 mL) and the red polydye was collected by filtration, washed with water containing acetic acid, hot water and dried in air (0.85 g). GPC analysis indicated a Mw of 2,772, a Mn of 1,306 and a Mw/Mn of 2.12. An absorption maximum was observed at 538 nm in the visible light absorption spectrum in DMF.

EXAMPLE 90

[0260] A mixture of the diacidic azo compound (1.23 g, 0.004 mole) having the formula

[0261]1,2-hexanediol, dimethanesulfonate (1.1 g, 0.004 mole), potassium carbonate (0.55 g) and DMF (8.0 mL) was heated at 95° C. for 1 hour. The reaction mixture was drowned into water (250 mL) containing acetic acid (5.0 mL). The yellow polydye was collected by filtration, washed with water and dried in air (yield—1.21 g). GPC analysis indicated a Mw of 1,726, a Mn of 1,079 and a Mw/Mn of 1.6. An absorption maximum at 400 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLE 91

[0262] A mixture of the diacidic azo compound (1.71 g, 0.003 mole) having the formula

[0263] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.85 g) and DMF (8.0 mL) was heated with occasional stirring at 95° C. for 2.0 hours. The reaction mixture was drowned into methanol (100 ml) and the red polydye was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield- 1.5 g). GPC indicated a Mw of 2,090, a Mn of 1,235 and a Mw/Mn of 1.69. An absorption maximum was observed at 545 nm in the visible light absorption spectrum in DMF.

EXAMPLE 91a

[0264] To conc. H₂SO₄(5.0 mL) was added dry NaNO₂ (0.72 g) portionwise with stirring, allowing the temperature to rise. The nitrosyl sulfuric acid solution was stirred and cooled and 1:5 acid (10 ml was added below about 15° C., followed by 5-amino-4-cyano-3-methylisothiazole (1.39 g, 0.01 mole) and 1:5 acid (10 ml) both added at 0-5° C. After being stirred at 0-5° C. for 2.0 hours an aliquot (0.005 mole) of the diazonium solution was added to a stirred solution of 3-acetamido-N,N-bis-(4-carboxyphenylmethyl)aniline (2.09 g, 0.005 mole) dissolved in 1:5 acid (30 ml) at 0-5° C. Ammonium acetate was added to neutralize the coupling mixture until neutral to Congo Red test paper. Water was added to the coupling mixture to precipitate the red dye, which was collected by filtration and dried in air (yield- 2.67 g). The product was reslurried in hot methanol, allowed to cool and the solid collected by filtration, washed with methanol and dried in air (yield- 2.10 g). FDMS indicated the structure to be that of the diacid azo compound used as a starting material for Example 91.

EXAMPLE 91b

[0265] To a slurry of the diester compound (12.00 g, 0.0269 mole) having the structure

[0266] in water (150 ml) was added aqueous 500 NaOH solution (10.80 g) and 2-ethoxyethanol (20 ml). The reaction mixture was heated at about 70-80° C. for 2.0 hours and allowed to cool. The cloudy reaction mixture was clarified by filtering through Celite filter aid and the filtrate was drowned into ice/water mixture (150 g). Conc. HCl was added dropwise with stirring to bring the pH to about 2.5. The tan solid was collected by filtration, washed with water and dried at 40° C. under nitrogen (yield- 10.04 g). FDMS indicated the product to have the structure of the coupler used in Example 91a.

EXAMPLE 92

[0267] A mixture of the diacidic azo compound (0.83 g, 0.002 mole) having the structure

[0268] 1,2-ethanediol, dimethanesulfonate (0.44 g, 0.002 mole), potassium carbonate (0.5 g) and DMF (7.5 ml) was heated at about 95° C. for 3.0 hours. The polydye was isolated by drowning the reaction mixture into water and acidifying with acetic acid, followed by filtering, washing with water and drying in air. GPC analysis indicated a Mw of 2,379, a Mn of 1,363 a Mw/Mn of 1.74. An absorption maximum was observed in DMF in the visible absorption spectrum at 480 nm.

EXAMPLE 93

[0269] A mixture of the diacidic azo compound (1.26 g, 0.003 mole) having the structure

[0270] 1,6-hexanediol, dimethanesulfonate (0.82 g, 0.003 mole), potassium carbonate (0.50 g) and DMF (8.0 mL) was heated at about 95° C. for 1.5 hours. The reaction mixture was drowned into methanol (100 mL) and acetic acid (1.0 mL) was added The initially sticky polydye solidified after standing for about 1.0 hour and was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.60 g). GPC analysis indicated a Mw of 2,667, a Mn of 1,695 and a Mw/Mn of 1.57. An absorption maximum at 508 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLES 93a

[0271] A mixture of the diacidic azo compound (3.62 g, 0.005 m) having the structure

[0272] 1,2-ethanediol, dimethanesulfonate (1.10 g, 0.005 m), potassium carbonate (1.50 g) and DMF (30 mL) was heated at about 95° C. with stirring for 2.0 hours. The reaction mixture was drowned into methanol (100 mL) and the red polydye was collected by vacuum filtration and washed with methanol, water containing acetic acid, hot water and dried in air (yield- 3.08 grams). GPC analysis indicated a Mw of 7,176, a Mn of 3,533 and a Mw/Mn of 2.02. An absorption maximum was observed in the visible light absorption spectrum at 525 nm.

EXAMPLE 93b

[0273] To conc. H₂SO₄ (5.0 mL) was added dry NaNO₂ (0.72 g) portionwise with stirring, allowing the temperature to rise. The nitrosyl sulfuric acid solution was stirred and cooled and 1:5 acid (1 part propionic:5 parts acetic acid) (10 mL) was added below about 15° C., followed by 2,6-dicyano-3,5-diphenylaniline (2.95 g, 0.01 m) and 1:5 acid (10 mL) both added at 0-5° C. After being stirred for 2.0 hours at 0-5° C., the diazonium solution was added to a stirred solution of 3-acetamido-N,N-bis (4-carboxyphenylmethyl)aniline (4.18 g, 0.01 m) dissolved in a mixture of 1:5 acid (75 mL) plus 15% aqueous sulfuric acid (15 mL) at 0-5° C. Ammonium acetate was added portionwise until the coupling mixture was neutral to Congo Red test paper. After about 1.0 hour, water was added to the coupling mixture and the resulting slurry heated to about 60° C. The red product was collected by filtration, washed well with hot water and dried in air (yield—5.43 g). FDMS analysis indicated the structure to be that of the starting material for Example 93-1.

EXAMPLE 93c

[0274] A mixture of the diacidic azo compound (1.80 g, 0.003 m) having the structure

[0275] 1,2-ethanediol, dimethanesulfonate (0.66 g, 0.003 m), potassium carbonate (1.0 g) and DMF (8 mL) was heated at about 95° C. with occasional stirring. The polydye was isolated by drowning the reaction mixture into methanol (100 mL) followed by filtration and washing with methanol, water containing acetic acid, water and was then dried in air (yield—0.52 g). GPC analysis using NMP (N-methyl-2-pyrrolidinone) solvent indicated a Mw of 5,413, a Mn of 2,196 and a Mw/Mn of 2.46. An absorbance maximum at 517 nm was observed in the visible absorption maximum in DMF.

EXAMPLE 93d

[0276] A sample of 2-amino-5-ethylthio-1,3,4-thiadiazole (1.61 g, 0.01 m) was diazotized and coupled with 3-acetamido-N,N-bis(4-carboxyphenylmethyl)aniline (4.18 g, 0.01 m) and the red product isolated using the procedure described above in Example 93-1a. FDMS indicated the structure of the azo compound to be that of the starting material for Example 93-2.

EXAMPLESs 94-118

[0277] Colored EASTAR® PETG 6763 film was produced by melt blending the polydyes of Examples 69-93 and extruding according to the following procedures to produce Examples 94-118 (Table 2).

[0278] EASTAR® PETG polyester 6763, a poly(ethylene-cyclohexanedimethylene) terephthalate (Eastman Chemical Company) (300 g of previously dried pellets) was dry blended with the azo dye composition (0.12 g) and the blend extruded and finally a 18-20 mil thick film prepare as described above for Examples 37-66.

EXAMPLE 119

[0279] A mixture of the diacidic anthrapyridone compound (0.93 g, 0.002 mole) having the structure

[0280] 1,2-ethandiol, dimethanesulfonate (0.44 g, 0.002 mole) potassium carbonate (.5 g) and DMF (0.5 mL) was heated at about 95° C. for 3.0 hours with occasional stirring. The reaction mixture was drowned into methanol (100 mL) and the violet polydye was collected by filtration, washed with methanol, water containing acetic acid, water and dried in air (yield—1.09 g). A number average molecular weight of 1,228 was obtained by GPC analysis. Absorption maxima at 544 and 583 nm were observed in the visible light absorption spectrum in DMF.

EXAMPLE 119a

[0281] To a mixture of 1-cyano-6-(3′,5′-dicarbomethoxyphenylamino)-3-methyl-3H-dibenz[f,ij]isoquinoline-2,7-dione (2.00 g, 0.00405 mole) stirred in 2-ethoxyethanol (50 mL) was added aqueous 50% NaOH solution (2.47 g). The reaction mixture was heated at 90-95° C. for 50 minutes and then was drowned into water. The mixture was acidified by addition of acetic acid and the solid product was collected by filtration, washed with water and dried in air (yield—1.78 g). FDMS indicated the product to be the diacidic anthrapyridone compound reacted in Example 119.

EXAMPLE 119b

[0282] A mixture of 6-bromo-i-cyano-3-methyl-3H-dibenz[f,ij]isoquinoline-2,7-dione (11.0 g, 0.03 mole), dimethyl 5-aminoisophthalate (25.1 g, 0.12 mole), cupric acetate (3.6 g), potassium carbonate (3.0 g) and DMF (90 mL) was heated and stirred under nitrogen to about 135-40° C. The reaction mixture became very thick and turned violet. Additional DMF (40 mL) was added and heating was continued at 135-40° C. for 2.0 hours. The reaction mixture was allowed to cool to about 60° C. and poured on a coarse fritted glass funnel for vacuum filtration. The product was washed with DMF and water and the water-wet cake was reslurried in boiling acetone (250 mL). After cooling, the product was collected by filtration, washed with acetone and dried in air (yield—10.8 g). FDMS indicated the product to be the diester anthrapyridone compound used in Example 119a.

EXAMPLE 120

[0283] A mixture of the diacidic nitroarylamine compound (2.50 g, 0.0057 mole) having the structure

[0284] 1,2-ethanediol, dimethanesulfonate (1.25 g, 0.0057 mole), potassium carbonate (1.6 g) and DMF (15 mL) was heated at 95° C. for 2.5 hours. The reaction mixture was drowned into methanol (200 mL) and the yellow polydye was collected by filtration, washed containing acetic acid, water and dried at 40° C. (yield—0.77 g). An absorption maximum was observed at 412 nm in the visible absorption spectrum in DMF.

EXAMPLE 121

[0285] A mixture of the diacidic nitroarylamine compound (4.40 g, 0.015 mole) having the structure

[0286] 1,2-ethanediol, dimethanesulfonate (3.27 g, 0.015 mole), potassium carbonate (2.0 g) and DMF 40 mL) was heated at 90-95° C. with stirring for 4.0 hours. The reaction mixture was drowned into methanol (200 mL) and the yellow polydye was collected by filtration, washed with methanol, water containing acetic acid, water and dried in air (yield—1.80 g). GPC analysis indicated a Mw of 1,585, a Mn of 1,024, a Mw/Mn of 1.54. An absorption maximum at 416 nm was observed in the visible light absorption spectrum in DMF.

EXAMPLES 122-124

[0287] Colored polyester film was produced by melt blending and extruding EASTAR® PETG polyester 6763 (Eastman Chemical Company) (300 g previously dried pellets) which had dry blended with the polydyes of Examples 119, 120, 121 to produce Examples 122-124, respectively, according to the procedure used to produce Examples 37-66. The film of Example 122 was violet and those of Examples 123 and 124 were bright yellow.

EXAMPLE 125

[0288] A mixture of the benzotriazole UV light absorbing compound (3.27 g, 0.01 mole) having the structure

[0289] 1,2-ethanediol, dimethanesulfonate (2.18 g, 0.01 mole), potassium carbonate (2.76 g) and DMF (25 mL) was heated at about 95° C. for 6.0 hours. The reaction mixture was drowned into methanol (200 mL) and a little acetic acid added. The polymeric UV light absorbing compound was collected by filtration, washed with water containing a little acetic acid, hot water and then dried in air (yield—2.88 g). GPC analysis indicated a Mw of 7,561, a Mn of 2,632 and a Mw/Mn of 2.87. An absorption maximum was observed at 350 nm in the UV light absorption spectrum in methylene chloride.

EXAMPLE 126

[0290] A benzylidene type UV light fluorescent compound (1.0 g, 0.0028 mole) having the structure

[0291] 1,6-hexenediol, dimethanesulfonate (0.0028 mole), potassium carbonate (0.97 g) and DMF (10 mL) were mixed and the reaction mixture was heated at for 3.0 hours at about 120-130° C. The reaction mixture was drowned into methanol (100 mL) and the polymer was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—0.69 g). GPC indicated a Mw of 50,717, a Mn of 16,044 and a MW/Mn of 3.16.

EXAMPLE 127

[0292] EASTAPAK® PET 7352, a poly(ethyleneterephthalate) (Eastman Chemical Company) (400 g of previously dried pellets) was dry blended with the polymeric UV light fluorescent material of Example 126 (0.16 g). The blend was extruded with a C. W. Brabender ¾ inch extruder, equipped with a mixing screw, at 285° C. into a water bath and the extrudate pelletized. The pellets which contained about 400 ppm of the UV light absorber showed a strong blue white fluorescence under UV light.

EXAMPLE 128

[0293] Example 127 was repeated except that 8 mg of the UV light fluorescent material of Example 126 was added to the EASTAPAK® PET 7352. The resulting pellets showed a strong blue-white fluorescence under UV light and appeared very white in sunlight.

EXAMPLE 129

[0294] A mixture of Pc-Al—O—O—C₆H₃-3,5-diCO₂H (Pc=phthalocyanine) (1.74 g, 0.0024 mole), 1,6-hexanediol, dimethanesulfonate (0.66 g, 0.0024 mole), potassium carbonate (0.83 g) and DMF (10 mL) was heated and stirred at about 125° C. for 1 hour and then at about 140° C. for 1 hour. The reaction mixture was drowned into methanol (50 mL) and the polymeric product was collected by filtration, washed with methanol, water containing acetic acid, hot water and dried in air (yield—1.48 g).

EXAMPLE 130

[0295] EASTAPAK® PET 7352, a poly(ethyleneterephthalate) (Eastman Chemical Company) (400 g of previously dried pellets) was dry blended with the polymeric phthalocyanine compound of Example 129 (0.12g). The blend was extruded with a C. W. Brabender ¾ inch extruder, equipped with a mixing screw, at 285° into a water bath and the extrudate pelletized. The cyan pellets were redried at 70° C. for about 17 hrs at a pressure of about 1-5 torr. A portion of the dried pellets (1.40 g) was pressed into a film at 285° C. using a 2-inch diameter circular mold in a Pasadena Hydraulic, Inc. press using 12,000 pounds ram force (4-inch ram). A transparent cyan film was produced by quenching in water and had an absorption maximum at 684 nm in the light absorption spectrum.

EXAMPLE 131

[0296] Example 130 was repeated except that 4 mg of the polymeric phthalocyanine compound of Example 129 was added to the PET. The final film contained about 10 ppm and had a light absorption maximum at 685 nm.

EXAMPLE 132

[0297] EASTAPAK® PET 7352, a poly(ethyleneterephthalate) (Eastman Chemical Company) (400 g of dried pellets) was dry blended with the polydye of Example 18 (0.6 g). The blend was extruded with a C. W. Brabender ³ inch extruder, equipped with a mixing screw, at 285° C. into a water bath and the extrudate pelletized. Good color production resulted with no evidence of color loss by sublimation to give dark red pellets containing about 0.15% by weight of the polydye.

EXAMPLE 133

[0298] Example 132 was repeated using 0.6 g of the polydye of Example 75 as the colorant to give yellow pellets having about 0.15% by weight of the polydye. No loss of color by sublimation was observed.

EXAMPLES 134-182

[0299] The diacidic azo compounds of Formula VI in Table 3 are reacted with essentially equimolar amounts of 1,2-ethanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 134-182 in Table 3.

EXAMPLES 183-193

[0300] The diacidic diazo compounds of Formula VII in Table 4 are reacted with essentially equimolar amounts of 1,4-butanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 183-193 in Table 4.

EXAMPLES 194-202

[0301] The diacidic bisazo compounds of Formula VIIa in Table 5 are reacted with essentially equimolar amounts of 1,3-propanediol, dimethanesulfonate in DMF in the presence of sodium carbonate to yield the polydyes of Examples 194-202 in Table 5.

EXAMPLES 203-211

[0302] The diacidic benzylidene (methine) compounds in Table 6 are reacted with essentially equimolar amounts of 1,4-cyclohexanedimethanol, dimethanesulfonate in DMF in the presence of sodium carbonate to yield the polydyes of Examples 203-211 in Table 6.

EXAMPLES 212-220

[0303] The diacidic 3-aryl-2,5-dioxypyrroline compounds of Formula X in Table 7 are reacted with essentially equimolar amounts of diethylene glycol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 212-220 in Table 7.

EXAMPLES 221-230

[0304] The diacidic 3-aryl-5-dicyanomethylene-2-oxypyrroline compounds of Formula XI in Table 8 are reacted with essentially equimolar amounts of triethylene glycol, dimethanesulfonate to yield the polydyes of Examples 221-230 in Table 8.

EXAMPLES 231-239

[0305] The diacidic azo-methine compounds of Formula XIII in Table 9 are reacted with essentially equimolar amounts of 1,4-butanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 231-239 in Table 9.

EXAMPLES 240-269

[0306] The diacidic anthraquinone compounds of Formula XIV in Table 10 are reacted with essentially equimolar amounts of 2,2,4,4-tetramehtyl-1,3-cyclobutanediol, dimethanesulfonate in N,N-dimethylacetamide in the presence of potassium carbonate to yield the polydyes of Examples 240-269 in Table 10.

EXAMPLES 270-326

[0307] The diacidic anthraquinone compounds of Formula XV in Table 11 are reacted with essentially equimolar amounts of 1,2-ethanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 270-326 in Table 11.

EXAMPLES 327-344

[0308] The diacidic anthraquinone compounds of Formula XVI in Table 12 are reacted with essentially equimolar amounts of 1,6-hexanediol, dimethanesulfonate in N-methyl-2-pyrrolidinone in the presence of sodium carbonate to yield the polydyes of Examples 327-344 in Table 12.

EXAMPLES 345-361

[0309] The diacidic anthrapyridine compounds of Formula XVIII in Table 13 are reacted with essentially equimolar amounts of 1,4-butanediol, di-p-toluenesulfonate in the presence of DMF to yield the polydyes of Examples 345-361 in Table 13.

EXAMPLES 362-381

[0310] The diacidic anthraquinone compounds of Formula XIX in Table 14 are reacted with 2,2-dimethyl-1,3-propanediol, dimethanesulfonate in essentially equimolar amounts in DMF in the presence of potassium carbonate to yield the polydyes of Examples 362-381 in Table 14.

EXAMPLES 382-396

[0311] The diacidic anthraquinone compounds of Formula XIXc of Table 15 are reacted with essentially equimolar amounts of 1,2-ethanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 382-396 in Table 15.

EXAMPLES 397-414

[0312] The diacidic anthraquinone compounds of Formula XIXd in Table 16 are reacted with essentially equimolar amounts of 1,6-hexanediol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 397-414 in Table 16.

EXAMPLES 415-435

[0313] The diacidic anthraquinone compounds of Formula XIXe in Table 17 are reacted in essentially equimolar amounts with ethylene glycol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 414-435 in Table 17.

EXAMPLES 436-449

[0314] The diacidic anthraquinone compounds of Formula XIXf in Table 18 are reacted in essentially equimolar amounts with 1,4-cyclohexanedimethanol, dimethanesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 436-449 in Table 18.

EXAMPLES 450-455

[0315] The diacidic anthrapyridine compounds of Table 19 are reacted with essentially equimolar amounts of 1,6-hexanediol, di-p-toluenesulfonate in DMF in the presence of potassium carbonate to yield the polydyes of Examples 450-455 in Table 19.

EXAMPLES 456-465

[0316] The diacidic nitroarylamine compounds of Table 20 are reacted with 1,4-butanediol, dimethanesulfonate in essentially equimolar amounts in DMF in the presence of potassium carbonate to yield the polydyes of Examples 456-465 in Table 20.

EXAMPLES 466-505

[0317] The miscellaneous diacidic compounds of Table 21 are reacted with essentially equimolar amounts of the disulfonate compounds of Table 21 in DMF in the presence of potassium carbonate to yield the polydyes of Examples 466-505 in Table 21.

EXAMPLES 506-522

[0318] The diacidic UV light absorbing compounds of Table 22 are reacted with essentially equimolar amounts of the disulfonate compounds of Table 22 in DMF in the presence of potassium carbonate to yield the polymeric UV absorbers of Examples 506-522 in Table 22.

EXAMPLES 523-536

[0319] The diacidic infrared light absorbing compounds of Table 23 are reacted with essentially equimolar amounts of the disulfonate compounds of Table 23 in DMF in the presence of potassium carbonate to yield the polymeric infrared light absorbing compounds of Examples 523-536 in Table 23. TABLE 1 Anthraquinone Polydyes in EASTAR ® PETG (300 ppm) Example Polydye Melt Blended and Extruded No. With EASTAR ® PETG Color of Film 37 Polydye of Example 7 Blue 38 Polydye of Example 8 Blue 39 Polydye of Example 9 Blue 40 Polydye of Example 10 Blue 41 Polydye of Example 11 Blue 42 Polydye of Example 12 Blue 43 Polydye of Example 13 Greenish-blue 44 Polydye of Example 14 Reddish-blue 45 Polydye of Example 15 Blue 46 Polydye of Example 16 Green 47 Polydye of Example 17 Bright blue 48 Polydye of Example 18 Bluish-red 49 Polydye of Example 19 Yellow 50 Polydye of Example 20 Orange 51 Polydye of Example 21 Red 52 Polydye of Example 22 Green 53 Polydye of Example 23 Yellow 54 Polydye of Example 24 Yellow 55 Polydye of Example 25 Yellow 56 Polydye of Example 26 Yellow 57 Polydye of Example 27 Blue 58 Polydye of Example 28 Red 59 Polydye of Example 29 Greenish-yellow 60 Polydye of Example 30 Yellow 61 Polydye of Example 31 Greenish-yellow 62 Polydye of Example 32 Blue 63 Polydye of Example 33 Yellow 64 Polydye of Example 34 Yellow 65 Polydye of Example 35 Greenish-blue 66 Polydye of Example 36 Greenish-blue

[0320] TABLE 2 Azo Polydyes in EASTAR ® PETG 6763 (300 ppm) Example Polydye Melt Blended and Extruded No. With EASTAR ® PETG Color of Film  94 Polydye of Example 69 Violet  95 Polydye of Example 70 Blue  96 Polydye of Example 71 Yellow-brown  97 Polydye of Example 72 Red  98 Polydye of Example 73 Orange  99 Polydye of Example 74 Yellow 100 Polydye of Example 75 Greenish-yellow 101 Polydye of Example 76 Scarlet 102 Polydye of Example 77 Yellow 103 Polydye of Example 78 Scarlet 104 Polydye of Example 79 Yellow 105 Polydye of Example 80 Red 106 Polydye of Example 81 Orange 107 Polydye of Example 82 Reddish-brown 108 Polydye of Example 83 Red 109 Polydye of Example 84 Reddish-blue 110 Polydye of Example 85 Blue 111 Polydye of Example 86 Brown 112 Polydye of Example 87 Reddish-brown 113 Polydye of Example 88 Magenta 114 Polydye of Example 89 Magenta 115 Polydye of Example 90 Yellow 116 Polydye of Example 91 Red 117 Polydye of Example 92 Orange 118 Polydye of Example 93 Scarlet

[0321] TABLE 3 Polydyes From Diacidic Compounds of Formula VI R₄—N═N—Z Example No. R₆ Z Color 134

violet 135

red 136

magenta 137

violet 138

scarlet 139

red 140

violet 141

blue 142

orange 143

scarlet 144

magenta 145

magenta 146

bluish-red 147

violet 148

blue 149

red 150

violet 151

violet 152

orange 153

red 154

navy blue 155

blue 156

red 157

orange 158

red 159

blue 160

blue 161

red 162

red 163

red 164

orange 165

yellow 166

yellow 167

orange 168

yellow 169

red 170

red 171

orange 172

blue 173

red 174

yellow 175

yellow 176

yellow 177

yellow 178

orange 179

yellow 180

yellow 181

orange 182

red

[0322] TABLE 4 Polydyes From Diacidic Compounds of Formula VII R₆—N═N—R₇—N═N—Z Example No. R₆ R₇ Z Color 183

red 184

red 185

reddish yellow 186

reddish yellow 187

red 188

yellow brown 189

blue 190

red 191

red 192

reddish orange 193

red

[0323] TABLE 5 Polydyes From Diacidic Compounds of Formula VIIa R₆—N═N—Y₁—N═N—R₆ Example No. R₆ Y₁ Color 194

red 195

orange 196

orange 197

orange 198

violet 199

red 200

violet 201

yellow 202

blue

[0324] TABLE 6 Polydyes From Diacidic Compounds of Formula VIII R₁₁—CH═D Example No. R₁₁ D Color 203

yellow 204

yellow 205

yellow 206

blue 207

yellow 208

red 209

red 210

yellow 211

yellow

[0325] TABLE 7 Polydyes From Diacidic Compounds of Formula X

Example No. R₁₁ R₁₂ Color 212

C₂H₅ red 213

H red 214

H red 215

CH₂C₆H₅ red 216

CH₃ violet 217

CH₂CH₂OH violet 218

red 219

CH₂CH₂CO₂H red 220

H red

[0326] TABLE 6 Polydyes From Diacidic Compounds of Formula XI

Example No. R₁₁ R₁₂ Color 221

H blue 222

H greenish blue 223

CH₂CN═CH₂ reddish blue 224

CH₂C₆H₁₁ blue 225

H blue 226

H blue 227

H blue 228

H blue 229

H blue 230

blue

[0327] TABLE 9 Polydyes From Diacidic Compounds of Formula XIII D═HC—R₇—N═N—Z Example No. D R₇ Z Color 231

red 232

blue 233

blue 234

blue 235

blue 236

blue 237

blue 238

blue 239

blue

[0328] TABLE 10 Polydyes From Diacidic Anthraquinone Compounds of Formula XIV

Ex- am- ple No. Q R₁₄ Color 240 5-S 1,4-diNHCH₂C(CH₂)₂CH₂OH blue 241 2-O— 1-NH₂,4-OH red 242 2-S— 1-NH₂,4-NHSO₂CH₃ violet 243 2-S— 1-NH₂,4-NHSO₂C₈H₅ violet 244 2-SO₂— 1-NH₂,4HC₆H₅ blue 245 2-SO₂— 1-NH₂,4-NHC₆H₄-4-CH₃ blue 245 2-SO₂— 1-NH₂,4-SC₆H₅ violet 247 2-S— 1-NH₂,4-NHCOC₆H₅ violet 248 4-S— 1-NH₂ red 249 4-S— 1-NHC₆H₁₁ violet 250 4-S— 1-NHC₆H₅ violet 251 4-NH— 1-NH₂,2-OCH₃ violet 252 4-NH— 1-NHC₆H₅ green 253 4-NH— 1-NHC₅H₃-2,5-diC₂H₅ blue 254 4-NH— 1-OH violet 255 2-S— 1,4-di-OH orange 256 2-SO₂— 1,4-di-OH orange 257 4-S— 1-NHCH₃ violet 258 4-S— 1-NHCH₂CH(C₂H₆)C₄H₉ violet 259 6(7)S— 1,4-diNHC₆H₃- 2,6-diC₂H₅ cyan 260 6(7)S— 1,4-diNHC₆H₂- 2,4,6-triCH₃ cyan 261 6(7)SO₂— 1,4-diNHC₅H₃-2-CH₃,C₂H₅ cyan 262 4-NH— 1,8-diOH,5-NO₂ blue 263 4-NH— 1,8-diOH,5-NH₂ blue 264 4-NH— 1,8-diOH,5-NHC₆H₆ blue 265 4-NH— 1,5-diOH,8-NO₂ blue 266 4-NH— 1-NH₂,2-CN cyan 267 4-NH— 1-NH₂,2-5-C₆H₅ blue 268 4-NH—

blue 269 4-NH—

blue

[0329] TABLE 11 Polydyes From Diacidic Anthraquinone Compounds of Formula XV

      Example No.

      R₁₄       Color 270 2,4-di-S—C₆H₄-3-CO₂H 1-NH₂ red 271 2,3-di-S—C₆H₄-4-CO₂H 1,4-diNH₂ blue 272 2,4-di-S—C₄N₄-2-CO₂H 1-NHCH₃ violet 273 2-SO₂C₆H₄-2-CO₂H,4-NHC₄-2-CO₂H 1-NH₂ blue 274 2-OC₆H₄-4-CO₂H,4-NHC₆H₄-2-CO₂H 1-NH₂ violet 275 2-OC₆H₄-3-CO₂H,4-S—NHC₆H₄-2-CO₂H 1-NH₂ red 276 2,4-di-S—C₆H₄-2-CO₂H 1-OH orange 277 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCH₃ blue 278 4,5-di-S—C₆H₄-3-CO₂H 1,8-diNHCH₂CH(CH₃)₂ blue 279 4,5-di-S—C₆H₄-4-CO₂H 1,8-diNH(CH₂)₇CH₃ blue 280 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCH₂(C₂H₅)C₂H₉ blue 281 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHC₆H₄-4-CH₃ blue 282 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHC₆H₁₁ blue 283 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNH(CH₂)₃OH blue 284 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCH₂C(CH₃)₂CH₂OH blue 285 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCH₂C₆H₅ blue 286 4,5-di-S—C₆H₄-2-CO₂H l,8-diNHCH₂CH₂C₆H₅ blue 287 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCH₂CH═CH₂ blue 288 4,5-di-S—C₆H₄-2-CO₂H 1.8-diNHCH₂C≡CH blue 289 4,5-di-S—C₆H₄-2-CO₂H

blue 290 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNHC₂H₅ blue 291 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNHCH₂CH(CH₃)CN blue 292 4,8-di-S—C₆H₄-4-CO₂H 1,5-diNHCH₂CH₂NHCOCH₃ blue 293 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNH(CH₂)₃OC₂H₅ blue 294 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNHCH₂C₅H₁₀-4-CH₃ blue 295 4,8-di-S—C₆H₄-2-CO₂H

blue 296 4,8-di-S—C₆H₄-2-CO₂H

blue 297 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNH(CH₂)₃OC₆H₅ blue 298 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNHCH(CH₃)(CH₂)₂C₆H₅ blue 299 4,8-di-S—C₆H₄-2-CO₂H 1,5-diNHCH(CH₂CH₃)₂ blue 300 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSCH₂CH₂OH red 301 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSCH₂CH₆ red 302 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSC₆H₅ red 303 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSC₆H₁₁ red 304 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSC₆H₄-4-OCH₃ red 305 4,8-di-S—C₆H₄-2-CO₂H l,5-diSC₆H₄-4-Cl red 306 4,8-di-S—C₆H₄-2-CO₂H 1,8-diSC₆H₄-4-CH₃ red 307 4,8-di-S—C₆H₄-2-CO₂H 1,8-diSC₆H₃-3,4-diCl red 308 4,8-di-S—C₆H₄-2-CO₂H 1,8-diSC₆H₄-2-NHCOCH₃ red 309 4,8-di-S—C₆H₄-2-CO₂H 1,8-diSC₆H₄-4-NHCOC₆H₅ red 310 4,8-di-S—C₆H₄-2-CO₂H 1,8-diSCH₂CH₂OCOCH₃ red 311 4,8-di-S—C₆H₄-2-CO₂H 1,5-diSC₆H₄-4-C(CH₅)₃ red 312 4,8-di-S—C₆H₄-2-CO₂H 1,5-dibenzothiazol-2-ythio red 313 4,8-di-S—C₆H₄-2-CO₂H 1,5-dibenzoxazol-2-ytthio red 314 4,8-di-S—C₆H₄-2-CO₂H

red 315 2,6-di-S—C₆H₄-2-CO₂H 1,5-diNH_(2,4,8-diOH) blue 316 2,6-di-O—C₆H₄-2-CO₂H 1,4,5,8-tetra NH₂ blue 317 4.8-di-S—C₆H₄-2-CO₂H 1,5-diNH₂,2,6-diBr blue 318 2,7-di-S—C₆H₄-2-CO₂H 1,8-diNH₂,4,5-diNHCO₂CH₃ blue 319 2,7-di-SO₂—C₆H₄-2-CO₂H 1,8-diNH₂,4,5-diOH cyan 320 4,5-di-S—C₆H₄-2-CO₂H 1,8-diNHCOCH₃ orange 321 2,7-di-S—C₆H₄-2-CO₂H 1,8-diNH₂,4,5-diNHC₆H₅ cyari 322 2,6-di-O—C₆H₄-2-CO₂H 1,8-diNH₂,4,5-diNHC₆H₁₁ blue 323 2,8-di-SO₂-C₆H₄-4-CO₂H 1,4,5,8-tetra NH₂ cyan 324 4,8-di-S—C₆H₄-2-CO₂H

blue 325 2,3-di-O—C₆H₄-4-CO₂H 1,4-diNH₂ violet 326 2,3-di-SO₂—C₆H₄-2-CO₂H 1,4-diNH₂ blue

[0330] TABLE 12 Polydyes From Diacidic Anthraquinone Compounds of Formula XVI

      Example No.

      R₁₆       Color 327

1,4-diOH orange 328

1-di-NH₂ violet 329

1-NH₃,4-OH red 330

1-NH₂,4-NHC₆H₅ violet 331

1-NH₂,4-NHC₆H₄-4-Cl blue 332

1-NH₂,4-NHC₆H₄-4-OCH₃ blue 333

1-NH₂,4-NHSO₂C₄H_(9−n) red 334

red 335

blue- green 336

1-NH₂,2-Br blue 337

1-NH₂SO₂C₆H₅-3,4-diCl blue 338

1-NH₂,2-CN cyan 339

1-NH₂,2-NO₃ cyan 340

1-NH₂,2-Br blue 341

1-NH₂,2-SO₂N(C₂H₅)₂ blue 342

1-NH₂,4-NHC₆H₄-3-Cl blue 343

1,8-diOH,5-NO₂ blue 344

1,5-diOH,8-NH₂ blue

[0331] TABLE 13 Polydyes From Diacidic Anthrapyridone Compounds of Formula XVIII

Example No.

R₁₄ R₁₅ R₁₆ Color 345

H CO₂C₂H₅ CH₃ red 346

H CN CH₂CH(CH₃)₂ violet 347

H H C₄H_(9-n) red 348

H Cl C₆H₁₁ red 349

H

CH₃ red 350

H CN C₆H₅ violet 351

H

CH₃ violet 352

H SO₂C₆H₅ CH₃ reddish blue 353

4-CH₃ CO₂C₂H₅ H red 354

H CO₂C₂H₅ H orange 355

H CN CH₃ scarlet 356

6-NHC₆H₅ CN CH₃ violet 357

6-NHC₆H₄-4-CH₃ CO₂C₂H₅ CH₃ red 358

6-NHC₆H₅ H CH₃ red 359

H COC₆H₅ CH₂CH₂OC₂H₅ red 360

H CN (CH₂)₇CH₃ violet 361

4-Br CN CH₃ violet

[0332] TABLE 14 Polydyes From Diacidic Anthraquinone Compounds of Formula XIX

Example No.

R₁₄ Color 362

H red 363

H red 364

H red 365

H red 366

1,4-diNH₂ blue 367

1,8-diNHCH₂CH(CH₃)₂ blue 368

1,5-diSC₆H₅ red 369

red 370

cyan 371

cyan 372

1,4-diNH₂ violet 373

1,8-diOH blue 374

1,8-diNHC₆H₁₁ blue 375

blue 376

1,8-diNHCH₂C(CH₃)₂CH₂OH blue 377

1,8-diNHCH₂CH(C₂H₅)C₄H_(9-n) blue 378

1,4,5,8-tetra NH₂ blue 379

1,8-diNH₂, 4,5-diOH blue 380

1,8-diNH₂, 4,5-diNHC₆h₅ cyan 381

H yellow

[0333] TABLE 15 Polydyes From Diacidic Anthraquinone Compounds of Formula XIXc

Example No.

R₁₄ Color 382

H green 383

H blue 384

H blue 385

H blue 386

H blue 387

H blue 388

1-NH₂ red 389

1,4-diNH₂ violet 390

1,4-diNH₂ blue 391

H red 392

H red 393

H red 395

H red 396

H red

[0334] TABLE 16 Polydyes From Diacidic Anthraquinone Compounds of Formula XIXd

Examle No.

R₁₄ Color 397

H red 398

1-NHC₄H_(9-n) blue 399

1-NH₂, 2-CN cyan 400

1-NH₂, 2-SO₂N(CH₃)C₆H₅ blue 401

1-NH₂, 2-CF₃ cyan 402

blue 403

1-NH₂-2-OCH₂CH₂OH violet 404

1-NH₂-2-Br blue 405

1-NH₂, 2-SO₂C₆h₅ blue 406

1-NH₂-2-Br blue 407

1-NH₂-4-OH red 408

1,4-diNH₂ violet 409

violet 410

red 411

red 412

1-NH₂, 4-NHC₆H₅ blue 413

1-NH₂, 4-NHC₆H₁₁ blue 414

1-NH₂, 4-NHC₆H₅ blue

[0335] TABLE 17 Polydyes From Diacidic Anthraquinone Compounds of Formula XIXe

Example No.

R₁₄ Color 415

H red 416

1-NHCH₃ blue 417

1-OH violet 418

1-NH₂-2-Br blue 419

1-NH₂-2-OC₆H₅ violet 420

1-NH₂-2-SO₂CH₃ blue 421

1-NH₂-2-COC₆H₅ blue 422

1-NH₂-2-CF₃ cyan 423

1-NH₂-2-CF₃ blue 424

1-NH₂-2-SO₂N(CH₃)₂ blue 425

1-NHC₆H₁₁ blue 426

1-NHC₆H₅ green 427

1-NH₂, 4-OH red 428

1-NH₂, 4-NHSO₂CH₃ red 429

1-NH₂, 4-NHCO₂C₂H₅ red 430

1-NH₂-4-NHCOC₂H₅ red 431

1,4-diNH₂ red 433

1-NH₂-4-NHCOC₂H₅ blue 434

1,8-diOH, 5-NO₂ blue 435

1-NH₂-2-SO₂C₆H₅ blue

[0336] TABLE 18 Polydyes From Diacidic Anthraquinones of Formula XIXf

Example No.

R₁₄ Color 436

H blue 437

H blue 438

H green 439

H green 440

H red 441

H red 442

1,4-diNH₂ violet 443

1,4-diNH₂ blue 444

H red 445

4,8-diNH₂3,7-diBr blue 446

1-NH₂ red 447

6,7-diCl cyan 448

H blue 449

H blue

[0337] TABLE 19 Polydyes From Diacidic Anthrapyridines Example No. Anthrapyridines Color 450

red 451

bluish- red 452

red 453

orange 454

violet 455

red

[0338] TABLE 20 Polydyes From Diacidic Nitroarylamines Example No. Nitroarylamine Compound Color 456

yellow 457

yellow 458

yellow 459

yellow 460

yellow 461

yellow 462

yellow 463

yellow 464

yellow 465

yellow

[0339] TABLE 21 Miscellaneous Polydyes Example No. Diacidic Compound Reacted 466

467

468

469

470

471

472

473

474

475

476

477

478

479

480

481

482

483

484

485

486

487

488

489

490

491

492

493

494

495

496

497

498

499

500

501

502

503

504

505

Example No. Disulfonate Compound Reacted Color 466 CH₂SO₂O(CH₂)₃OSO₂CH₃ red 467

468

469

470

471

472

yellow 473 CH₃SO₂(OCH₂CH₂)₃OSO₂CH₃ yellow 474 CH₂SO₂OCh₂CH₂SCH₂CH₂OSO₂CH₃ red 475

red 476

violet 477

yellow 478 CH₃SO₂OCH₂CH₂OSO₂CH₃ orange 479 CH₂SO₂OCH₂CH₃OCH₂CH₂OSO₂CH₃ orange 480 CH₂SO₂OCH₂CH(CH₃)CH₂OSO₂CH₃ yellow 481 CH₃CH₂SO₂OCH₂CH₂CH₂OSO₂CH₂CH₃ red 482 n-C₄H₉SO₂OCH₂CH₂CH₂CH₂OSO₃C₄H₉ yellow 483 CH₂SO₂O(CH₂)₆OSO₂CH₃ red 484

orange 485

reddish- yellow 486

yellow 487

blue 488

orange 489

yellow 490 CH₃OCH₂SO₂O(CH₂)₄OSO₂CH₂OCH₃ yellow 491 ClCH₂SO₂OCH₂CH₂OSO₂CH₂Cl yellow 492 CH₃SO₂OCH₂CH₂OCH₂CH₂OSO₂CH₃ blue 493

greenish- blue 494

greenish- blue 495

red 496 CH₃SO₂OCH₂CH₂SO₂CH₃CH₂OSO₂CH₃ orange 497 CH₂SO₂O(CH₂)_(12OSO) ₂CH₃ red 498

blue 499

orange 500 CH₂SO₂O(CH₂)₆OSO₂CH₃ red 501 CH₃SO₂OCH₂CH₂OSO₂CH₃ blue 502 CH₃SO₂OCH₂CH₂OCH₂CH₂OSO₂CH₃ blue 503 CH₃SO₂OCH₂CH₂SCH₂CH₂OSO₂CH₃ 504

reddish- yellow 505 CH₃SO₂OCH₂CH₂OSO₂CH3 red

[0340] TABLE 22 Miscellaneous Polydyes Exam- ple No. Diacidic Compound Reacted Disulfonate Compound Reacted 506

CH₂SO₂O(CH₂)₆OSO₂CH₃ 507

CH₃SO₂OCH₂CH₃OSO₂CH₃ d508

509

CH₂SO₂O(CH₂)₄OSO₂CH₃ 510

CH₃SO₂O(CH₂)₃OSO₂CH₃ 511

CH₃SO₂O(CH₂)₆OSO₂CH₃ 512

CH₃SO₂OCH₂CH₂OSO₂CH₃ 513

CH₃SO₂O(CH₂)₄OSO₂CH₃ 514

CH₃SO₂O(CH₂)₆OSO₂CH₃ 515

CH₃SO₂OCH₂CH(CH₃)CH₂OSO₂CH₃ 516

CH₃SO₂O(CH₂CH₂O)₃SO₂CH₃ 517

CH₃SO₂OCH₂CH₂OSO₂CH₃ 518

CH₃SO₂OCH₂CH₂SCH₂CH₂OSO₂CH₃ 519

CH₃SO₂O(CH₂)₆OSO₂CH₃ 520

521

522

[0341] TABLE 23 Polymeric Infrared Light Absorbers Example No. Diacidic Compound Reacted Disulfonate Compound Reacted 523

CH₃SO₂OCH₂CH₂OSO₂CH₃ 524

CH₃SO₂O(CH₂)₃OSO₂CH₃ 525

CH₃SO₂O(CH₂)₄OSO₂CH₃ 526

CH₃SO₂O(CH₂)₆OSO₂CH₃ 527

CH₃SO₂O(CH₂)₁₂OSO₂CH₃ 528

CH₃SO₂OCH₂CH₂OCH₂CH₂OSO₂CH₃ 529

CH₃SO₂OCH₂CH₂OSO₂CH₃ 530

CH₃SO₂OCH₂CH₂CH₂OSO₂CH₃ 531

CH₃SO₂OCH₂CH₂OSO₂CH₃ 532

CH₃SO₂OCH₂CH₂OSO₂CH₃ 533

CH₃SO₂OCH₂CH₂OSO₂CH₃ 534

CH₃SO₂OCH₂CH₂OSO₂CH₃ 535 NcSi(OC₄H₉-³⁻⁶-a(CO₂H)₂ CH₃SO₂OCH₂CH₂OSO₂CH₃ Nc = naphthalocyanine 535

CH₃SO₂O(CH₂)₆OSO₂CH₃

EXAMPLE 537

[0342] To dimethylfomamide (DMF, 45.0 mL) was added 1,5-bis(2-carboxyphenyl-thio)anthraquinone (17.9 g, 0.035 mole). The mixture was stirred for about 10 minutes and then 1,8-diazabicyclo[5,4,0]undec-7-ene (DBU, 10.4 g, 0.068 mole) was added followed by 1,2-ethanediol, dimethanedisulfonate (7.64 g, 0.035 mole) and additional DMF (10.0 mL). The reaction mixture was stired at about 110° C. for 3.0 hours and allowed to cool to about 55° C. Methanol (35.0 g) was added dropwise with stirring followed by water (20 mL) and acetic acid (3.0 mL). The yellow solid was collected by filtration, washed with methanol (25 mL), warm water (50 mL) and then finally with methanol to facilitate drying. The yield of polymeric and cyclic yellow product was 18.2 g.

EXAMPLES 538-543

[0343] The procedure described in Example 537 was repeated exactly except that the reactant X—B—X₁ used in each example was as follows:

[0344] Example 538: 1,3-propanediol, dimethanedisulfonate

[0345] Example 539: 1,4-butanediol, dimethanedisulfonate

[0346] Example 540: diethylene glycol, dimethanedisulfonate

[0347] Example 541: 1,6-hexanediol, dimethanedisulfonate

[0348] Example 542: 1,4-cyclohexanedimethanol, dimethanedisulfonate

[0349] Example 543: 1,12-dodecanediol, dimethanedisulfonate The weight yields (Weight, g), percent yields (Yield), weight average molecular weights (Mw), number average molecular weights (Mn), and polydispersities (Mw/Mn, by GPC) for each of the light absorbing (yellow) compositions prepared in Examples 537-543 are presented in Table 24. The percent yields were calculated by dividing the actual weight of the polymer

[0350] obtained in grams by the theoretical number of moles of repeating unit multiplied by the gram molecular weight of the repeating unit and then multiplying the number thus obtained by 100. TABLE 24 Example Weight Yield Mw Mn Mw/Mn 537 18.2 96.6 7,512 1,106 6.8 538 18.8 97.2 5,224 1,051 5.0 539 19.4 98.0 13,856 1,202 11.5 540 20.1 98.7 9,849 1,840 5.4 541 20.2 97.4 7,396 870 8.5 542 20.7 95.3 3,685 808 4.6 543 22.7 95.5 5,503 1,116 4.9

[0351] The approximate amount of cyclic compounds of formula I-A present in each of the light absorbing compositions produced in Examples 537-543 was determined by a combination of GPC, NMR and FDMS analyses. The weight percentages of the cyclic compounds having the structure

[0352] wherein m is 1, 2, 3, or 4 present in the compostiion of Examples 537-543 is set forth in Table 25. The remainder or balance of the light absorbing compositions was presumed to be a linear polymer. TABLE 25 Example m = 1 m = 2 m = 3 m = 4 537 0.1 3.4 1.5 0.7 538 0.8 3.3 1.3 <0.1 539 6.9 4.1 1.3 0.2 540 9.5 3.1 0.8 <0.1 541 26.7 4.0 1.1 0.2 542 20.4 4.0 0.7 <0.1 543 20.1 2.2* 0.5* <0.1 

We claim:
 1. A method comprising reacting a) at least one diacidic monomer, comprising about 1 to 100 mole % of at least one light-absorbing monomer having a light absorption maximum between about 300 nm and about 1200 nm and 99-0 mole % of a non-light absorbing monomer which does not absorb significant light at wavelengths above 300 nm or has a light absorption maximum below 300 nm, with b) an organic compound having the formula X—B—X₁ wherein B is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃— C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene- C₁—C₄ alkylene, C₂— C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L- C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from the group consisting of —O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; X and X₁ are reactive groups and are independently selected from the group consisting of bromine, iodine and R—SO₂O; wherein R is selected from the group consisting of C₁—C₆ alkyl; C₁—C₆ alkyl substituted with chlorine, fluorine, C₁—C₆ alkoxy, aryl, aryloxy, arylthio or C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl or aryl, wherein said reaction is carried out in a solvent in the presence of a base to form a light absorbing polymeric composition having the formula

wherein B is as defined above, n is at least 2 and A comprises the residue of said diacidic monomer.
 2. The process of claim 1 where said light-absorbing monomers have the formula H—Y—H wherein H represents an acidic hydrogen atom; Y is a divalent light-absorbing moiety selected from the group consisting of chromophoric classes of azo, disazo, triazo, bis-azo, methine, arylidene, polymethine, azo-methine, azamethine, anthraquinone, anthrapyridone (3H-dibenz[f,ij]isoquinoline-2,7-dione, nitroarylamines anthrapyridine (7H-dibenz[f,ij]isoquinoline-7-one, phthaloylphenothiazine (14H-naphth[2,3-a]phenothiazine-8,13-dione, benzanthrone (7H(de)anthracene-7-one), anthrapyrimidine (7H-benzo[e]perimidine-7-one), anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, fluorindine (5,12-dihydroquinoxaline [2,3-b]phenazine, quinophthalone, phthalocyanine, metal phthalocyanine, naphthalocyanine, metal naphthalocyanine, nickel dithiolenes, squarylium compounds, croconium compounds, coumarin (2H-1-benzopyran-2-one), coumarin imine (2H-1-benzopyran-2-imine), perinone, benzodifuran, phthaloylacridone, phthaloylphenoxazine (14H-naphtho[2,3-a]phenoxazine-8,13-done, phthaloylacridone (13H-naphtho[2,3-c] acridine-5,8,14-trione), anthraquinonethioxanthane (8H-naphtho[2,3-c]thioxanthene-5,8,13-trione, anthrapyridazone, pyrrolo[3,4-c]pyrrole, indigo, thioindigo, quinoline, xanthene, acridine, azine, cyanine, oxazine, 1,4 and 1,5-naphthoquinones, 2,5-diarylaminoterephthalic acids and esters, pyromellitic acid dimide, naphthalene-1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylenetetracarboxylic acid diimide, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline, arylisoindoline, hydroxybenzophenone, benoztriazole, naphthotriazole, diminoisoindoline, naphthopyran (3H-naphtho[2,1-6]pyran-3-one and 3-imine, phthalimides, 2-arylbenzazoles, carbostyryls, 1,2-diarylethenes, 2,5-diarylthiophenes, 2,5-diaryl-1,3,4-oxadiazoles, triazines, 2,5-diarylfurans, 2,5-diaryl-1,3,4-thiadiazoles, thiophenes, 1,3-diphenyl-2-pyrazolines, 2-arylbenzofurans, 2,6-diphenylbenzofurans, quinolines, quinoxalines, 3,4-diarylfuanones, distyrylarenes, benzanthrones, polyarenes and naphthalimides.
 3. The method of claim 2 wherein the hydrogen atoms of said formula H—Y—H are independently bonded to an oxygen, sulfur, or nitrogen atom which is a part of the light absorbing moiety Y and which in combination provides two acidic functional groups.
 4. The method of claim 3 wherein said acidic functional groups have pKa values of from about 1.5 to about
 12. 5. The method of claim 3 wherein said acidic functional groups are independently selected from the group consising of —CO₂H, —SH, —OH attached to an aromatic ring, —CONHCO—, —SO₂—NH—CO—, —SO₂—NH—SO₂—, 1(H)-1,2,4-triazol-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from the group consisting of C₁—C₆ alkyl, C₃—C₈ cycloalkyl, aryl and C₁—C₆ alkyl substituted with at least one group selected from the group consisting of C₁—C₆ alkoxy, aryl, aryloxy, arylthio and C₃—C₈ cycloalkyl.
 6. The method of claim 1 wherein said non light-absorbing monomers have the formula H—Y₁—H wherein H represents an acidic hydrogen atom; Y₁ is a divalent moiety selected from the group consisting of—O₂C—R₁—CO₂— and—O—R₂—O— and—O₂C—R₃—O—, wherein R₁ is selected from the group consisting of C₂—C₁₂ alkylene, 1-4-cyclohexylene, arylene, arylene-O-arylene, arylene—SO₂—arylene, arylene-S-arylene, and C₁—C₄ alkylene-O- C₁—C₄ alkylene; wherein R₂ is selected from the group consisting of arylene, arylene-O-arylene, arylene-S-arylene, arylene-SO₂-arylene, phenylene-phenylene, and phenylene-C(R₄)₂-phenylene; wherein R₄ is selected from the group consisting of hydrogen and C₁—C₄ alkyl; wherein R₃ is selected from arylene.
 7. The method of claim 1 wherein said polymeric composition is linear.
 8. The method of claim 1 wherein said diacidic monomers have pK_(a) values of about 12 or below.
 9. The method of claim 2 wherein H—Y—H includes a moiety selected from the group consisting of carboxy groups attached to an aromatic ring carbon or aliphatic carbon, hydroxy groups attached to an unsubstituted or substituted phenyl or naphthyl radical, —CO—NHCO— groups attached to an aromatic ring to provide an imide and 1(H)-1,2,4-triazol-3-yl group having the formula

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl and aryl.
 10. The method of claim 1 where n is between about 2 and about
 25. 11. The method of claim 1 wherein n is between about 3 and about
 15. 12. The method of claim 1 wherein said base is selected from the group consising of alkali metal carbonates, alkali metal bicarbonates and tertiary amines, aromatic nitrogen bases, bicyclic nitrogen containing bases having non-hindered electron pairs and mixtures thereof.
 13. The method of claim 12 wherein said base is selected from the group consisting of triethylamine, tri-n-butylamine, N-methylpiperidine, N,N′-dimethylpiperazine, N-methylmorpholine and N,N,N′,N′-tetramethylethylenediamine, pyridines, picolines, quinolines, isoquinolines, N-alkylpyrroles, N-alkylimidazoles, 1,8-diazabicyclo[5,4,0]undec-7-ene (DBU) 1,5-diazabicylco[4,3,0]non-5-ene (DBN) and 1,4-diazadicyclo[2,2,2]octane (DABCO®) and mixtures thereof.
 14. The method of claim 1 wherein said solvent is one or more aprotic polar solvents.
 15. The method of claim 1 wherein said solvent is selected from the group consisting of N,N-dimethylacetamide, N,N-dimethylformamide, N-methyl-2-pyrrolidone, N-methyl-N-phenyl formamide, dimethylsulfoxide, aliphatic nitriles, sulfolane, hexamethyl phosphoramide, water, alcohols, ketones pyridine and ether-alcohols and mixtures thereof.
 16. The method of claim 15 wherein said solvent is selected from the group consisting of N,N-dimethylacetamide, N,N-dimethylformamide, N-methyl-2-pyrrolidone, N-methyl-N-phenyl formamide, dimethylsulfoxide, aliphatic nitriles, sulfolane and hexamethyl phosphoramide and mixtures thereof.
 17. The method of claim 1 wherein said reacting is conducted at a temperature between about 75° C. and about 125° C.
 18. The method of claim 1 wherein said organic compound having the formula X—B—X₁ is selected from the group consisting of disulfonate compounds where X and X₁ are both a sulfonate ester of the formula-OSO₂R, wherein R is selected from C₁—C₄ alkyl, phenyl or p-methylphenyl and wherein B is selected from C₂—C₆ alkylene, —CH₂-1,4-cyclohexylene-CH₂—, —CH₂CH₂(O CH₂CH₂)₁₋₄ and—CH₂CH₂O-1,4-phenylene-O—CH₂CH₂—.
 19. The method of claim 18 wherein said B moiety of organic compound of Formula II is selected from the group consisting of—CH₂CH₂—, —CH₂CH(CH₃)CH₂—, —CH₂C(CH₃)₂CH₂—, —(CH₂)₄—, —(CH₂)₆—, —CH₂CH₂OCH₂CH₂— and—CH₂-1,4-cyclohexylene-CH₂—.
 20. The method of claim 1 wherein said organic compound having the formula X—B—X₁ is selected from the group consisting of 1,2-ethandiol, dimethanesulfonate; 1,2-ethanediol bis(4-methylbenzenesulfonate); 1,4 butanediol, dimethane sulfonate; 1,6-hexanediol, dimethanesulfonate; 1,3-propanediol, 2,2-dimethyl-, dimethanesulfonate; 1,4-cyclohexanedimethanol, dimethanesulfonate; 1,1,3,3-tetramethylcyclobutanediol, dimethanesulfonate, and ethanol 2,2′-oxybisdimethanesulfonate.
 21. The method of claim 1 wherein A of said light absorbing polymeric composition comprises 100 mole % of said light-absorbing monomer.
 22. The method of claim 1 wherein said diacidic light absorbing monomer has a light absorption maximum between about 300 nm and about 1200 nm and is present in said light absorbing polymeric composition in an amount at least about 50% by weight %.
 23. A light absorbing composition having the formula

wherein A₁ comprises the residue of at least one diacidic monomer having a light absorption maximum between about 300 nm and about 1200 nm, and wherein B is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃—C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, and C₂— C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L- C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; wherein n is at least
 2. 24. A composition comprising a thermoplastic polymer blended with at least one light absorbing linear polymeric composition of claim 23 .
 25. The composition of claim 24 wherein said thermoplastic polymer is selected from the group consisting of polyesters, polyolefins, polyamides, polyimides, polyvinyl chloride, polyurethanes, polycarbonates, cellulose esters, polyacrylates, polyvinylesters, polyester-amides, polystyrene, polyacrylonitrile-butadiene- styrene, polystyrene-acrylonitrile and mixtures and blends thereof.
 26. The composition of claim 23 wherein A₁ comprises the residue of at least one diacidic monomer having the structure H—Y—H wherein H represents an acidic hydrogen atom and Y is a divalent light-absorbing moiety selected from the chromophoric classes consisting of azo, disazo, triazo, bis-azo, methine, arylidene, polymethine, azo-methine, azamethine, anthraquinone, anthrapyridone (3H-dibenz[f,ij] isoquinoline-2,7-dione, nitroarylamines anthrapyridine (7H-dibenz[f,ij]isoquinoline-7-one, phthaloylphenothiazine (14H-naphth[2,3-a]phenothiazine-8,13-dione, benzanthrone (7H(de)anthracene-7-one), anthrapyrimidine (7H-benzo[e]perimidine-7-one), anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, fluorindine (5,12-dihydroquinoxaline [2,3-b]phenazine, quinophthalone, phthalocyanine, metal phthalocyanine, naphthalocyanine, metal naphthalocyanine, nickel dithiolenes, squarylium compounds, croconium compounds, coumarin (2H-1-benzopyran-2-one), coumarin imine (2H-1-benzopyran-2-imine), perinone, benzodifuran, phthaloylacridone, phthaloylphenoxazine (14H-naphtho[2,3-a]phenoxazine-8,13-done, phthaloylacridone (13H-naphtho[2,3-c] acridine-5,8,14-trione), anthraquinonethioxanthane (8H-naphtho[2,3-c]thioxanthene-5,8,13-trione, anthrapyridazone, pyrrolo[3,4-c]pyrrole, indigo, thioindigo, quinoline, xanthene, acridine, azine, cyanines, oxazine, 1,4 and 1,5-naphthoquinones, 2,5-diarylaminoterephthalic acids and esters, pyromellitic acid dimide, naphthalene-1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylenetetracarboxylic acid diimide, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline, arylisoindoline, hydroxybenzophenone, benoztriazole, naphthotriazole, diminoisoindoline, naphthopyran (3H-naphtho[2,1-6]pyran-3-one and 3-imine, phthalimides, 2-arylbenzazoles, carbostyryls, 1,2-diarylethenes, 2,5-diarylthiophenes, 2,5-diaryl-1,3,4-oxadiazoles, triazines, 2,5-diarylfurans, 2,5-diaryl-1,3,4-thiadiazoles, thiophenes, 1,3-diphenyl-2-pyrazolines, 2-arylbenzofurans, 2,6-diphenylbenzofurans, quinolines, quinoxalines, 3,4-diarylfuanones, distyrylarenes, benzanthrones, polyarenes and naphthalimides.
 27. The light absorbing linear polymeric composition of claim 23 or 26 wherein A₁ further comprises less than about 50% by weight of the total composition of a residue of at least one non-light absorbing monomer having the formula H—Y₁—H wherein Y₁ is a divalent moiety, selected from the group consisting of—O₂C—R₁—CO₂— and—O—R₂—O— and—O₂C—R₃—O—, wherein R₁ is selected from the group consisting of C₂—C₁₂ alkylene, 1-4-cyclohexylene, arylene, arylene-O-arylene, arylene-SO₂-arylene, arylene-S-arylene, and C₁—C₄ alkylene-O- C₁—C₄ alkylene; wherein R₂ is selected from the group consisting of arylene, arylene-O-arylene, arylene-S-arylene, arylene-SO₂-arylene, phenylene-phenylene, and phenylene-C(R₄)₂-phenylene; wherein R₄ is selected from the group consisting of hydrogen and C₁—C₄ alkyl; wherein R₃ is arylene; wherein B is is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene-C₃—C₈-cycloalkylene-C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, and C₂—C₄-alkylene-L-arylene-L-C₂—C₄ alkylene and C₂—C₄ alkylene-(L-C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; wherein n is at least
 2. 28. The light absorbing linear polymeric composition of claim 25 wherein A₁ comprises the residue of at least one diacidic monomer having at least one acidic group other than carboxy and having a light absorption maximum between about 300 nm and about 1200 nm and wherein B is a divalent organic radical selected from C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃—C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, and C₂— C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L-C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl—, —N(SO₂ C₁—C₆ alkyl)—, —(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; wherein n is at least
 2. 29. The process of claim 2 wherein said light absorbing monomer comprises two carboxy groups as acidic functional groups.
 30. The process of claim 2 wherein said light absorbing monomer comprises two 1(H)-1,2,4-triazol-3-ylthio groups as acidic functional groups.
 31. The process of claim 2 wherein said light absorbing monomer comprises one carboxy and one 1(H)-1,2,4-triazol-3-ylthio group as acidic functional groups.
 32. The process of claim 2 wherein said light absorbing monomer comprises two hydroxy groups attached to aromatic ring(s).
 33. The process of claim 2 wherein said light absorbing monomer comprises one imide group and one carboxy group.
 34. The process of claim 2 wherein said light absorbing monomer comprises one imide group and one 1(H)-1,2,4-triazol-3-ylthio group.
 35. The composition of claim 25 wherein said light absorbing monomer comprises two carboxy groups as acidic functional groups.
 36. The composition of claim 25 wherein said light absorbing monomer comprises two 1(H)-1,2,4-triazol-3-ylthio groups as acidic functional groups.
 37. The composition of claim 25 wherein said light absorbing monomer comprises one carboxy and one 1(H)-1,2,4-triazol-3-ylthio group as acidic functional groups.
 38. The composition of claim 25 wherein said light absorbing monomer comprises two hydroxy groups attached to aromatic ring(s).
 39. The composition of claim 25 wherein said light absorbing monomer comprises one imide group and one carboxy group.
 40. The composition of claim 23 wherein said light absorbing monomer comprises one imide group and one 1(H)-1,2,4-triazol-3-ylthio group.
 41. The composition of claim 23 wherein said light absorbing monomer comprises a diacidic sulfamoyl (—SO₂NH₂) group.
 42. The composition of claim 25 wherein said light absorbing monomer comprises two acidic groups independently selected from the group consisting of —CO₂H, SH, hydroxy attached to an aromatic ring, —CONHCO— (imide), —SO₂NHCO—, —SO₂NHSO₂—, 1(H)-1,2,4-triazolyl-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to an aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from the group consisting of C₁—C₆ alkyl; C₁—C₆ alkyl substituted with at least one group selected from C₁—C₆ alkoxy, aryl, aryloxy, arylthio and C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl; aryl.
 43. The composition of claim 27 wherein said light absorbing monomer comprises two carboxy groups as acidic functional groups.
 44. The composition of claim 27 wherein said light absorbing monomer comprises two 1(H)-1,2,4-triazol-3-ylthio groups as acidic functional groups.
 45. The composition of claim 27 wherein said light absorbing monomer comprises one carboxy and one 1(H)-1,2,4-triazol-3-ylthio group as acidic functional groups.
 46. The composition of claim 27 wherein said light absorbing monomer comprises two hydroxy groups attached to aromatic ring(s).
 47. The composition of claim 27 wherein said light absorbing monomer comprises one imide group and one carboxy group.
 48. The composition of claim 27 wherein said light absorbing monomer comprises one imide group and one 1(H)-1,2,4-triazol-3-ylthio group.
 49. The composition of claim 27 wherein said light absorbing monomer comprises a diacidic sulfamoyl (—SO₂NH₂) group.
 50. The composition of claim 27 wherein said light absorbing monomer comprises two acidic groups independently selected from—CO₂H, SH, hydroxy attached to an aromatic ring, —CONHCO— (imide), —SO₂NHCO—, —SO₂NHSO₂—, 1(H)-1,2,4-triazolyl-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to an aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from C₁—C₆ alkyl; C₁—C₆ alkyl substituted with at least one group selected from C₁—C₆ alkoxy, aryl, aryloxy, arylthio and C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl; aryl.
 51. The light absorbing linear polymeric composition of claim 27 wherein said at least one diacidic monomer comprises at least about 50% by weight of the total composition.
 52. The composition of claim 51 wherein the light absorbing portion of A comprises the residue of at least one diacidic light absorbing monomer selected from the group consisting of the anthraquinone and anthrapyridone colorants having the structures:

wherein R₁₄ is selected from the group consisting of hydrogen and 1-4 groups selected from amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, halogen, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, NHCO C₁—C₆ alkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl, C₁—C₆ alkoxycarbonyl, aryloxy, arylthio, heteroarylthio, cyano, nitro, trifluoromethyl, thiocyano, SO₂ C₁—C₆ alkyl, SO₂ aryl, —SO₂NH C₁—C₆ alkyl, —SO₂N(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON(C₁—C₆ alkyl)₂, CON(C₁—C₆ alkyl) aryl, C₁—C₆ alkyl, furfurylamino, tetrahydrofurfurylamino, 4-(hydroxymethyl) cyclohexanemethylamino,

or hydroxy; Q and Q′ are independently selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; R₁₅ is selected from the group consisting of hydrogen, cyano, C₁—C₆ alkylamino, C₁—C₆ alkoxy, halogen, arylthio, aryl, heteroaryl, heteroarylthio, C₁—C₆ alkoxycarbonyl, aroyl or arylsulfonyl; R₁₆ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl and aryl; R₁₆′ is selected from the group consisting of hydrogen, C₂—C₆ alkyl, halogen and C₁—C₆ alkoxy; wherein each C₁—C₆ alkyl group and C₁—C₆ alkyl group which is a portion of another group may contain at least one substituent selected from the group consisting of hydroxy, cyano, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkoxy, C₁—C₆ alkylcyclohexyl, hydroxmethyl cyclohexyl, aryl and heteroaryl; with the provision that two acidic groups containing one acidic proton each or one acidic group containing two acidic hydrogens be present in the diacidic compounds.
 53. The composition of claim 26 or 27 wherein the light absorbing portion of A comprises the residue of at least one light absorbing monomer selected from the group consisting of azo, disazo, bis-azo and azomethine and having respectively the structures: R₆—N═N—Z, R₆—N═N—R₇—N═N—Z, R₆—N═N—Y₁—N═N—R₆ and D═HC—N═N—Z wherein R₆ is the residue of an aromatic or heteroaromatic amine which has been dizaotized and coupled with a coupling component H-Z and is derived from an amine selected from the group consisting of aromatic and heteroaromatic amine classes selected from the group consisting of aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino-2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz-2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino-1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide with said aromatic and heteroaromatic ring systems being unsubstituted or substituted with one or more groups selected from C₁—C₁₀ alkyl, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl, carboxy, halogen, C₁—C₆ alkoxycarbonyl, formyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, dicyanovinyl, C₃—C₈-cycloalkanoyl, thiocyano, trifluroacetyl, cyano, carbamoyl, —CONH—C₁—C₆ alkyl, CONHaryl, CON(C₁—C₆ alkyl)₂, sulfamoyl, SO₂NH C₁—C₆ alkyl, SO₂N(C₁—C₆ alkyl)₂, SO₂NHaryl, SO₂NH C₃—C₈ cycloalkyl, CONH C₃—C₈ cycloalkyl, aryl, aroyl, —NHSO₂ C₁—C₆ alkyl, —N(C₁—C₆ alkyl)SO₂ C₁—C₆ alkyl, —NHSO₂ aryl, NHCO C₁—C₆ alkyl, NHCO C₃—C₈ cycloalkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHCONH C₁—C₆ alkyl, NHCONHaryl, N(C₁—C₆ alkyl)aryl, arylazo, heteroaryl, aryloxy, arylthio, C₃—C₈ cycloalkoxy, heteroarylazo, heteroarylthio, arylsulfonyl, tricyanovinyl, aryloxysulfonyl, C₁—C₆ alkylsulfonyl, trifluoromethyl, fluorosulfonyl, trifluoromethylsulfonyl, thiocyano, hydroxy, nitro or CH═D, wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂; wherein R₇ is a divalent aromatic or heteroaromatic radical selected from the group consisting of 1,4-phenylene, naphthalene-1,4-diyl, thiazol-2,5-diyl and thiophene-2,5-diyl:

wherein R₈ is selected from the group consisting of hydrogen or 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, cyano, halogen, —NHCO C₁—C₆ alkyl, —NHCO₂ C₁—C₆ alkyl, —NHCO aryl, —NHCONH aryl or NHCONH C₁—C₆ alkyl; R₉ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, halogen, aryl, heteroaryl; R₁₀ is selected from the group consisting of hydrogen, C₁—C₆ alkoxycarbonyl, cyano, carbamoyl, aryl, arylsulfonyl, aroyl, —CONH C₁—C₆ alkyl, or C₁—C₆ alkylsulfonyl; wherein Z is the residue of a coupling compound selected from the group consisting of electron rich compound classes of anilines, 1-aminonaphthalenes, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro-2H-1,4-benzoxazine), pyrazolones, pyrazoles, 3-cyano-6-hydroxy-2-pyridones, 2,3-dihydroindoles, indoles, 4-hydroxycoumarins, 4-hydroxy-2-quinolones, imidazo[2,1-b]thiazoles, julolidines (2,3,6,7-tetrahydro-1H, 5H-benzo[ij]quinolizines), 1-oxajulolidines, 1,2,5,6-tetrahydro-4H-pyrrolo[3,2,1-ij]quinolines, 2,6-diamino-3 cyanopyridines, 2-aminothiazoles, 2-aminothiophenes, 5,5-dimethyl-1,3-cyclohexanedione (dimedone), phenols, naphthols, 2,4-pentanediones or acetoacetarylides; wherein Y₁ is the residue of a bis coupling component selected from the group consisting of anilines, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro- 2H-1,4-benzoxazines), 3-cyano-6-hydroxy-2-pyridones, 2,6-diaminopyridines, 2,3-dihydroindoles, naphthylamines, 2-aminothiazoles, or a combination of these; with the provision that two acidic functional groups containing one acidic hydrogen each or a functional group containing two acidic hydrogen are present in the diacidic light absorbing monomer.
 54. The composition of claim 53 wherein Z is selected from the group consisting of:

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl,NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl or aryl; R₁₆′ is selected from hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; Q is selected from the group consisting of —O—, —N(COR₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀), —SO₂(R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl or C₁—C₁₀alkyl; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(COC₁—C₆ alkyl)—, —N(SO₂C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of hydrogen or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 55. The composition of claim 26 or 51 wherein the light absorbing portion of A comprises the residue of at least one light absorbing monomer selected from the group consisting of methine, arylidene, polmethine, azamethine, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxypyrroline and arylisoindoline and having respectively the structures:

wherein R₁₁ is the residue of an electron rich aromatic compound selected from the group consisting of an aniline, 1-naphthylamine, 1,2-dihydroquinoline, 1,2,3,4-tetrahydroquinoline, 1,3,3-trimethyl- 2-methyleneindole, 1,3-dihydro-2-methylene- 1,1,3-trimethyl-2H-benz[e]indole, imidazo [2,1-b] thiazole, benzomorpholine (3,4-dihydro-2H-1,4, benzoxazine), 2,3-dihydroindole, indole, 2-aminothiazole, julolidine (2,3,6,7-tetrahydro-1H, 5H- benz [ij] quinolizine, 1-oxajulolidine, 4H-pyrrolo [3,2,1-ij]-quinoline, phenol, naphthol, thiophenol, pyrrole, pyrazole, furan, thiophene, carbazole, phenothiazine or phenoxazine compound; R₁₂ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ alkenyl, C₃—C₈-alkynyl, C₃—C₈ cycloalkyl, aryl, CH₂CH₂O₁₋₃ R₁₃ and C₁—C₄ alkylene- C₃—C₈ cycloalkylene, wherein the C₁—C₆ alkyl groups may be substituted by at least one group selected from the group consisting of carboxy, C₁—C₆ carbalkoxy, C₁—C₆ alkanoyloxy, cyano, hydroxy, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl or aryl; R₁₃ is selected from the group consisting of hydrogen, C₁—C₆ alkoxy or C₁—C₆ alkanoyloxy; wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups containing one acidic hydrogen each, or a functional group containing two acidic hydrogens are present.
 56. The composition of claim 55 wherein R₁₁ is selected from the group consisting of the electron rich aromatic residues corresponding to the structures:

wherein R₂₆ is selected from the group consisting of hydrogen or a group selected from the group consisting of C₁—C₆ alkoxycarbonyl, CO₂H, C₁—C₆ alkyl or C₁—C₆ alkoxy; wherein R₁₇ is selected from the group consisting of hydrogen, and 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl or aryl; R₁₆′ is selected from the group consisting of hydrogen, one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; Q is selected from the group consisting of —O—, —N(COR₁₀)—, —N(R₁₀)—, —S——SO₂—, —CO₂—, CON(R₁₀)—, SO₂(R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl or C₁—C₁₀ alkyl; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of hydrogen or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 57. The composition of claim 51 wherein the light absorbing portion of A₂ comprises a residue of at least one diacidic coumarin compounds selected from the group consisting of the structures

wherein Z₃ is selected from the group consisting of cyano, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkylsulfonyl, arylsulfonyl, aryl, heteroaryl, formyl, aroyl, C₁—C₆ alkanoyl or—CH═D, wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl,NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl or aryl; R₁₆′ is selected from hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen, and C₁—C₆ alkoxy; Q is selected from the group consisting of —O—, —N(COR₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, CON(R₁₀), SO₂(R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl or C₁—C₁₀ alkyl; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl; wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups containing one acidic hydrogen each, or a functional group containing two acidic hydrogens are present.
 58. The composition of claim 54 wherein the light absorbing portion of A₁ comprises the residue of at least one bis-azo light absorbing monomer wherein the bis coupling component Y₁ is represented by the structure Z₁-L₁-Z₂, wherein Z₁ and Z₂ are independently selected from the group consisting of

wherein, L₁ is bonded to the nitrogen atom of Z₁ and Z₂; wherein L₁ is selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, arylene, C₁—C₄ alkylene-C₃—C₈ cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, C₂—C₄ alkylene-O-arylene-O- C₂—C₄ alkylene, C₂—C₄ alkylene O₁₋₃ C₂—C₄ alkylene, C₂—C₄ alkylene- S— C₂—C₄ alkylene, C₂—C₄ alkylene-SO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ C₁—C₆ alkyl)— C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ aryl)— C₂— C₄— alkylene, C₂—C₄ alkylene- OCO₂— C₂—C₄ alkylene, C₂—C₄ alkylene- O₂C-arylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C— C₁—C₁₂ alkylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C— C₃—C₈ cycloalkylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-NHCO— C₂—C₄ alkylene and C₂—C₄ alkylene-NHSO₂— C₂—C₄ alkylene; wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl or aryl; R₁₆′ is selected from hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; Q is selected from the group consisting of —O—, —N(COR₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, CON(R₁₀), SO₂(R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl or C₁—C₁₀ alkyl; R₁₈ is selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl; R₂₀, R₂₁ R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 59. The diacidic anthraquinone compounds having Formulae

wherein R₁₄ is selected from the group consisting of hydrogen, 1-4 groups selected from amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, halogen, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, NHCO C₁—C₆ alkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl, C₁—C₆ alkoxycarbonyl, aryloxy, arylthio, heteroarylthio, cyano, nitro, trifluoromethyl, thiocyano, SO₂C₁—C₆ alkyl, SO₂ aryl, —SO₂NH C₁—C₆ alkyl, —SO₂N(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON(C₁—C₆ alkyl)₂, CON(C₁—C₆ alkyl) aryl, C₁—C₆ alkyl, furfurylamino, tetrahydrofurfurylamino, 4-(hydroxymethyl) cyclohexanemethylamino,

or hydroxy; Q and Q′ are independently selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; R₁₆′ is selected from hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; wherein each C₁—C₆ alkyl group and C₁—C₆ alkyl group which is a portion of another group may contain at least one substituent selected from the group consisting of hydroxy, cyano, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkoxy, C₁—C₆ alkylcyclohexyl, hydroxmethyl cyclohexyl, aryl and heteroaryl; with the provision that two acidic groups containing one acidic proton each or one acidic group containing two acidic hydrogens be present in the compounds of Formula XIV, XIXc, XIXd, XIXe XIXf.
 60. The diacidic anthraquinone compounds of claim 57 having the following structures:

wherein Sub is a substituent selected from the group consisting of halogen, trifluoromethyl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryloxy, arylthio, heteroarylthio, cyano, nitro, SO₂NHC₁—C₆ alkyl, SO₂N (C₁—C₆ alkyl)2, SO₂N (C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON (C₁—C₆ alkyl)₂, CON (C₁—C₆ alkyl) aryl, C₁—C₆ alkyl, SO₂ C₁—C₆ alkylsulfonyl and SO₂ aryl; Sub₁ is a substituent selected from the group consisting of amino, C₁—C₁₂ alkylamino, arylamino and C₃—C₈ cycloalkylamino.
 61. The diacidic anthrapyridone compounds having Formulae

wherein R₁₄ is selected from the group consisting of hydrogen, 1-4 groups selected from amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, halogen, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, NHCO C₁—C₆ alkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl, C₁—C₆alkoxycarbonyl, aryloxy, arylthio, heteroarylthio, cyano, nitro, trifluoromethyl, thiocyano, SO₂C₁—C₆ alkyl, SO₂ aryl, —SO₂NH C₁—C₆ alkyl, —SO₂N(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON(C₁—C₆ alkyl)₂, CON(C₁—C₆ alkyl) aryl, C₁—C₆ alkyl or hydroxy; Q and Q′ are independently selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; R₁₅ is selected from the group consisting of hydrogen, cyano, C₁—C₆ alkylamino, C₁—C₆ alkoxy, halogen, arylthio, aryl, heteroaryl, heteroarylthio, C₁—C₆ alkoxycarbonyl, aroyl or arylsulfonyl; R₁₆ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl and aryl; R₁₆′ is selected from the group consisting of hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; wherein each C₁—C₆ alkyl group and C₁—C₆ alkyl group which is a portion of another group may contain at least one substituent selected from the group consisting of hydroxy, cyano, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkoxy, C₁—C₆ alkylcyclohexyl, hydroxmethyl cyclohexyl, aryl and heteroaryl; with the provision that two acidic groups containing one acidic proton each or one acidic group containing two acidic hydrogens be present in the compounds of Formula XVIII, XVIIIa, XVIIIb, and XIXa.
 62. The diacidic anthrapyridone compound of claim 61 having the structure:


63. The diacidic anthraquinone compounds having the formulae

where R₁₆′ is selected from the group consisting of hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; and Sub₃ is a substituent selected from C₁—C₆ alkylthio, arylthio and heteroarylthio and Sub₂ is a substituent selected from the group consisting of amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, furfurylamino, tetrahydrofurfurylamino, 4-(hydroxymethyl) cyclohexanemethylamino, NHCO C₁—C₆ alkyl, NHCO aryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl and


64. The diacidic anthraquinone compounds of claim 59 having the formulae:

wherein Sub₂ is as defined in claim 63 ; Sub₄ is selected from the group consisting of Sub₂, NHCO C₁—C₆ alkyl, NHCO₂ C₁—C₆ alkyl, NHCO aryl, NHSO₂ C₁—C₆ alkyl, NHS02 aryl, C₁—C₆ alkylthio, arylthio, heteroarylthio and hydroxy; Q is selected from the group consisting of —O—, S—, —SO₂—; Q′ selected from the group consisting of —O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl.
 65. A diacidic anthraquinone compounds having the formula

wherein Sub, Sub₁ and R₁₆′ are as defined in claim 60 .
 66. The diacidic anthraquinone compounds having the structures

wherein Q is selected from the group consisting of —O—, S— and —SO₂—; Q′ is selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; and R₁₆′ is selected from the group consisting of hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy.
 67. The diacidic anthraquinone compounds having the structures:

wherein Sub₁ defined as in claim 60 , Sub₄ is defined as in claim 64 , Q is selected from the group consisting of —O—, —S—and —SO₂—; Q′ is selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; and R₁₆′ is selected from the group consisting of hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy.
 68. The diacidic anthraquinone compounds having the structures:

wherein Q is selected from the group consisting of —O—, —S— and —SO₂—; Sub₁ is a substitutent selected from the group consisting of amino, C₁—C₁₂ alkylamino, arylamino and C₃—C₈ cycloalkylamino; Q′ is selected from the group consisting of—O—, —N(CO₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; and R₁₆′ is selected from the group consisting of hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy.
 69. The diacidic azo and disazo compounds of the formulae R₆—N═N—Z (VI) and R₆—N═N—R₇—N═N—Z (VII), respectively wherein R₆ is the residue of a diazotized aromatic or heteroaromatic amine and Z is the residue of an electron rich coupling component selected from the group consisting of the classes of anilines, 1-aminonaphthalenes, 1,2-dihydroquinolines, 1,2,3,4-teterahydroquinolines, benzomorpholines (3,4-dihydro-2H-1,4-benzoxazine), pyrazolones, pyrazoles, 3-cyano-6-hydroxy-2-pyridones, 2,3-dihydroindoles, indoles, 4-hydroxycoumarins, 4-hydroxy-2-quinolones, imidazo[2,1-b]thiazoles, julolidines (2,3,6,7-tetrahydro-1H, 5H-benzo[ij]quinolizines), 1-oxajulolidines, 1,2,5,6-tetrahydro-4H-pyrrolo[3,2,1-ij]quinolines, 2,6-diamino-3 cyanopyridines, 2-aminothiazoles, 2-aminothiophenes, 5,5-dimethyl-1,3-cyclohexanedione (dimedone), phenols, naphthols, 2,4-pentanediones or acetoacetarylides; R₇ is a divalent aromatic or heteroaromatic radical selected from the group consisting of the classes of 1,4-phenylene, naphthalene -1, 4-diyl, thiazol-2,5-diyl and thiophene-2,5-diyl; with the provision that R₆ or Z contains a carboxy (—CO₂H) acidic group and that another acidic group selected from the group consisting of (—CO₂H), —SH, —OH attached to aromatic ring, —CONHCO—, —SO₂NH—CO—, —SO₂NH— SO₂—, and 1(H) 1, 2, 4-triazol-3-yl, be present on or as part of R₆ or Z so that each R₆ and Z moiety contains one acidic group.
 70. The diacidic azo and disazo compounds of claim 69 wherein R₆ and Z each contain a carboxy (—CO₂H) acidic group.
 71. The diacidic azo and bisazo compounds of claim 69 wherein R₆ is the residue of substituted diazotized aromatic or heteroaromatic amine compounds derived from the classes of aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino- 2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz-2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino-1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide and Z is the residue of an electron rich coupling coupler residue selected from the group consisting of the following:

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′, R₁₆′ and Q are as defined in claim 63 ; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 72. The diacidic azo and disazo compounds of claim 69 of the formulae R₆—N═N—Z (VI) and R₆—N═N—R₇—N═N—Z (VII), respectively, wherein one of R₆ and Z contains two carboxy (—CO₂H) acidic groups.
 73. The diacidic azo and disazo compounds of claim 69 or 72 wherein R₆ is the residue of a diazotized substituted or unsubstituted diazotized aromatic or heteromatic amine compound derived from an amine selected from aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino-2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz- 2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino- 1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide and Z is the residue of an electron rich coupling component selected from the group consisting of the following:

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′, R₁₆′ and Q are as defined in claim 63 ; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 74. The diacidic azo and bisazo compounds of claim 72 wherein Z is an electron rich coupler selected from the group consisting of the following:

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ al~kylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄, NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′, R₁₆′ and Q are as defined in claim 63 ; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 75. The diacidic bisazo compounds having the formula R₆—N═N—Y₁—N═N—R₆ (VIIa) wherein R₆ is the residue of a substituted diazotized aromatic or heteroaromatic amine compound derived from the classes of aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino-2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz- 2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino- 1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide and Y₁ is the residue of a bis coupling component selected from the group consisting of the classes of anilines, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro-2H-1,4-benzoxazines), 3-cyano-6-hydroxy-2-pyridones, 2,6-diaminopyridines, 2,3-dihydroindoles, naphthylamines, 2-aminothiazoles, or a combination of these, with the provision that each R₆ group contain one acidic group selected from the group consisting of —CO₂H, —SH, —OH attached to an aromatic ring, —NHCONH—, —SO₂NHCO—, —SO₂NHSO₂—, 1 (H)-1,2,4-triazol-3-yl-, imidazolyl, benzimidazoyl, pyrazolyl and —SO₂H attached to aromatic ring.
 76. The bis-azo compounds of claim 75 wherein each R₆ group contains one carboxy (—CO₂H) group.
 77. The bis-azo compounds of claim 75 wherein Y₁ has the formula Z₁-L₁-Z₂ wherein Z₁ and Z₂ are independently selected from the group consisting of:

wherein L₁ is bonded to the nitrogen atom of Z₁ and Z₂; wherein L₁ is selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, arylene, C₁—C₄ alkylene-C₃—C₈ cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, C₂—C₄ alkylene-O- arylene-O- C₂—C₄ alkylene, (C₂—C₄ alkylene O₁₋₃ C₂—C₄ alkylene, C₂—C₄ alkylene- S— C₂—C₄ alkylene, C₂—C₄ alkylene-SO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ C₁—C₆ alkyl)— C₂—C₄ alkylene, C₂—C₄ alkylene-N(SO₂ aryl)— C₂—C₄— alkylene, C₂—C₄ alkylene-OCO₂— C₂—C₄ alkylene, C₂—C₄ alkylene- O₂C-arylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C— C₁—C₁₂ alkylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-O₂C— C₃—C₈ cycloalkylene-CO₂— C₂—C₄ alkylene, C₂—C₄ alkylene-NHCO— C₂—C₄ alkylene and C₂—C₄ alkylene-NHSO₂— C₂—C₄ alkylene; R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₆ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′, R₁₆′ and Q are as defined in clain 63; R₁₈ is selected from the group consisting of hydrogen, a group selected from the group consisting of unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl; R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl.
 78. The diacidic methine, arylidene, polymethine, azamethine, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene -2-oxypyrroline and aryl isoindoline corresponding to formulae VIII, VIIIa, VIIIb, IX, X, XI and XII, respectively:

wherein R₁₁ is the residue of an aniline, 1-naphthylamine, 1,2-dihydroquinoline, 1,2,3,4-tetrahydroquinoline, 1,3,3-trimethyl-2-methyleneindole, 1,3-dihydro-2-methylene-1,1,3-trimethyl-2H-benz[e]indole, imidazo [2,1-b] thiazole, benzomorpholine (3,4-dihydro-2H-1,4,benzoxazine), indole, 2,3-dihydroindole, 2-aminothiazole, julolidine (2,3,6,7-tetrahydro-1H, 5H- benz [ii] quinolizine, 1-oxajulolidine, 4H-pyrrolo [3,2,1-ij]-quinoline, phenol, naphthol, thiophenol, pyrrole, pyrazole, furan, thiophene, carbazole, phenothiazine or phenoxazine compound; R₁₂ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ alkenyl, C₃—C₈-alkynyl, C₃—C₈ cycloalkyl, aryl, CH₂CH₂O₁₋₃ R₁₃ and C₁—C₄ alkylene- C₃—C₈ cycloalkylene, wherein the C₁—C₆ alkyl groups may be substituted by at least one group selected from the group consisting of carboxy, C₁—C₆ carbalkoxy, C₁—C₆ alkanoyloxy, cyano, hydroxy, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl or aryl; R₁₃ is selected from the group consisting of hydrogen, C₁—C₆ alkoxy or C₁—C₆ alkanoyloxy; wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis (dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups selected from the group consisting of —CO₂H, —SH, —OH attached to aromatic ring, —CONHCO—, —SO₂NHCO—, —SO₂NHSO₂—, 1(H) -1,2,4, -triazol-3-yl, imidazolyl, benzimidazolyl, pyrazolyl and SO₂H attached to aromatic ring be present or one diacidic sulfamoyl (—SO₂NH₂) be present.
 79. The diacidic anthrapyridine compounds having the structures:

wherein Sub₅ in a substituent selected from the group consisting of —N (C₁—C₁₀ alkyl)₂, —N (C₁—C₁₀ alkyl) aryl, —N (C₁—C₁₀ alkyl) C₃—C₈ cycloalkyl, miorpholino and piperidino; Q and Q′ are selected fromn the group consisting of —NH—, —O—, —S—and —SO₂—, R₁₆′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy.
 80. The nitroarylamine compounds having the structure:

wherein ring A may be substituted with one or more groups selected from the group consisting of halogen, —SO₂N(C₁—C₆ alkyl)₂, —CON (C₁—C₆ alkyl)₂, SO₂ C₁—C₆ alkyl, SO₂ aryl, C₁—C₆ alkyl, C₁—C₆ alkoxy, carboxy, and nitro; Ar is phthalimid-3 (or 4)-yl, phenyl, or 2-thienyl, or these substituted with one or more groups selected from the group consisting of halogen, C₁—C₆ alkyl, C₁—C₆ alkoxy, 1(H)-1,2,4, -triazolyl-3-ylthio, carboxy, or hydroxy, with the provision that two acidic groups be present.
 81. The nitroarylamine compounds of claim 80 wherein two carboxy groups are present on Ar or ring A or one carboxy is present on each of Ar and ring A.
 82. The diacidic compounds of claim 72 , having the formula R₆—N═N—Z, wherein R₆ is selected from the group consisting of

wherein Sub₆ is selected from the group consisting of hydrogen, one to four groups selected from C₁—C₁₀ alkyl, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl, halogen, , C₁—C₆ alkoxycarbonyl, formyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, dicyanovinyl, C₃— C₈-cycloalkanoyl, thiocyano, trifluroacetyl, cyano, carbamoyl, —CONH C₁—C₆ alkyl, CONHaryl, CON(C₁—C₆ alkyl)₂, SO₂N(C₁—C₆ alkyl)₂, CONH C₃—C₈ cycloalkyl, aryl, aroyl, —N(C₁—C₆ alkyl)SO₂ C₁—C₆ alkyl, NHCO C₁—C₆ alkyl, NHCO C₃—C₈ cycloalkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHCONH C₁—C₆ alkyl, NHCONHaryl, N(C₁—C₆ alkyl)aryl, arylazo, heteroaryl, aryloxy, arylthio, C₃—C₈ cycloalkoxy, heteroarylazo, heteroarylthio, arylsulfonyl, tricyanovinyl, aryloxysulfonyl, C₁—C₆ alkylsulfonyl, trifluoromethyl, fluorosulfonyl, trifluoromethylsulfonyl, thiocyano, nitro and CH═D, wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis (dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides and aryl-C(CH₃)C═C(CN)₂; with the provision that one acidic group selected from the group consisting of carboxy,

be present on either R₁₇ , R₁₈, R₁₉ or R₂₄; Q is selected from the group consisting of —O—, —S, and —SO₂—.
 83. The compounds of claim 82 wherein R₁₈ is selected from the group consisting of C₁—C10 alkylene-CO₂H,


84. The diacidic compounds of claim 82 wherein R₆ is selected from the group consisting of

and Z is selected from

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, halogen, NHCOR₂₄, NHCO₂R₂₄ and NHCONHR, ₂₄, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; wherein each C₁—C₁₀ alkyl group in R₂₄ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, carboxy, aryl, aryloxy, arythio, CO₂ C₁—C₆ succinimido, C₁—C₆ alkyoxy and alkyl, cyano, hydroxy,

R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ alkyl, C₃—C₈ alkenyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to from a radical

wherein Q₂ is selected from the group consisting of —O—, —S—, —SO₂, —CO—, —CO₂, —N (COC₁—C₆ alkyl)—, —N (SO₂ C₁—C₆ alkyl)—, —N (COaryl)—, and —N (SO₂ aryl)—; R₂₀, R₂₁, and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; with the provision that either R₁₇ contain one acidic group selected from the group consisting of carboxy and

with the groups R₁₈ and R₁₉ being void of acidic groups or R₁₇ may be void of acidic groups and R₁₈ be selected from the group consisting of C₁—C₁₀ alkylene —CO₂H,

wherein Q is selected from the group consisting of —O—, —S—, and —SO₂—; with the final provision that only two carboxy groups be present.
 85. The diacidic compounds of claim 61 having the formula R₆—N═N—Z wherein R₆ is the residue of a substituted heterocyclic diazotized amine and selected from the group consisting of

wherein Sub₇ is one or more substituent selected from the group consisting of hydrogen, halogen, C₁—C₆ alkyl, aryl, heteroaryl, C₁—C₆ alkanoyl, CONH C₁—C₆ alkyl, SO₂ C₁—C₆ alkyl, SO₂ aryl, C₁—C₆ alkoxycarbonyl, aroyl, cyano, formyl and nitro; Sub₈ is selected from the group consisting of hydrogen, halogen, C₁—C₆ alkyl, aryl and heteroaryl; Sub₉ is selected from the group consisting of C₁—C₆ alkyl C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, and aryl; Sub₁₀ is selected from the group consisting of cyano, nitro, C₁—C₆ alkylsulfonyl, arythio, arylsulfonyl and C₁—C₆ alkoxycarbonyl; Sub₁₁ is hydrogen one or more substituents selected from the group consisting of C₁—C₆ alkyl, cyano, nitro, halogen, arylthio, heteroarylthio, arylsulfonyl, aryloxy and C₁—C₆ alkylsulfonyl; Q is selected from the group consisting of —O—, —S—and —SO₂—; wherein Z is a coupling component selected from the group consisting of

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄, NHCO₂R₂₄, and NHCONHR₂₄, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; wherein each C₁—C₂ ₁₀ alkyl group in R₂₄ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl and aryl; R₁₆′ is selected from the group consisting of hydrogen, one or two groups selected from C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl; with the provision that one acidic group selected from the group consisting of carboxy,

be present on either R₁₇ , R₁₈, R₁₉ or R₂₄; Q is selected from the group consisting of —O—, —S, and —SO₂—; with the provision that R₆ and Z each contain one acidic group.
 86. The diacidic compounds of claim 85 having the formula R₆—N═N—Z, wherein R₆ is selected from the group consisting of

and Z is selected from the group consisting of

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, halogen, NHCOR₂₄, NHCO₂R₂₄ and NHCONHR₂₄, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; wherein each C₁—C₁₀ alkyl group in R₂₄ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, carboxy, aryl, aryloxy, arythio, CO₂ C₁—C₆ succinimido, C₁—C₆ alkyoxy and alkyl, cyano, hydroxy,

R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ alkyl, C₃—C₈ alkenyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to from a radical

wherein Q₂ is selected from the group consisting of —O—, —S—, —SO_(2,) —CO—, —CO₂, —N (COC₁—C₆ alkyl)—, —N (SO₂ C₁—C₆ alkyl)—, —N (Coaryl)—, and —N (SO₂ aryl)—; R₂₀, R₂₁, and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; with the provision that either R₁₇ contain one acidic group selected from the group consisting of carboxy and

with the groups R₁₈ and R₁₉ being void of acidic groups or R₁₇ may be void of acidic groups and R₁₈ be selected from the group consisting of C₁—C₁₀ alkylene —CO₂H,

wherein Q is selected from the group consisting of —O—, —S—, and —SO₂ —; with the final provision that only two carboxy groups be present.
 87. The diacidic compounds of claim 71 having the formula R₆—N═N—Z, wherein R₆ is the residue of a diazotized aromatic amine and is selected from the group consisting of

wherein Sub₁₂ is one or more groups selected from the group consisting of hydrogen, C₁—C₆ alkyl, cyano, nitro, C₁—C₆ alkylthio, C₁—C₆ alkylsulfonyl, aryl, heteroaryl, arylthio, arylsulfonyl, halogen, trifluoromethyl, alkanoyl, aroyl, formyl, NHCO aryl, NHCO C₁—C₆ alkyl, C₁—C₆ alkoxycarbonyl, C₁—C₆alkoxy and —SO₂N (C₁—C₆ alkyl)₂; Q is selected from the group consisting of —O—, —S—, —SO₂—, —CONH— and —SO₂N (C₁—C₆ alkyl)—; Z is selected from the group consisting of

wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O— C₂—C₆ alkylene —OH, O—C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene—C₁—C₆ alkanoyloxy, halogen, C₁—C₆ alkoxycarbonyl, trifluoromethyl, NHCOR₂₄, NHCO₂R₂₄ and NHCON(R₂₄) R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl and aryl; wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido and C₁—C₆ alkoxy; R₁₈ and R₁₉ are selected from the group consisting of hydrogen C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl, and aryl; R₁₈ and R₁₉ in combination may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —SO₂—, —S—, —CO—, —CO₂—, —N(COC₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, —N(SO₂ aryl)—; R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl; with the provision that no acidic groups be present on Z.
 88. The diacidic compounds of claim 87 wherein R₆ has the structure

and Z is selected from


89. The diacidic compound of claim 72 wherein R₆ is residue of a diazotized heterocyclic amine and is selected from the group consisting of

wherein Sub₈ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, halogen, aryl and heteroaryl; Sub₉ is selected from the group consisting of C₁—C₆ alkyl C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, and aryl; Q is selected from the group consisting of —O—, —S—and —SO₂—; with the provision that no acidic groups be present on Z.
 90. The diacidic compounds of claim 72 wherein R₆ is selected from the group consisting of

wherein Sub₈ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, heteroaryl and aryl; Sub₉ is selected from the group consisting of C₁—C₆ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl and aryl; Sub₁₃ is selected from the group consisting of hydrogen, one or more groups selected from C₁—C₁₀ alkyl, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl, halogen, , C₁—C₆ alkoxycarbonyl, formyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, dicyanovinyl, C₃— C₈-cycloalkanoyl, thiocyano, trifluroacetyl, cyano, carbamoyl, —CONH C₁—C₆ alkyl, CONHaryl, CON(C₁—C₆ alkyl)₂, SO₂N(C₁—C₆ alkyl)₂, CONH C₃—C₈ cycloalkyl, aryl, aroyl, —N(C₁—C₆ alkyl) SO₂ C₁—C₆ alkyl, NHCO C₁—C₆ alkyl, NHCO C₃—C₈ cycloalkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHCONH C₁—C₆ alkyl, NHCONHaryl, N(C₁—C₆ alkyl)aryl, arylazo, heteroaryl, aryloxy, arylthio, C₃—C₈ cycloalkoxy, heteroarylazo, heteroarylthio, arylsulfonyl, tricyanovinyl, aryloxysulfonyl, C₁—C₆ alkylsulfonyl, trifluoromethyl, fluorosulfonyl, trifluoromethylsulfonyl, thiocyano, nitro and CH═D, wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis (dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides and aryl-C(CH₃)C═C(CN)₂; Sub₁₄ is selected from the group consisting of hydrogen, halogen, cyano, C₁—C₆ alkylthio, arylthio, C₁—C₆ alkoxycarbonyl, nitro, heteroarylthio, C₁—C₆ alkylsulfonyl, arylsulfonyl, and aryloxy; Sub₁₅ is selected from the group consisting of hydrogen, C₁—C₆ alkythio, C₁—C₆ alkysulfonyl, aryl, arylazo, —CH═D, cyano, C₁—C₆ alkysulfonyl, aryl, heteroaryl, arylthio, arylsulfonyl, C₁—C₆ alkoxy, trifluoromethyl and C₁—C₆ alkoxycarbonyl; Sub₁₆ is selected from the group consisting of hydrogen, one or two groups selected from halogen, C₁—C₆ alkylsulfonyl, nitro, cyano, C₁—C₆ alkoxycarbonyl, thiocyano and C₁—C₆ alkylthio; Sub₁₇ is selected from the group consisting of hydrogen, one or two groups selected from C₁—C₆ alkyl, halogen, nitro and SO₂N (C₁—C₆ alkyl)₂; Sub₁₈ is selected from the group consisting of hydrogen, aryl, C₁—C₆ alkylthio, C₁—C₆ alkylsulfonyl and heteroaryl; Sub₁₉ is selected from the group consisting of hydrogen, one or more groups selected from C₁—C₆ alkyl, cyano, nitro, aryl, heteroaryl, arylazo, —CH═D, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkylsulfonyl, arylsulfonyl, CONH C₁—C₆ alkyl, C₁—C₆ alkanoyl, aroyl, halogen, formyl and heteroarylazo; Sub₂₀ is selected from the group consisting of hydrogen, one or two groups selected from C₁—C₆ alkyl, aryl, cyano, nitro, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkysulfonyl, arylazo, heteroarylazo, heteroaryl, SO₂N (C₁—C₆ alkyl)₂, formyl, and —CH═D; Sub₂₁ is selected from the group consisting of hydrogen, one to three groups selected from C₁—C₆ alkyl, halogen, cyano, C₁—C₆ alkylthio, C₁—C₆ alkylsulfonyl, arylsulfonyl, arylthio, heteroarylthio, C₁—C₆ alkoxy and aryloxy; Sub₂₂ is selected from the group consisting of hydrogen, one to three groups selected from C₁—C₆ alkyl, halogen, C₁—C₆ alkylsulfonyl, nitro, cyano, arylthio and heteroarylthio; Z is selected from the group consisting of

wherein R₁₇ is selected form the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkoxycarbonyl, trifluoromethyl,NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′, R₁₆′ and Q are as defined in claim 63 ; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl; with the provision that two carboxy (—CO₂H) groups be on Z, such that the two carboxy groups be present on either R₁₇ or R₁₈, or one carboxy may be present on each of R₁₇ and R₁₈.
 91. The diacidic compounds of claim 90 wherein R₁₈ is

or R₁₇ is


91. The diacidic compounds of claim 89 wherein R₁₈ and R₁₉ are independently selected from the group consisting of

R₁₈ is selected from the group consisting of the groups listed immediately above and R₁₇ is selected from the group consisting of

or NHCO C₁—C₄ alkylene CO₂H; wherein Q is selected from the group consisting of —S—, —O— or —SO₂—.
 92. A method comprising reacting a) at least one diacidic monomer, comprising about 1 to 100 mole % of at least one light-absorbing monomer having a light absorption maximum between about 300 nm and about 1200 nm and 99-0 mole % of a non-light absorbing monomer which does not absorb significant light at wavelengths above 300 nm or has a light absorption maximum below 300 nm, with b) an organic compound having the formula X—B—X₁ wherein B is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃— C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene- C₁—C₄ alkylene, C₂— C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L- C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from the group consisting of —O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; X and X₁ are reactive groups and are independently selected from the group consisting of bromine, iodine and R—SO₂O; wherein R is selected from the group consisting of C₁—C₆ alkyl; C₁—C alkyl substituted with chlorine, fluorine, C₁—C₆ alkoxy, aryl, aryloxy, arylthio or C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl or aryl, wherein said reaction is carried out in a solvent in the presence of a base to form a light absorbing composition comprising a mixture of a polymer having the formula

and a cyclic compound having the general formula

wherein B is as defined above, n is at least 2, m is 1, 2, 3 or 4 and A comprises the residue of said diacidic monomer.
 93. The process of claim 92 where said light-absorbing monomers have the formula H—Y—H wherein H represents an acidic hydrogen atom; Y is a divalent light-absorbing moiety selected from the group consisting of chromophoric classes of azo, disazo, triazo, bis-azo, methine, arylidene, polymethine, azo-methine, azamethine, anthraquinone, anthrapyridone (3H-dibenz[f,ij]isoquinoline-2,7-dione, nitroarylamines anthrapyridine (7H-dibenz[f,ij]isoquinoline-7-one, phthaloylphenothiazine (14H-naphth[2,3-a]phenothiazine-8,13-dione, benzanthrone (7H(de)anthracene-7-one), anthrapyrimidine (7H-benzo[e]perimidine-7-one), anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, fluorindine (5,12-dihydroquinoxaline [2,3-b]phenazine, quinophthalone, phthalocyanine, metal phthalocyanine, naphthalocyanine, metal naphthalocyanine, nickel dithiolenes, squarylium compounds, croconium compounds, coumarin (2H-1-benzopyran-2-one), coumarin imine (2H-1-benzopyran-2-imine), perinone, benzodifuran, phthaloylacridone, phthaloylphenoxazine (14H-naphtho[2,3-a]phenoxazine-8,13-done, phthaloylacridone (13H-naphtho[2,3-c] acridine-5,8,14-trione), anthraquinonethioxanthane (8H-naphtho[2,3-c]thioxanthene-5,8,13-trione, anthrapyridazone, pyrrolo[3,4-c]pyrrole, indigo, thioindigo, quinoline, xanthene, acridine, azine, cyanine, oxazine, 1,4 and 1,5-naphthoquinones, 2,5-diarylaminoterephthalic acids and esters, pyromellitic acid dimide, naphthalene-1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylenetetracarboxylic acid diimide, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline, arylisoindoline, hydroxybenzophenone, benoztriazole, naphthotriazole, diminoisoindoline, naphthopyran (3H-naphtho[2,1-6]pyran-3-one and 3-imine, phthalimides, 2-arylbenzazoles, carbostyryls, 1,2-diarylethenes, 2,5-diarylthiophenes, 2,5-diaryl-1,3,4-oxadiazoles, triazines, 2,5-diarylfurans, 2,5-diaryl-1,3,4-thiadiazoles, thiophenes, 1,3-diphenyl-2-pyrazolines, 2-arylbenzofurans, 2,6-diphenylbenzofurans, quinolines, quinoxalines, 3,4-diarylfuanones, distyrylarenes, benzanthrones, polyarenes and naphthalimides.
 94. The method of claim 93 wherein said acidic functional groups are independently selected from the group consising of —CO₂H, —SH, —OH attached to an aromatic ring, —CONHCO—, —SO₂—NH—CO—, —SO₂—NH—SO₂—, 1(H)-1,2,4-triazol-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from the group consisting of C₁—C₆ alkyl, C₃—C₈ cycloalkyl, aryl and C₁—C₆ alkyl substituted with at least one group selected from the group consisting of C₁—C₆ alkoxy, aryl, aryloxy, arylthio and C₃—C₈ cycloalkyl.
 95. The method of claim 92 wherein said non light-absorbing monomers have the formula H—Y₁—H wherein H represents an acidic hydrogen atom; Y₁ is a divalent moiety selected from the group consisting of—O₂C—R₁—CO₂— and—O— R₂—O— and—O₂C—R₃—O—, wherein R₁ is selected from the group consisting of C₂—C₁₂ alkylene, 1-4-cyclohexylene, arylene, arylene-O-arylene, arylene-SO₂-arylene, arylene-S-arylene, and C₁—C₄ alkylene-O- C₁—C₄ alkylene; wherein R₂ is selected from the group consisting of arylene, arylene-O-arylene, arylene-S-arylene, arylene-SO₂-arylene, phenylene-phenylene, and phenylene-C(R₄)2-phenylene; wherein R₄ is selected from the group consisting of hydrogen and C₁—C₄ alkyl; wherein R₃ is selected from arylene.
 96. A light absorbing composition comprising a mixture of a polymer having the formula

and a cyclic compound having the general formula

wherein A₁ comprises the residue of at least one diacidic monomer having a light absorption maximum between about 300 nm and about 1200 nm, and wherein B is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃—C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, and C₂— C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L- C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N (C₁—C₆ alkyl)— and combinations thereof; wherein n is at least 2 and m is 1, 2, 3 or
 4. 97. A composition comprising a thermoplastic polymer blended with at least one light absorbing linear polymeric composition of claim 96 .
 98. The composition of claim 97 wherein said thermoplastic polymer is selected from the group consisting of polyesters, polyolefins, polyamides, polyimides, polyvinyl chloride, polyurethanes, polycarbonates, cellulose esters, polyacrylates, polyvinylesters, polyester-amides, polystyrene, polyacrylonitrile-butadiene- styrene, polystyrene-acrylonitrile and mixtures and blends thereof.
 99. The composition of claim 96 wherein A₁ comprises the residue of at least one diacidic monomer having the structure H—Y—H wherein H represents an acidic hydrogen atom and Y is a divalent light-absorbing moiety selected from the chromophoric classes consisting of azo, disazo, triazo, bis-azo, methine, arylidene, polymethine, azo-methine, azamethine, anthraquinone, anthrapyridone (3H-dibenz [f,ij] isoquinoline-2,7-dione, nitroarylamines anthrapyridine (7H-dibenz[f,ij]isoquinoline-7-one, phthaloylphenothiazine (14H-naphth[2,3-a]phenothiazine-8,13-dione, benzanthrone (7H(de)anthracene-7-one), anthrapyrimidine (7H-benzo[e]perimidine-7-one), anthrapyrazole, anthraisothiazole, triphenodioxazine, thiaxanthene-9-one, fluorindine (5,12-dihydroquinoxaline [2,3-b]phenazine, quinophthalone, phthalocyanine, metal phthalocyanine, naphthalocyanine, metal naphthalocyanine, nickel dithiolenes, squarylium compounds, croconium compounds, coumarin (2H-1-benzopyran-2-one), coumarin imine (2H-1-benzopyran-2-imine), perinone, benzodifuran, phthaloylacridone, phthaloylphenoxazine (14H-naphtho[2,3-a]phenoxazine-8,13-done, phthaloylacridone (13H-naphtho[2,3-c] acridine-5,8,14-trione), anthraquinonethioxanthane (8H-naphtho[2,3-c]thioxanthene-5,8,13-trione, anthrapyridazone, pyrrolo[3,4-c]pyrrole, indigo, thioindigo, quinoline, xanthene, acridine, azine, cyanines, oxazine, 1,4 and 1,5-naphthoquinones, 2,5-diarylaminoterephthalic acids and esters, pyromellitic acid dimide, naphthalene-1,4,5,8-tetracarboxylic acid diimide, 3,4,9,10-perylenetetracarboxylic acid diimide, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxopyrroline, arylisoindoline, hydroxybenzophenone, benoztriazole, naphthotriazole, diminoisoindoline, naphthopyran (3H-naphtho[2,1-6]pyran-3-one and 3-imine, phthalimides, 2-arylbenzazoles, carbostyryls, 1,2-diarylethenes, 2,5-diarylthiophenes, 2,5-diaryl-1,3,4-oxadiazoles, triazines, 2,5-diarylfurans, 2,5-diaryl-1,3,4-thiadiazoles, thiophenes, 1,3-diphenyl-2-pyrazolines, 2-arylbenzofurans, 2,6-diphenylbenzofurans, quinolines, quinoxalines, 3,4-diarylfuanones, distyrylarenes, benzanthrones, polyarenes and naphthalimides.
 100. The light absorbing composition of claim 99 wherein A₁ further comprises less than about 50% by weight of the total composition of a residue of at least one non-light absorbing monomer having the formula H—Y₁—H wherein Y₁ is a divalent moiety, selected from the group consisting of—O₂C—R₁—CO₂— and—O—R₂—O— and—O₂C—R₃—O—, wherein R₁ is selected from the group consisting of C₂—C₁₂ alkylene, 1-4-cyclohexylene, arylene, arylene-O-arylene, arylene-SO₂-arylene, arylene-S-arylene, and C₁—C₄ alkylene-O- C₁—C₄ alkylene; wherein R₂ is selected from the group consisting of arylene, arylene-O-arylene, arylene-S—arylene, arylene-SO₂-arylene, phenylene-phenylene, and phenylene-C(R₄)₂-phenylene; wherein R₄ is selected from the group consisting of hydrogen and C₁—C₄ alkyl; wherein R₃ is arylene; wherein B is is a divalent organic radical selected from the group consisting of C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene-C₃—C₈-cycloalkylene-C₁—C₄ alkylene, C₁—C₄ alkylene-arylene-C₁—C₄ alkylene, and C₂—C₄-alkylene-L-arylene-L-C₂—C₄ alkylene and C₂—C₄ alkylene-(L-C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof.
 101. The light absorbing composition of claim 100 wherein A₁ comprises the residue of at least one diacidic monomer having at least one acidic group other than carboxy and having a light absorption maximum between about 300 nm and about 1200 nm and wherein B is a divalent organic radical selected from C₂—C₁₂ alkylene, C₃—C₈ cycloalkylene, C₁—C₄ alkylene- C₃— C₈-cycloalkylene- C₁—C₄ alkylene, C₁—C₄ alkylene-arylene- C₁—C₄ alkylene, and C₂—C₄-alkylene-L-arylene-L- C₂—C₄ alkylene and C₂—C₄ alkylene-(L-C₂—C₄ alkylene)₁₋₄, wherein L is a linking group selected from—O—, —S—, —SO₂—, —NH—, —N(C₁—C₆ alkyl)—, —N(aryl—, —N(SO₂ C₁—C₆ alkyl)—, —(SO₂aryl)—, —SO₂N(C₁—C₆ alkyl)— and combinations thereof; wherein n is at least
 2. 102. The composition of claim 99 wherein said light absorbing monomer comprises two acidic groups independently selected from the group consisting of —CO₂H, SH, hydroxy attached to an aromatic ring, —CONHCO— (imide), —SO₂NHCO—, —SO₂NHSO₂—, 1(H)-1,2,4-triazolyl-3-yl-, imidazolyl, benzimidazolyl, pyrazolyl, —SO₂H attached to an aromatic ring, —NHSO₂R₅ and—SO₂NHR₅, wherein R₅ is selected from the group consisting of C₁—C₆ alkyl; C₁—C₆ alkyl substituted with at least one group selected from C₁—C₆ alkoxy, aryl, aryloxy, arylthio and C₃—C₈ cycloalkyl; C₃—C₈ cycloalkyl; aryl.
 103. The composition of claim 100 wherein said light absorbing monomer comprises two carboxy groups as acidic functional groups.
 104. The composition of claim 100 wherein the light absorbing portion of A comprises the residue of at least one diacidic light absorbing monomer selected from the group consisting of the anthraquinone and anthrapyridone colorants having the structures:

wherein R₁₄ is selected from the group consisting of hydrogen and 1-4 groups selected from amino, C₁—C₁₀ alkylamino, C₃—C₈ alkenylamino, C₃—C₈ alkynylamino, C₃—C₈ cycloalkylamino, arylamino, halogen, C₁—C₆ alkoxy, C₁—C₆ alkylthio, aryl, aroyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, NHCO C₁—C₆ alkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHSO₂ C₁—C₆ alkyl, NHSO₂ aryl, C₁—C₆ alkoxycarbonyl, aryloxy, arylthio, heteroarylthio, cyano, nitro, trifluoromethyl, thiocyano, SO₂ C₁—C₆ alkyl, SO₂ aryl, —SO₂NH C₁—C₆ alkyl, —SO₂N(C₁—C₆ alkyl)₂, —SO₂N(C₁—C₆ alkyl) aryl, CONH C₁—C₆ alkyl, CON(C₁—C₆ alkyl)₂, CON(C₁—C₆ alkyl) aryl, C₁—C₆ alkyl, furfurylamino, tetrahydrofurfurylamino, 4- (hydroxymethyl) cyclohexanemethylamino,

or hydroxy; Q and Q′ are independently selected from the group consisting of—O—, —N(COR₁₀)—, —N(SO₂R₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, —CON(R₁₀)—, SO₂N (R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl, or C₁—C₁₀ alkyl; R₁₅ is selected from the group consisting of hydrogen, cyano, C₁—C₆ alkylamino, C₁—C₆ alkoxy, halogen, arylthio, aryl, heteroaryl, heteroarylthio, C₁—C₆ alkoxycarbonyl, aroyl or arylsulfonyl; R₁₆ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl and aryl; R₁₆′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, halogen and C₁—C₆ alkoxy; wherein each C₁—C₆ alkyl group and C₁—C₆ alkyl group which is a portion of another group may contain at least one substituent selected from the group consisting of hydroxy, cyano, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkoxy, C₁—C₆ alkylcyclohexyl, hydroxmethyl cyclohpxyl, aryl and heteroaryl; with the provision that two acidic groups containing one acidic proton each or one acidic group containing two acidic hydrogens be present in the diacidic compounds.
 105. The composition of claim 100 wherein the light absorbing portion of A comprises the residue of at least one light absorbing monomer selected from the group consisting of azo, disazo, bis-azo and azomethine and having respectively the structures: R₆—N═N—Z, R₆—N═N—R₇—N═N—Z, R₆—N═N—Y₁—N═N—R₆ and D═HC—N═N—Z wherein R₆ is the residue of an aromatic or heteroaromatic amine which has been dizaotized and coupled with a coupling component H-Z and is derived from an amine selected from the group consisting of aromatic and heteroaromatic amine classes selected from the group consisting of aniline, 1-aminonaphthalene, 1-aminoanthraquinone, 4-aminoazobenzene, 2-aminothiazole, 2-aminobenzothiazole, 3-amino-2,1-benzisothiazole, 2-aminothieno[2,3-d]thiazole, 5-aminoisothiazole, 5-aminopyrazole, 4-aminopyrazoloisothiazole, 2-amino-1,3,4-thiadiazole, 5-amino-1,2,4-thiadiazole, 5-amino-1,2,3-triazole, 2-amino-1,3,4-triazole, 2(5) aminoimidazole, 3-aminopyridine, 2(3) aminothiophene, 2(3) aminobenzo[b]thiophene, 2-aminothieno[3,2-b]thiophene, 3-aminothieno[2,3-c]isothiazole, 3-amino-7-benz-2,1-isothiazole, 3-aminobenzothienoisothiazole, 3-aminoisothiazole[3,4-d]pyrimidine, 5-amino-1,2,3-triazole, 3(4) aminophthalimide and 5(6) amino-1,2-benzisothiazolon-1,1-dioxide with said aromatic and heteroaromatic ring systems being unsubstituted or substituted with one or more groups selected from C₁—C₁₀ alkyl, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl, carboxy, halogen, C₁—C₆ alkoxycarbonyl, formyl, C₁—C₆ alkanoyl, C₁—C₆ alkanoyloxy, dicyanovinyl, C₃—C₈-cycloalkanoyl, thiocyano, trifluroacetyl, cyano, carbamoyl, —CONH—C₁—C₆ alkyl, CONHaryl, CON(C₁—C₆ alkyl)₂, sulfamoyl, SO₂NH C₁—C₆ alkyl, SO₂N(C₁—C₆ alkyl)₂, SO₂NHaryl, SO₂NH C₃—C₈ cycloalkyl, CONH C₃—C₈ cycloalkyl, aryl, aroyl, —NHSO₂ C₁—C₆ alkyl, —N(C₁—C₆ alkyl)SO₂ C₁—C₆ alkyl, —NHSO₂ aryl, NHCO C₁—C₆ alkyl, NHCO C₃—C₈ cycloalkyl, NHCOaryl, NHCO₂ C₁—C₆ alkyl, NHCONH C₁—C₆ alkyl, NHCONHaryl, N(C₁—C₆ alkyl)aryl, arylazo, heteroaryl, aryloxy, arylthio, C₃—C₈ cycloalkoxy, heteroarylazo, heteroarylthio, arylsulfonyl, tricyanovinyl, aryloxysulfonyl, C₁—C₆ alkylsulfonyl, trifluoromethyl, fluorosulfonyl, trifluoromethylsulfonyl, thiocyano, hydroxy, nitro or CH═D, wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂; wherein R₇ is a divalent aromatic or heteroaromatic radical selected from the group consisting of 1,4-phenylene, naphthalene-1,4-diyl, thiazol-2,5-diyl and thiophene-2,5-diyl:

wherein R₈ is selected from the group consisting of hydrogen or 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, cyano, halogen, —NHCO C₁—C₆ alkyl, —NHCO₂ C₁—C₆ alkyl, —NHCO aryl, —NHCONH aryl or NHCONH C₁—C₆ alkyl; R₉ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, halogen, aryl, heteroaryl; R₁₀ is selected from the group consisting of hydrogen, C₁—C₆ alkoxycarbonyl, cyano, carbamoyl, aryl, arylsulfonyl, aroyl, —CONH C₁—C₆ alkyl, or C₁—C₆ alkylsulfonyl; wherein Z is the residue of a coupling compound selected from the group consisting of electron rich compound classes of anilines, 1-aminonaphthalenes, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro-2H-1,4-benzoxazine), pyrazolones, pyrazoles, 3-cyano-6-hydroxy-2-pyridones, 2,3-dihydroindoles, indoles, 4-hydroxycoumarins, 4-hydroxy-2-quinolones, imidazo[2,1-b]thiazoles, julolidines (2,3,6,7-tetrahydro-1H, 5H-benzo[ij]quinolizines), 1-oxajulolidines, 1,2,5,6-tetrahydro-4H-pyrrolo[3,2,1-ij]quinolines, 2,6-diamino-3 cyanopyridines, 2-aminothiazoles, 2-aminothiophenes, 5,5-dimethyl-1,3-cyclohexanedione (dimedone), phenols, naphthols, 2,4-pentanediones or acetoacetarylides; wherein Y₁ is the residue of a bis coupling component selected from the group consisting of anilines, 1,2-dihydroquinolines, 1,2,3,4-tetrahydroquinolines, benzomorpholines (3,4-dihydro- 2H-1,4-benzoxazines), 3-cyano-6-hydroxy-2-pyridones, 2,6-diaminopyridines, 2,3-dihydroindoles, naphthylamines, 2-aminothiazoles, or a combination of these; with the provision that two acidic functional groups containing one acidic hydrogen each or a functional group containing two acidic hydrogen are present in the diacidic light absorbing monomer.
 106. The composition of claim 100 wherein the light absorbing portion of A comprises the residue of at least one light absorbing monomer selected from the group consisting of methine, arylidene, polmethine, azamethine, 3-aryl-2,5-dioxypyrroline, 3-aryl-5-dicyanomethylene-2-oxypyrroline and arylisoindoline and having respectively the structures:

wherein R₁₁ is the residue of an electron rich aromatic compound selected from the group consisting of an aniline, 1-naphthylamine, 1,2-dihydroquinoline, 1,2,3,4-tetrahydroquinoline, 1,3,3-trimethyl- 2-methyleneindole, 1,3-dihydro-2-methylene- 1,1,3-trimethyl-2H-benz[e]indole, imidazo [2,1-b] thiazole, benzomorpholine (3,4-dihydro-2H-1,4,benzoxazine), 2,3-dihydroindole, indole, 2-aminothiazole, julolidine (2,3,6,7-tetrahydro-1H, 5H- benz [ij] quinolizine, 1-oxajulolidine, 4H-pyrrolo [3,2,1-ij]-quinoline, phenol, naphthol, thiophenol, pyrrole, pyrazole, furan, thiophene, carbazole, phenothiazine or phenoxazine compound; R₁₂ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ alkenyl, C₃—C₈-alkynyl, C₃—C₈ cycloalkyl, aryl, CH₂CH₂O₁₋₃ R₁₃ and C₁—C₄ alkylene- C₃—C₈ cycloalkylene, wherein the C₁—C₆ alkyl groups may be substituted by at least one group selected from the group consisting of carboxy, C₁—C₆ carbalkoxy, C₁—C₆ alkanoyloxy, cyano, hydroxy, chlorine, fluorine, C₁—C₆ alkoxy, C₃—C₈ cycloalkyl or aryl; R₁₃ is selected from the group consisting of hydrogen, C₁—C₆ alkoxy or C₁—C₆ alkanoyloxy; wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups containing one acidic hydrogen each, or a functional group containing two acidic hydrogens are present.
 107. The composition of claim 100 wherein the light absorbing portion of A₂ comprises a residue of at least one diacidic coumarin compounds selected from the group consisting of the structures

wherein Z₃ is selected from the group consisting of cyano, C₁—C₆ alkoxycarbonyl, C₁—C₆ alkylsulfonyl, arylsulfonyl, aryl, heteroaryl, formyl, aroyl, C₁—C₆ alkanoyl or—CH═D, wherein R₁₇ is selected from the group consisting of hydrogen, 1-2 groups selected from C₁—C₆ alkyl, C₁—C₆ alkoxy, C₁—C₆ alkylthio, —O C₂—C₆ alkylene-OH, O C₂—C₆ alkylene- C₁—C₆ alkanoyloxy, C₁—C₆ alkylene-OH, C₁—C₆ alkylene- C₁—C₆ alkanoyloxy, halogen, carboxy, C₁—C₆ alkoxycarbonyl, trifluoromethyl,NHCOR₂₄ , NHCO₂R₂₄, NHCON(R₂₄)R₂₅, and NHSO₂R₂₅, wherein R₂₄ is selected from the group consisting of hydrogen, C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl, R₂₅ is selected from the group consisting of C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl or aryl wherein each C₁—C₁₀ alkyl group in R₂₄ and R₂₅ may be further substituted with one or more groups selected from the group consisting of C₃—C₈ cycloalkyl, aryl, aryloxy, arylthio, CO₂H, CO₂ C₁—C₆ alkyl, cyano, hydroxy, succinimido, C₁—C₆ alkoxy,

wherein R₅′ is selected from the group consisting of hydrogen, C₁—C₆ alkyl or aryl; R₁₆′ is selected from hydrogen or one or two groups selected from C₁—C₆ alkyl, halogen, and C₁—C₆ alkoxy; Q is selected from the group consisting of —O—, —N(COR₁₀)—, —N(R₁₀)—, —S—, —SO₂—, —CO₂—, CON(R₁₀), SO₂(R₁₀)—, wherein R₁₀ is selected from the group consisting of hydrogen, aryl, C₃—C₈ cycloalkyl or C₁—C₁₀ alkyl; R₁₈ and R₁₉ are independently selected from the group consisting of hydrogen, unsubstituted C₁—C₁₀ alkyl, substituted C₁—C₁₀ alkyl, C₃—C₈ cycloalkyl, C₃—C₈ alkenyl, C₃—C₈ alkynyl and aryl or R₁₈ and R₁₉ may be combined with another element to which they are attached to form a radical Z having the formula

wherein Q₂ is selected from the group consisting of a covalent bond, —O—, —S—, —SO₂—, —CO—, —CO₂—, —N—(C₁—C₆ alkyl)—, —N(CO C₁—C₆ alkyl)—, —N(SO₂ C₁—C₆ alkyl)—, —N(CO aryl)—, or—N(SO₂ aryl); R₂₀, R₂₁ and R₂₂ are independently selected from the group consisting of or C₁—C₆ alkyl; R₂₃ is selected from the group consisting of hydrogen, C₁—C₆ alkyl, C₃—C₈ cycloalkyl, heteroaryl or aryl; wherein D is the residue of an active methylene compound selected from the group consisting of malononitrile, α-cyanoacetic acid esters, malonic acid esters, α-cyanacetic acid amides, α-C₁—C₆ alkylsulfonylacetonitriles, α-arylsulfonylacetonitriles, α-C₁—C₆ alkanoylacetonitriles, α-aroylacetonitriles, α-heteroarylacetonitriles, bis(heteroaryl)methanes, 1,3-indanediones, 2-furanones, benzo-2-furanones, naphtho-2-furanones, 2-indolones, 3-cyano-1,6-dihydro-4-methyl-2,6-dioxy (2H)-pyridines, benzo (b) thieno-3-ylidene propane dinitrile-5,5-dioxides, 1,3-bis(dicyanomethylene) indanes, barbituric acid, 5-pyrazolones, dimedone, 3-oxo-2,3-dihydro-1-benzothiophene-1,1-dioxides or aryl-C(CH₃)C═C(CN)₂, with the proviso that two acidic functional groups containing one acidic hydrogen each, or a functional group containing two acidic hydrogens are present. 